• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.120-125
• /
• 2004

Fatigue life of welded joints are governed by the propagation of multiple collinear surface cracks distributed randomly along weld bead. These cracks propagate in mutual interaction and coalescence of them. To estimate the fatigue life, the influences of above two mechanisms on the fatigue life should be taken into account. These two mechanisms appear through the stress intensity factors disturbed mutually. However, it is difficult to calculate the stress intensity factors of multiple surface cracks located in vicinity of weld toe. The stress intensity factors are calculated normally by using the Mk-factors, but such Mk-factors are very rare in literature. In this study, the Mk-factors were obtained from a parametric study on crack length and depth, in which a finite element method is used. A fatigue test for a cruciform welded joint was conducted. The fatigue life of the tested specimen was estimated through present method with the informations obtained from the test, e.g. the number, size and locations of the cracks. The estimated and measured fatigue life showed a good agreement.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2005년도 추계학술발표대회 논문집
• /
• pp.234-238
• /
• 2005

This paper explains the fatigue test procedure of a composite train carbody. The composite carbody with length of 23m was manufactured as a sandwich structure composed of a 40mm-thick aluminium honeycomb core and 5mm-thick woven fabric carbon/epoxy face. In order to evaluate fatigue strength of the composite carbody, the carbody will be excited by two 50-ton capacity hydraulic actuators. The excitation frequency will be measured by natural frequency evaluation test under full weight condition. The test The fatigue test is to be conducted For $2{\times}10^6$cycles. During the fatigue test, the nondestructive tests using X-ray and liquid penetrant will be performed. From crack detection tests, the location and Fatigue crack progress will be investigated.

• 대한기계학회논문집A
• /
• 제27권12호
• /
• pp.2055-2060
• /
• 2003

Striation is a typical pattern observed on the fatigue fracture surface and the spacing is known to correspond to a macroscopic fatigue crack growth rate, and many models for the predict in the formation of such striation have been proposed. However, these theories and methods can't be applied under random loading spectrum. In this study, the fatigue tests were carried out on aluminum alloy under random loading spectrum. The fatigue fracture surfaces were observed in the scanning electron microscope (SEM) and great quantities of SEM micrographs were synthesized and saved in computer system. The space and morphology of several large-scale striations, which are expected to from at the relatively greater load range in loading block, were observed. The crack length for each loading blocks was decided in consideration of regularity and repetition of those striations. It is shown that the applicability of fractographic methods on the fatigue fracture surface under random loading spectrum.

• 한국안전학회지
• /
• 제8권4호
• /
• pp.47-53
• /
• 1993

The growth of short cracks can be well described in terms of the effective stress intensity factor range, which is calculated on the base of crack closure. The relation between the crack opening SIF and crack length is determined from the experimental results. The crack opening SIF of short cracks, Kop, can be predicted from the crack opening SIF at threshold of long crack, Kop.L. The growth rate of short cracks at notch root can be predicted from the crack opening SIF of short cracks, Kop, and the growth equation of long cracks in region II.

• 대한기계학회논문집A
• /
• 제28권1호
• /
• pp.55-62
• /
• 2004

Although the previous researches evaluated the fatigue behavior of glass fiber/epoxy laminates using the traditional fracture mechanism, their researches were not sufficient to do it: the damage zone of glass fiber/epoxy laminates was occurred at the delamination zone instead of the crack-metallic damages. Thus, previous researches were not applicable to the fatigue behavior of glass fiber/epoxy laminates. The major purpose of this study was to evaluate delamination behavior using the relationship between crack length and delamination width in hybrid composite material such as Al/GFRP laminate. The details of investigation were as follows : 1) Relationship between crack length and delamination width, 2) Relationship between delamination aspect ratio and delamination area rate, 3) Variation of delamination growth rate is attendant on delamination shape factors. The test results indicated that the delamination growth rate depends on delamination width delamination aspect ratio and delamination shape factors.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1999년도 춘계학술대회 논문집
• /
• pp.32-38
• /
• 1999

Fatigue crack propagation behavior for block load in high strength aluminum alloys was investigated in this study. The materials used in this study are aluminum alloy 5052-H32. Initial crack was made by applying cyclic load to a through crack with chevron notch. Crack length was measured from calibration curve, which was plotted by known crack length and resistance of standard specimens. Load was obtained from linear regression formula. Unloading elastic compliance method was applied to check the crack closure and cracked area. The present study results can be usefully applied to predicting the change of crack propagation rate, the crack closure, and the delay of crack propagation.

