• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.115-117
• /
• 2005

The purpose of this study is to establish the fatigue design criteria for the notched structural components subjected to high mean stress. In order to do it, the effects of stress concentration factor on the monotonic and cyclic tensile properties were investigated. Based on the results, two fatigue design approaches for the notched specimen using Goodman diagram was established and verified by comparing with the experimental result.

• International Journal of Automotive Technology
• /
• v.7 no.5
• /
• pp.579-584
• /
• 2006

Aluminum Resistance Spot Weld(Al RSW) is an enabling technology for body assembly of low mass fraction vehicles. Due to the unreliable durability of spot-welded joints, applications of Al RSW are limited. This study presents experimental investigation on the use of a post-weld cold working process to improve the fatigue strength of Al RSW. The post-weld cold working process includes special shaped indenters that are pressed or driven into the structure to induce compressive residual stresses. The mechanical properties of the post-weld cold worked Al RSW were investigated, including the experimental results of fatigue and micro-hardness tests. Comparisons of the mechanical properties and qualitative results between the as-welded RSW specimens and the post-weld cold worked RSW specimens are discussed. The post-weld cold worked Al RSW samples had an increase in both microhardness and fatigue life.

• Journal of the korean Society of Automotive Engineers
• /
• v.5 no.2
• /
• pp.31-40
• /
• 1983

A study was made of the effect of cold working and stabilizing temperature on the fatigue properties of Aluminum alloy 5083. The amount of cold working ranged from 14% to 35% and stabilizing temperature was 120.deg. C-160.deg. C. Rotary bending fatigue test was carried out, and it was found that 1) E specimen that had been cold worked by the cold reduction of 35% and stabilized at 160.deg. C for 2 hours was showed the most excellent fatigue limit and endurance ratio and, 2) By the results of the between crack propagation behavior and stress intensity factor, E specimen was showed the better resistance to fatigue crack growth than others.

• Journal of Mechanical Science and Technology
• /
• v.15 no.7
• /
• pp.1022-1031
• /
• 2001

The elastic modulus and fatigue properties of canine and human trabecular bone tissues (single trabecular) were experimentally determined on a microstructural level using four-point bending cyclic test, and they were compared based on microstructural characteristics and mineral density. The results showed that canine trabecular bone tissue had significantly lower modulus and lower fatigue strength than human tissue. The observed microstructural differences between the two tissues may be more responsible for the differences, although the lower mineral density in canine tissue might also have contributed to the lower modulus and fatigue strength.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.256-259
• /
• 2008

An micro-probe tip must be manufactured using thin film to evaluate integrity of the semiconductor with narrow distance between pads. In this study, fatigue tests were performed for BeCu thin film which is used in micro-probe tip of semiconductor test machine. The thin film was manufactured by electro plating process, and the specimens were fabricated by wire-cut electric discharge method to make hour glass type specimen of $5000{\mu}m$ width, $29200{\mu}m$ length and $30{\mu}m$ thickness. The fatigue test of load control with 10Hz frequency was performed, in ambient environment. The fatigue cycles were tension-tension with mean stress, at stress ratio, R=0.1.

• Journal of the Korean Society of Safety
• /
• v.25 no.6
• /
• pp.28-33
• /
• 2010

Stainless steel is useful material for various industrial facilities such as the nuclear and steam power plant and the heavy chemical industry due to its good corrosion resistance and mechanical properties. However, it has also a large problem that is sensitized in the welding process and its corrosion resistance and mechanical properties decreases by sensitization. Thus, corrosion and corrosion fatigue characteristics of artificially sensitized austenitic STS304 were investigated through the EPR test and corrosion fatigue test. Obtained results are as follows: 1) According to the sensitizing period increase, Cr deficiency layer is linearly expanded. 2) Degree of sensitization(Ia/Ir) proportionally increased with sensitizing period. However, after 4hrs, it showed constant value. 3) Cr-carbide($Cr_{23}C_6$) in the grain boundary increased as sensitizing period increases until six hours. 4) corrosion fatigue strength of sensitized STS304 were remarkably reduced compare to non-sensitized ones.

