• 대한기계학회논문집
• /
• 제11권6호
• /
• pp.867-876
• /
• 1987

본 연구에서는 보통강재인 SS 41 강을 열처리하여 얻은 M.E.F.복합조직강의 모상입경변화와 3.5% NaCl수용액의 pH변화 조건하에서 반복굽힘피로실험을 하여 부식 피로파괴에 미치는 영향에 대해 고찰하였다.

• 대한기계학회논문집A
• /
• 제27권12호
• /
• pp.2055-2060
• /
• 2003

Striation is a typical pattern observed on the fatigue fracture surface and the spacing is known to correspond to a macroscopic fatigue crack growth rate, and many models for the predict in the formation of such striation have been proposed. However, these theories and methods can't be applied under random loading spectrum. In this study, the fatigue tests were carried out on aluminum alloy under random loading spectrum. The fatigue fracture surfaces were observed in the scanning electron microscope (SEM) and great quantities of SEM micrographs were synthesized and saved in computer system. The space and morphology of several large-scale striations, which are expected to from at the relatively greater load range in loading block, were observed. The crack length for each loading blocks was decided in consideration of regularity and repetition of those striations. It is shown that the applicability of fractographic methods on the fatigue fracture surface under random loading spectrum.

• 한국생산제조학회지
• /
• 제19권4호
• /
• pp.462-468
• /
• 2010

Fatigue crack growth caused by surface defects is one of the most important subjects for the evaluation and the assurance of safety in pressure vessels, piping systems, LPG/LNG fuel tank and other various structures. So, this paper aims to investigate the relationship between the surface roughness of fracture CT specimens and the moments on the specimen when doing fatigue test for the evaluation and the assurance of safety of structures from fatigue crack deconstruction. In this experiment, the CT specimens were loaded by a fatigue testing machine with changing loads until they are broken. The surface roughness of the fracture CT specimens was measured using 3D precise shape measuring equipment and digital holography. As a result of this study, It was identified that the average roughnesses are similar at the positions that has a same moments by comparing the results with the moments on the specimen according to the position.

• 한국정밀공학회지
• /
• 제14권11호
• /
• pp.69-76
• /
• 1997

The rotating bending fatigue tests were performed using the specimens taken from Cr-Mo-V steel, widely sued in thermal power plant turbines, at various temperatures such as room temperature, 300 .deg. C, 425 .deg. C and 550 .deg. C. The characteristics of fatigue crack propagation were examined and analyzed by using fracture mechanics parameter. The plastic replica method was also applied in order to measure the crack length on the basis of serial observation of fatigue crack propagation behavior on the defected specimen surface. The fatigue crack propagation behavior of Cr-Mo-V steel was investigated within the frame work of elastic-plastic fracture mechanics. The propagation law of fatigue crack is obtained uniquely by using the term .sigma. $^{n}$ sub a/where .sigma. $_{a}$ is the service stress, a is the crack length and n is a constant. The values of constant n are nearly equal to 2.48, 2.60 and 8.61 at room temperature, 300 .deg. C and 425 .deg. C.

• 소성∙가공
• /
• 제10권3호
• /
• pp.179-184
• /
• 2001

The influence of the fatigue crack propagation by shot peening was studied in this paper. Fatigue tests were carried out on the unpeened and shot peened CT specimens. The changes of mechanical properties, residual stress, fatigue fracture surface etc. by shot peening were investigated. The mechanical properties, residual stress, fatigue surface etc. by shot peening were investigated. The mechanical peened specimen improved in fatigue life up to 14% by shot peening. The reason of increase in the fatigue life was closely related with the compressive residual stress, which was 519.7MPa on surface. Another reason was the constraint on crack opening on surface region, it is due to the decrease in slope of crack propagation direction.

• 한국정밀공학회지
• /
• 제18권11호
• /
• pp.174-178
• /
• 2001

Chrome-molybden steel or chrome steel for machine structures has been shown to excellent hardenability adding boron of a small amount at low carbon steel. These days, boron steel has been used high strength bolt and wear resistant components of construction equipment. SEM results showed classical fatigue fractures, consist with surface crack initiation. The specimens were tested repeatedly(9 times) under controlled load rotary bending fatigue tests. In the study, the fatigue crack initiation as well as fatigue crack growth behavior and the fracture mechanism were investigated through observations of fracture of boron steel surface(AISI 51B20).

