• Journal of Mechanical Science and Technology
• /
• v.17 no.3
• /
• pp.343-349
• /
• 2003

The fuselage-wing intersection suffers from the cyclic bending moment of variable amplitude. Therefore, the influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in AFRP/Al laminate of fuselage-wing was investigated in this study. The cyclic bending moment fatigue test in AFRP/Al laminate was performed with five levels of bending moment. The shape and size of the delamination Lone formed along the fatigue crack between aluminum sheet and aramid fiber-adhesive layer were measured by an ultrasonic C-scan. The relationships between da/dN and ΔK, between the cyclic bending moment and the delamination zone size, and between the fiber bridging behavior and the delamination zone were studied. As results, fiber failures were not observed in the delamination zone in this study, the fiber bridging modification factor increases and the fatigue crack growth rate decrease and the shape of delamination zone is semi-elliptic with the contour decreasing non-linearly toward the crack tip.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.04a
• /
• pp.125-133
• /
• 2002

In this study, it was investigated about endurance limit and fatigue behavior of load carrying fillet welded cruciform joints according to welding methods of SMAW, SAW, MIG and FCAW commonly using for welding structures in present. Endurance limit carried omit highly in the order of SMAW, MIG, SAW, FCAW and fatigue crack propagation ratio carried out lowly in the order of SMAW, MIG, FCAW, SAW. By these results, it is needed to use SMAW or MIG welding methods for welding structures with small welding capacity and SAW or FCAW methods for large welding structures after due consideration about economic gains and operation efficiency of welding. Fatigue crack propagation ratio is more effected by strength of welding materials than endurance limit of welding materials according to welding methods.

• Journal of Welding and Joining
• /
• v.5 no.1
• /
• pp.73-80
• /
• 1987

During PWHT, it is well known that residual stress in weld HAZ is one of the reasons for PWHT embitterment. In case of static loading, it was experimentally found that fracture toughness of weld HAZ was dependant upon PWHT conditions. However, the effects of PWHT on fatigue behavior are not clearly verified. Therefore, in this paper, the effects of heating rate PWHT conditions and residual stress simulated in weld HAZ of Cr-Mo steel on fatigue crack propagation behavior were evaluated by fatigue Testing and SEM observation. The obtained results are summarized as follows; 1. Applied stress($10 Kgf/mm^2$) in weld HAZ during PWHT tneded to decrease fatigue strength and to increase fatigue crack growth rate. 2. Applied stress and slow heating rate of 60.deg. C/hr during PWHT contributed to precipitin of impurity elements as well as carbide, which promoted the fatigue crack growth. 3. Fatigue crack growth rate decreased at the heating rate of 220.deg. C/hr in contrast with 600.deg. C/hr and 60.deg. C/hr.

• Journal of the Korean Society of Safety
• /
• v.15 no.3
• /
• pp.40-44
• /
• 2000

The fatigue and tensile test were carried out with Mild steel using the Dump Frame of commercial car. The specimens were heat-treated at $810^{\circ}C$ and $930^{\circ}C$ and worked 4.5, 6.0, 8.0mm thickness in order to look over the mechanical properties and fatigue life by heat treatment and thickness from the tensile test result, the yield strength of the heat treated specimens was increased about 35% more than that of the non-heat treated specimen. The fatigue life of non-heated specimen was decreased 15% but that of heat treated specimens at $870^{\circ}C$ and $930^{\circ}C$ were decreased 16.38% and 13.16% respectably according to increasing the thickness from 4.5 to 8.0mm.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.4
• /
• pp.48-55
• /
• 2000

For the Tailor Welded Blank sheet used for automobile body panel, the characteristics of fatigue strength and crack propagation behavior were studied. The thickness of specimens was joined to be same (0.9mm+0.9mm) and different (0.9mm+2.0mm) .As a base test, mechanical properties around weld zone were examined . The results indicated that there were no significant decreases in mechanical properties , but hardness around weld bead was 2.3 times greater than base material . The fatigue strength was the highest when the loading direction was parallel to the welding direction, which was about 85% of tensile strength of base material. It was decreased by 8.5% when the thickness of specimens and base metal was different, and it was increased by 25% when pres-strain was applied. The crack propagation rate was noticeably decreased around weld line and rapidly increased as it passed through weld line. Reviewing the shape of the crack propagation , crack width around weld line was around the weld zone due to retardation of crack growth , but is became narrow passing weld line due to decreased toughness.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.2
• /
• pp.646-652
• /
• 2014

