• Journal of Aerospace System Engineering
• /
• v.8 no.3
• /
• pp.41-46
• /
• 2014

Fatigue evaluations for the rotor blades of commercial or military rotorcraft have been carried out using the safe life concept since 1950s. Particularly, in the case of a rotor blade made of a composite material, a highly reliable fatigue life could be predicted by evaluation the cumulative damage using combination of fatigue life curve and load spectrum. However, there is a limit in adequately evaluating the strength reducing phenomena caused by damages or defects generated during the manufacturing process or impact damage induced by operational usages, using only the safe life concept. In this study, the fatigue evaluation process based on the damage tolerance concept is described and illustrated by means of successful application to substantiate the retirement time of composite rotor blades.

• 한국방재학회:학술대회논문집
• /
• 2008.02a
• /
• pp.317-320
• /
• 2008

Between traffic-induced vibration of a bridge and fatigue damage of its attached structures are very closely related. But any evaluation and design method considering the fatigue damage is not established yet. As an experimental method of evaluation of the fatigue durability, a method based on cumulative damage using a stress range histogram has been often used. However, to use the method, the fatigue durability of unmeasured points could not be evaluated. Then, in this paper, dynamic analysis of a sign frame on a bridge is carried out based on the vibration data of the bridge. And model optimization was performed for good agreement between measured responses and computed responses. As a result, we could get stress range histograms and calculate fatigue durability of unmeasured points.

• Journal of the Korean Society for Railway
• /
• v.9 no.2 s.33
• /
• pp.169-173
• /
• 2006

The major objective of this study is to investigate the fatigue life evaluation of immovability crossing for railway turnout by the field test. In railway engineering, an appliance is necessary to allow a vehicle to move from one track to another. This appliance came to be known technically as turnout. So, turnout is required very complex railway technologies such as rolling stock, track. Due to the plan under the application of high speed train, turnout are needed more stable far fatigue behaviors. It analyzed the mechanical behaviors of turnout crossing with propose its advanced technical type on the field test and fatigue evaluation far the dynamic fatigue characteristics. As a result, the advanced type crossing are obviously effective for the fatigue damage ratio and dynamic response which is non-modified type. The analytical and experimental study are carried out to investigate the passing path of contact surface and fatigue damage trend decrease dynamic stresses and deflections on advanced crossing type, And the advanced type reduce dynamic fatigue damage ratio and increase fatigue life(about each 38%) more than non-modified type. From the field test results of the servicing turnout crossing, it is evaluated that the modification of contact angle, weight, material and sectional properties is very effective fur ensure against fatigue risks.

• Proceedings of the KSR Conference
• /
• 2006.11b
• /
• pp.447-453
• /
• 2006

The major objective of this study is to investigate the fatigue behavior evaluation of immovability crossing for railway turnout by the field test. In railway engineering, an appliance is necessary to allow a vehicle to move from one track to another. This appliance came to be known technically as turnout. So, turnout is required very complex railway technologies such as rolling stock, track. Due to the plan under the application of high speed train, turnout are needed more stable for fatigue behaviors. It analyzed the mechanical behaviors of turnout crossing with propose its advanced technical type on the field test and fatigue evaluation for the dynamic fatigue characteristics. As a result, the advanced type crossing are obviously effective for the fatigue damage ratio and dynamic response which is non-modified type. The analytical and experimental study are carried out to investigate the passing path of contact surface and fatigue damage trend decrease dynamic stresses and deflections on advanced crossing type. And the advanced type reduce dynamic fatigue damage ratio and increase fatigue life(about each 38%)more than non-modified type. From the field test results of the servicing turnout crossing, it is evaluated that the modification of contact angle, weight, material and sectional properties is very effective for ensure against fatigue risks.

• Journal of Ocean Engineering and Technology
• /
• v.34 no.2
• /
• pp.120-127
• /
• 2020

Evaluation of fatigue strength considering the springing effect of very large container ships is crucial in the design stage. In this study, we established a fatigue strength evaluation method considering a linear springing component in the frequency domain. Based on a three-dimensional global model, a fluid-structure interaction analysis was performed and the modal superposition method was applied to determine the hot spot stress at the hatch corner of very large container ships. Fatigue damage was directly estimated using the stress transfer function with a linear springing response. Furthermore, we proposed a new methodology to apply the springing effect to fatigue damage using hull girder loads. Subsequently, we estimated the fatigue damage contribution due to linear springing components along the ship length. Finally, we discussed the practical application of the proposed methods.