• 대한기계학회논문집A
• /
• 제27권5호
• /
• pp.673-680
• /
• 2003

This study verified the relationship between fracture mechanics parameters(ΔK, ΔK$\sub$eff/, K$\sub$max/) and X-ray parameters (${\alpha}$$\sub$r/, B) for SG365 steel at elevated temperature up to 300$^{\circ}C$. The fatigue crack propagation test were carried out and X-ray diffraction technique according to crack length direction was applied to fatigue fractured surface. The residual stress on the fracture surface was found to increase low ΔK region, reach to a maximum value at a certain value of K$\sub$max/ or ΔK and then decrease. Residual stress were independent on stress ratio by arrangement of ΔK and half value breadth were independent by the arrangement of K$\sub$max/. The equation of ${\alpha}$$\sub$r/ - ΔK was established by the experimental data. Therefore, tincture mechanics parameters could be estimated by the measurement of X-ray parameters.

• 한국해양공학회지
• /
• 제16권3호
• /
• pp.54-58
• /
• 2002

This study investigates a relationship between fracture mechanics parameters (Stress Intensity Factor Range: ΔK, Maximum Stress Intensity Factor; Kmax) and X-ray parameters (residual stress:$\sigma$r half-value breadth: B) for SG365 steel at elevated temperature up to 30$0^{\circ}C$. The fatigue crack propagation test were carried out and X-ray diffraction technique according to the direction of crack length was applied to fatigue fractured surface. The residual stress on the fracture surface was found to increase at low ΔK region, to reach a maximum value at a certain value of Kmax or ΔK and then to decrease. Residual stress was independent of stress ratio by arrangement of ΔK and half value breadth were independent of the arrangement of Kmax. The equation of $\sigma$r-ΔK was established by the experimental data. therefore, fracture mechanics parameters could be estimated by the measurement of X-ray parameters.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 추계학술대회논문집A
• /
• pp.317-323
• /
• 2001

This study verified the relationship between fracture mechanics parameters$({\Delta}K,\;{\Delta}K_{eff},\;K_{max})$ and X-ray parameters $(\sigma_r,\;B)$ for SG365 steel at elevated temperature up to $300^{\circ}C$. The fatigue crack propagation test were carried out and X-ray diffraction technique according to crack length direction was applied to fatigue fractured surface. The residual stress on the fracture surface was found to increase low ${\Delta}K$ region, reach to a maximum value at a certain value of $K_{max}\;or\;{\Delta}K$ and then decrease. Residual stress were independent on stress ratio by arrangement of ${\Delta}K$ and half value breadth were independent by the arrangement of $K_{max}$. The equation of $\sigma_r-{\Delta}K$ was established by the experimental data. Therefore, fracture mechanics parameters could be estimated by the measurement of X-ray parameters.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 1993년도 한국자동제어학술회의논문집(국제학술편); Seoul National University, Seoul; 20-22 Oct. 1993
• /
• pp.307-311
• /
• 1993

Research concerning gears included in rotating machines has been reported using the acoustic emission (AE) method, however, almost no research has been conducted using the AE method in regard to running gears in a bending fatigue processor spur gear teeth. Therefore, in this report, a power circulating-type gear testing machine was used and AE signals and crack length were measured in the bending fatigue process of case-hardened spur gear. Furthermore, the envelope of the AE signal was detected and various analysis were carried out in this data. In the course of the experiments, the following results were observed : the AE signal envelope consists mainly of contact frequency component and twice as many as this;two peaks of AE appear in each tooth contact by the tip corner contact ; as a result of the severe tip corner contact ; as a result of the severe tip corner contact with the sudden increase of crack length, AE signal becomes large.