It is the primary aim of this paper to propose the empirical fatigue crack propagation model fit to describe a crack growth behavior of AZ31 magnesium alloys under the different specimen thickness conditions. The empirical models estimated are Paris-Erdogan model, Walker model, Forman model, and modified-Forman model. The parameters of each model are estimated by maximum likelihood method. The statistical crack growth data needed for an estimation of empirical models are obtained by fatigue crack propagation tests under the three cases of specimen thickness. It is found that the good empirical models fit to describe a crack growth behavior of AZ31 magnesium alloys under the different specimen thickness conditions are Paris-Erdogan model and Walker model. It is also verified that a fatigue crack growth rate exponent of a empirical model may be a material constant at the specimen thickness conditions of 4.75mm and 6.60mm.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.1
• /
• pp.143-150
• /
• 2003

Experimental research has been carried out to investigate the characteristics of the fatigue crack initiation and propagation behavior of Tailor Welded Blank(TB) sheet used for vehicle body. We used three types of specimens which were machined of the same base metal: one is 1.4mm thick, another is 1.6mm thick, and the third(TB specimen) is laser-welded of two specimens(1.4mm and 1.6mm thick ones). The results of tensile and hardness test indicate that the yield strength of the TB specimen is the highest, and the hardness around welding bead is higher than that of base metal. Fatigue strength and fatigue limit of the TB specimen are much superior to those of the base metal up to $10^6$ cycles. The fatigue crack propagation of the heat-affected zone of the TB specimen is slower than that of the base metal. Welding bead has the fastest crack Propagation in the low stress intensity factor range$(\DeltaK)$ region, but the slowest in the high $\DeltaK$ region. The fatigue propagation characteristic of the TB specimen is relatively stable in comparison with that of the base metal in the high ${\Delta}K$ region around over $28MPa\sqrt{m}$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.531-535
• /
• 2005

This study investigates the behavior of fatigue crack propagating between holes or holes lilted with another materials. It is experimentally and analytically confirmed that the center crack stops when its tip reaches near the center line of the holes and a small crack is initiated from the boundaries of holes or the holes filled with another materials and it propagates to final fracture. The mechanical behaviors of center crack near the another materials are also investigated. The phenomenon that this crack propagates to fracture is investigated by compliance method.

• International Journal of Railway
• /
• v.5 no.2
• /
• pp.71-76
• /
• 2012

Recently, axle load, operating speed and traffic density on railroads have had a tendency to increase and thereby cause additional pressure applied on used track. These operating conditions frequently result in service failure due to wear caused by wheel-rail contact and fatigue damage under cyclic loading. Among rail defects, the transverse crack, which has been the most dangerous type of fatigue damages, is developed from the subsurface crack near the rail running face and grows perpendicular to the rail surface. Therefore, it is necessary to investigate systematically the growth behavior of transverse crack for rail steel under mixed mode. In this study, the fatigue crack growth behavior of the transverse crack in rail steel was experimentally investigated under mixed-mode variable amplitude loadings.

• Journal of Industrial Technology
• /
• v.18
• /
• pp.117-124
• /
• 1998

In recently, according to increase the construction rate of steel bridge, it is necessary to develop the high strength, high toughness steel. Thus, this study show to evaluate the fatigue characteristic of SWS 570 B first used within a country. With the weld-joined compact tension specimens compared with each other, that is, transverse and lengthwise about the crack propagation, high and low in the input heat level, the fatigue test were performed. The log-log curves between the fatigue crack propagation rate da/dN and the transition range of the stress intensity factor ${\Delta}K$ ahead the crack tip were drawed, with these data. By using this curve, we obtained C and m which is material constant from Paris-Erdogan power law. The obtained results from this study indicate that fatigue crack growth rate of SWS 570 B is not influenced by softening effect which occurs in the HAZ(heat-affected zone) when high and low heat input weld is carried out. Softening effects, which affect fatigue properties, are shown that it is not affected to the fatigue growth rates significantly.