• Transactions of the Korean Society of Mechanical Engineers
• /
• v.3 no.3
• /
• pp.116-123
• /
• 1979

On the basis of optical microscope and electro microscope observation for the fatigue fracture process of medium corbon martensitic structure produced by rapid heat treatment, mainly the abstracts of the studied results for the morphology of fatigue crack initiation process of high hardened steel are summarized as follows. Fatigue crack initiated from inclusion on the surface or subsurface. Above all the crack which initiated from inclusion exposed on the surface in as follows. (1) fatigue crack initiated from the boundary of the matrix and inclusion. (2) fatigue crack initiated at surrounding of small pit by drop out of inclusion.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.1
• /
• pp.62-69
• /
• 1986

Fatigue surface crack growth was studied in 7075-T651 aluminum alloy plates subjected largely to bending loads. The surface crack length and its depth were measurement by the unloading elastic compliance method. The surface crack growth rate dc/dN, on the surface and da/dN, in the depth direction were obtained by the secant method. The stress intensity factor range .DELTA.K was computed by means of Newman and Raju equation. The aspect ratio a/c was presented in form of a/c=0.815-0.853(a/T). The effect of the stress ratio on the stable surface crack growth rates under increasing .DELTA.T is larger in lower .DELTA.K, while the relation between dc/dN, da/dN and the effective stress intensity factor range .DELTA.K$_{eff}$ is weakly dependent on the stress ratio.o.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.4
• /
• pp.929-940
• /
• 1995

The fatigue strength and fracture topography in the friction welded interface of high speed steel (HSS-Co) to SM55C carbon steel have been investigated through the fatigue test, SEM fractograph and EDS (energy dispersive spectrometer) analysis. Three kinds of specimens used in this research are the friction welded joints, HSS-Co and SM55C carbon steel with circumferential notch, saw notch and smooth, respectively. The notch sensitivity factor, .eta. of the friction welded joints is lower than that of the base materials, and that represents a superiority of the joint performance of FRW. Fracture topography of the FRW specimens with a notch showed a cleavage or brittle appearance, while that of the FRW smooth specimen appeared to be ductile. Furthermore, although fatigue crack likely initiated near the weld interface of the FRW smooth specimen, crack propagation continued into the HAZ of SM55C steel. Finally, fatigue fractures of the base materials were associated primarily with the inclusions located at the outer periphery of the specimen.