• 한국주조공학회지
• /
• 제25권1호
• /
• pp.16-22
• /
• 2005

This study aims to investigate the effects of the microstructures and nodule type on the fatigue characteristics of cast iron. Fatigue tests were carried out in tension-tension mode using a servo-hydraulic testing machine with load control mode operating at a frequency of 15 Hz. The tests were conducted at stress ratio R=Kmin/Kmax, of 0.1. Initial crack ${\Dalta}K$ values were highly performed with increase in tensile strength of DCI fatigue specimens. ${\Dalta}K_{th}$ region, fatigue crack propagation was primarily advanced through cell boundary and in periphery of near nodule. Fatigue crack propagation rate of D2 consisted with 2Phase(Ferrite+Pearlite) was slow due to crack closure enhanced by crack deflection and occurred crack branching. The generation of crack branch was occurred due to interaction of crack-nodule. At Threshold and Paris zone, the fractographs of the fatigue fracture surface for DCI show typical striations of a ductile fracture and isolated cleavage planes near graphite. The effect of microstructure on fatigue crack propagation of GC strongly depends on the type of flake. The generation of crack branch occurred due to interaction of crack-nodule. The fractographs of the fatigue fracture surface for GC show cleavage plane along the flake graphite.

• 한국기계가공학회지
• /
• 제2권4호
• /
• pp.67-72
• /
• 2003

In this study, to investigate the effects of 2-step shot peening at the surface of spring steel, crack growth tests are conducted on spring steel and shot peened specimens. And then the residual stresses and fractographs are examined. The crack growth equation that can describe the whole crack growth behavior is used to evaluate the experiment results. The results show that fatigue crack glows slowly in the shot peened specimen than in the unpeened. And in the case of the 2-step shot peened specimen the initial stress intensity factor range and the fracture toughness is higher than the unpeened specimen due to the compressive residual stress. Fractographs show that the compressive residual stress of the surface suppress the fatigue crack opening and consequently slow crack growth rates.

• 한국기계가공학회지
• /
• 제3권4호
• /
• pp.88-94
• /
• 2004

High manganese steel was maintained stability of Non-Magnetics performance. Fatigue tests were carried out under constant stress amplitude, using a non-magnetic high manganese steel. The fatigue crack growth mechanism of the high manganese steel was clarified from results such as observation of crack growth path and fracture surface. The result of getting this study was shown as following: 1) Remarkably ${\Delta}Kth$ of the high manganese steel is big with about 3 times of the general steel product. 2) In the low ${\Delta}K$ value region, da/dN is dependent on Kmax, and in the high ${\Delta}K$ value region, it is dependent on ${\Delta}Keff$. The reason of this behavior is crack closure due to fracture surface roughness and fretting oxide. 3) It seems to ease the stress concentration of crack tip crack growth behavior in the ${\Delta}Kth$ vicinity by the generation of the secondary crack.

• 한국세라믹학회지
• /
• 제34권10호
• /
• pp.1053-1059
• /
• 1997

The dynamic fatigue behavior of alumina ceramics was observed at room temperature using four point bending system. The dynamic fatigue fracture strength and the dynamic fatigue lifetime were observed as a function of crosshead speed and the notch length. The notched specimen showed the smaller deviation in dynamic fatigue fracture strength than the unnotched specimen. The crack growth exponent n and the material constant A of the notched specimen could be represented as functions of the notch length. Fracture strength of the specimen calculated from the notch length, when the notch length was regarded as the crack size, was in good agreement with the measured 4 point bending strength. Fracture surface of the specimen showed the different fracture modes according to the crosshead speed. The four point flexural strength, fracture toughness, Young's modulus and Weibull modulus of the alumina were measured as 360 MPa, 3.91 MPa.m1/2, 159GPa, 17.64, respectively.