• 대한기계학회논문집
• /
• 제3권3호
• /
• pp.116-123
• /
• 1979

On the basis of optical microscope and electro microscope observation for the fatigue fracture process of medium corbon martensitic structure produced by rapid heat treatment, mainly the abstracts of the studied results for the morphology of fatigue crack initiation process of high hardened steel are summarized as follows. Fatigue crack initiated from inclusion on the surface or subsurface. Above all the crack which initiated from inclusion exposed on the surface in as follows. (1) fatigue crack initiated from the boundary of the matrix and inclusion. (2) fatigue crack initiated at surrounding of small pit by drop out of inclusion.

• 대한기계학회논문집
• /
• 제10권1호
• /
• pp.62-69
• /
• 1986

본 연구에서는 표면균열의 전파거동에 관한 연구의 일환으로 경량화재료 로서 항공기 구조용으로 널리 사용되고 있는 7075-T651 알루미늄합금을 준비하고 제하탄성 compliance법을 이용하여 표면 및 깊이 방향의 균열진전거동의 특성을 밝히고져 한다.

• 대한기계학회논문집
• /
• 제19권4호
• /
• pp.929-940
• /
• 1995

The fatigue strength and fracture topography in the friction welded interface of high speed steel (HSS-Co) to SM55C carbon steel have been investigated through the fatigue test, SEM fractograph and EDS (energy dispersive spectrometer) analysis. Three kinds of specimens used in this research are the friction welded joints, HSS-Co and SM55C carbon steel with circumferential notch, saw notch and smooth, respectively. The notch sensitivity factor, .eta. of the friction welded joints is lower than that of the base materials, and that represents a superiority of the joint performance of FRW. Fracture topography of the FRW specimens with a notch showed a cleavage or brittle appearance, while that of the FRW smooth specimen appeared to be ductile. Furthermore, although fatigue crack likely initiated near the weld interface of the FRW smooth specimen, crack propagation continued into the HAZ of SM55C steel. Finally, fatigue fractures of the base materials were associated primarily with the inclusions located at the outer periphery of the specimen.