• Journal of Korea Foundry Society
• /
• v.17 no.6
• /
• pp.577-584
• /
• 1997

Evaluation of rolling contact fatigue damage as well as material development for roll of rolling mill is being studied until quite recently. In this paper, a focus has been imposed on evaluating the rolling contact fatigue damage. In order for this, the accumulating process of rolling contact damage using the ferritic, pearlitic and bainitic DCI has been analyzed by X-ray diffraction technique. The main finds are; 1) The graphite in DCI is considered to be a cause of interfering in the redistribution of stress. Eventually, it results in the branching of crack. 2) The evaluation of rolling contact fatigue damage can be estimated in terms of the change of residual stress and/or a half-value breadth on surface during rolling contact.

• Structural Engineering and Mechanics
• /
• v.17 no.5
• /
• pp.655-670
• /
• 2004

This paper aims to evaluate the effect of typhoons on fatigue damage accumulation in steel decks of long-span suspension bridges. The strain-time histories at critical locations of deck sections of long-span bridges during different typhoons passing the bridge area are investigated by using on-line strain data acquired from the structural health monitoring system installed on the bridge. The fatigue damage models based on Miner's Law and Continuum Damage Mechanics (CDM) are applied to calculate the increment of fatigue damage due to the action of a typhoon. Accumulated fatigue damage during the typhoon is also calculated and compared between Miner's Law and the CDM method. It is found that for the Tsing Ma Bridge case, the stress spectrum generated by a typhoon is significantly different than that generated by normal traffic and its histogram shapes can be described approximately as a Rayleigh distribution. The influence of typhoon loading on accumulative fatigue damage is more significant than that due to normal traffic loading. The increment of fatigue damage generated by hourly stress spectrum for the maximum typhoon loading may be much greater than those for normal traffic loading. It is, therefore, concluded that it is necessary to evaluate typhoon induced fatigue damage for the purpose of accurately evaluating accumulative fatigue damage for long-span bridges located within typhoon prone regions.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.353-358
• /
• 2002

The purpose of this paper was to estimate the cumulative damage of pavement concrete by split tension fatigue test. The split tension fatigue test of variable amplitude loading were performed in two and three stages. The results of the fatigue test by variable amplitude loading showed that the sums of damage were greater than 1 in the increasing sequence loading tests, and less than 1 in the decreasing sequence loading tests. The remaining life estimated by equivalent damage theory was almost similar to that of experimental results.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.316-321
• /
• 2000

The role of fatigue on the surface damage of 5% chrome cold milling work roll is evaluated. Uniaxial and torsional fatigue tests are carried out, and the baseline data for fatigue life evaluation are established. An appropriate multiaxial fatigue parameter is developed from the fatigue data. Fatigue tests are also performed under compressive mean stresses, and a mean stress model is formulated. A computer program is developed to assess the interaction of fatigue and grinding of the roll. The fatigue damage is computed for selected servicing conditions. It is found that the fatigue damage can be an important issue when the effect of mean stress is ignored, however the fatigue damage is negligibly small when the effect of mean stress including the residual stresses currently used is fully accounted. The result indicates that spalling due to the growth of thermal shock cracks is more important than fatigue damage in roll surface failure.

• Structural Engineering and Mechanics
• /
• v.44 no.4
• /
• pp.417-429
• /
• 2012

Taking the superficial temperature increment as the major fatigue damage indicator, the infrared thermography was used to predict fatigue parameters (fatigue strength and S-N curve) of welded joints subjected to fatigue loading with a high mean stress, showing good predictions. The fatigue damage status, related to safety evaluation, was tightly correlated with the temperature field evolution of the hot-spot zone on the specimen surface. An energetic damage model, based on the energy accumulation, was developed to evaluate the residual fatigue life of the welded specimens undergoing cyclic loading, and a good agreement was presented. It is concluded that the infrared thermography can not only well predict the fatigue behavior of welded joints, but also can play an important role in health detection of structures subjected to mechanical loading.