• Journal of the Korean Society of Propulsion Engineers
• /
• v.5 no.4
• /
• pp.20-30
• /
• 2001

This study represents the Nondestructive Test about impact damage of composite materials made by different lay-up patterns and degrees. For this study, they were examined by the drop test on composite materials of two type lap-up patterns with fabric and unidirectional prepreg and examined nondestructive test of those. Nondestructive methods were X-ray test with $ZnI_2$ penetrant and Ultrasonic C-scan. The defect detectability of X-ray and Ultrasonic test was compared according to defect species. And the amounts of damage on impacted zone wert compared according to impact energy on two type test specimens. At results, Ultrasonic test was more effective to detect delamination and Penetrant X-ray test was more effective to detect matrix crack and fiber fracture. There were some differences in defect shapes and grades according to lay-up patterns and degrees, and the trend appeared that matrix crack, delamination, fiber fracture occured and increasing defects sizes according to increasing impact energy.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.194-205
• /
• 1994

In this research, we attempt to fabricate an excellent CFRC(Carbon Fiber Reinforced Carbon), which has good thermal and mechanical properties, with 8H/satin woven fabric prepreg, high modulus and high strength type continuous carbon fiber and raw coal tar pitch(RCTP) matrix or THF soluble fraction(THFSP) matrix which has good graphitizability. Green bodies were fabricated with hot press molding technique and CFRC samples were made after carbonization, impregnation, recarbonization and graphitization steps. For the purpose of characterization of the physical properties, SEM, polarized light microscope, TGA were observed, and tested flexural strength, modulus and ILSS. After heat treating the THFSP matrix up to $2300^{\circ}C$, the value of $C_0$/2 was 3.380$\AA$, which is analogous to the structure of natural graphite and the value of 2$\theta$ is $26.276^{\circ}$ approached to the Bragg's angle of natural graphite. As a result of TGA to test the high temperature air oxidation, the THFSP matrix, graphitized up to $2300^{\circ}C$, exhibited the best air oxidation resistance. And mechanical properties were increased up to 65~70% as fiber volume fraction increased. Because of the good orientation graphitizability, the fracture surface of THFSP matrix CFRC is very good.