• Transactions of Materials Processing
• /
• v.13 no.5
• /
• pp.435-440
• /
• 2004

The temperature in hot forming of metallic materials, such as hot extrusion and hot forging, ranges from $300^{\circ}C$ to $900^{\circ}C$. Correspondingly, the die also exhibits high temperatures close to that of a work piece and its life is limited generally by high temperature fatigue. Thus, the analysis of high temperature fatigue would need the mechanical properties over the wide ranges of temperature. However, very few studies on the high temperature fatigue of brittle materials have been reported. Especially, the study on the fatigue behavior over such transition temperature regime is very rare. In this paper, the stress-strain curves and stress-life curves of a die steel such as STD61 are experimentally obtained. The wide ranges of temperature from $300^{\circ}C$ to $900^{\circ}C$ are considered in experiments and the transition temperature zone is carefully examined.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.3
• /
• pp.165-171
• /
• 2003

In a structure, many components are fastened together using bolts, nuts and rivets through drilled holes. Not only do these fastened joints enable easy assembly and dismantling, they are also able to transfer as well as to distribute loads applied onto the structures. The major drawback of such connections, however, is that the fatigue life of the components is reduced by the presence of the hole since the stress concentration around the hole is increased. In addition, the hole drilling process itself may introduce defects or roughness at the surfaces of the hole that may cause further decrease in fatigue performance of the components. For applications where fatigue loadings are important, one way to compensate the decrease in fatigue life of the components is by introduction of beneficial compressive residual stress around the hole using cold working. The material used for this research were A12024-T351 and A17050-T7451 using the primary member of aircraft. We present, In this paper, the characteristics of coldworking by evaluation of the hole expansion ratio, residual stress distribution, and fatigue properties.

• Structural Engineering and Mechanics
• /
• v.53 no.2
• /
• pp.311-324
• /
• 2015

The purpose of this study was to investigate experimentally the fatigue performance of reinforced concrete (RC) beams with hot-rolled ribbed fine-grained steel bars of yielding strength 500MPa (HRBF500). Three rectangular and three T-section RC beams with HRBF500 bars were constructed and tested under static and constant-amplitude cyclic loading. Prior to the application of repeated loading, all beams were initially cracked under static loading. The major test variables were the steel ratio, cross-sectional shape and stress range. The stress evolution of HRBF500 bars, the information about crack growth and the deflection developments of test beams were presented and analyzed. Rapid increases in deflections and tension steel stress occured in the early stages of fatigue loading, and were followed by a relatively stable period. Test results indicate that, the concrete beams reinforced with appropriate amount of HRBF500 bars can survive 2.5 million cycles of constant-amplitude cyclic loading with no apparent signs of damage, on condition that the initial extreme tensile stress in HRBF500 steel bars was controlled less than 150 MPa. It was also found that, the initial extreme tension steel stress, stress range, and steel ratio were the main factors that affected the fatigue properties of RC beams with HRBF500 bars, whose effects on fatigue properties were fully discussed in this paper, while the cross-sectional shape had no significant influence in fatigue properties. The results provide important guidance for the fatigue design of concrete beams reinforced with HRBF500 steel bars.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.4
• /
• pp.1301-1308
• /
• 1996

In order to save the energy and protect the environment, it were studied about ecomaterials with the developed countries as central figure. In the Metal Matrix Composites(MMCs), this trends appeared the development of the MMCs which had excellent mechanical properties in spite of the low volume fraction of reinforcement. Therefore, in this study, fatigue crack growth test, tensile and hardness test were conducted in order to investigate the mechanical and fatigue properties of 5 %, and 10 % $SiC_{p}$/Al composites. As the results, in the tensile and hardness test, tensile strength and hardness increased but fatigue crack growth rate decreased with $SiC_{p}$/Al volume fraction. And in the view of fatigue failured surface through the SEM, fatigue crack initiated around the SiC particle and in low $\Delta{K}$ regions, fatigue creck detoured the SiC particle but crack propagated through the SiC particle in the high $\DeltaK$ regions.