• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.75-79
• /
• 2014

This paper has an aim to study the effect of PWHT(for 140min. at $600^{\circ}C$) on FCAW weld metal properties (tensile, charpy impact and CTOD value) of YS 460 MPa steels for ship and offshore structures. On the basis of these study, it was found that strength was decreased and elongation was increased by PWHT. These phenomenon resulted from the reduction of acicula ferrite volume fraction by grain growth. Also, Charpy impact and CTOD value were decreased by PWHT. These phenomenon resulted from grain growth. Because the grain boundary grown by PWHT can play a role as crack initiation site and make the crack propagate more easily. Although weld metal properties were decreased by PWHT, tensile and impact properties could meet the class societies requirements for welds of YS 460 MPa steel, but decrease of fracture toughness need to be consider seriously.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.642-648
• /
• 2004

The microstructure and crack tip opening displacement (CTOD) of deposit weld metal were investigated for a 30 mm- thick plate welded with flux cored arc welding (FCAW) and submerged arc welding (SAW) processes. The CTOD test was carried out both as welded condition and as stress-relieved specimen by local compression. The crack growth rates in FCAW were faster than those in a SAW, and the acicular ferrite content by the SAW process was increased relatively more than that by the FCAW process. The fatigue crack growth rate in a welded specimen was faster than that in locally compressed specimen. The CTOD value of locally compressed specimens was lower than that of as welded specimen. Furthermore, the CTOD value tested with the SAW process was higher than that tested with the FCAW process.

• Journal of Welding and Joining
• /
• v.1 no.2
• /
• pp.76-82
• /
• 1983

The chemical composition of deposit metal by flux cored arc welding can be easily regulated though addition of deoxidizers and alloying elements in cored flux and fluxes of flux coored wire arc analogous to those of coated electrode. It is necessary to investigate the transfer and yield efficiency due to addition of necessary alloy elements in deposit metal. This report is made to intorduce an experimental equation from the relation between welding condition and extent of penetration, deposit metal and weld melt slag and to estimate transfer and yield efficiency of alloy components in fluxes through chemical analysis of deposit metal.

• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.54-59
• /
• 2010

The effects of welding parameters such as contact tip-to-work distance (CTWD), voltage, and current on the weld metal diffusible hydrogen contents (HD) were investigated and rationalized by the calculation of heating time and amount of heat generated in the extension length of flux cored wire. As CTWD increased from 15 to 25mm, HD decreased from 8.46 to 5.45mL/100g deposited metal. Calculations showed that, with an increase of CTWD, the amount of heat generated increased from 46 to 92J in addition to an increase of heating time. Increase of current from 250 to 320A, however, gave little variation of HD. It showed that no significant change in the amount of heat generated was found, and heating time was decreased with an increase of current. It also showed that CTWD is more influential than voltage in relatively lower heat input ranges, while voltage is more in higher input ranges

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.

• Journal of Ocean Engineering and Technology
• /
• v.27 no.5
• /
• pp.77-81
• /
• 2013

The effects of the welding parameters, contact tip-to-workpiece distance (CTWD), current, and voltage on the diffusible hydrogen content in weld metal deposited by self-shielded flux cored arc welding were investigated and rationalized by comparing the amount of heat generated in the extension length of the wire. This showed that as CTWD increased from 15mm to 25mm, the amount of heat generated was increased from 71.1J to 174.8J, and the hydrogen content was decreased from 11.3mL/100g to 5.9mL/100 g. Even if little difference was observed in the amount of heat generated, the hydrogen content was increased with an increase in voltage because of the longer arc length. A regression analysis showed that the regression coefficient of voltage in self-shielded flux cored arc welding is greater than that in $CO_2$ arc welding. This implies that voltage control is more important in self-shielded flux cored arc welding than in $CO_2$ arc welding.

• Journal of the Korean Society of Safety
• /
• v.34 no.6
• /
• pp.7-12
• /
• 2019

Flux Cored Arc Welding (FCAW), which has been widely used in many industries, was developed in the 1950s to supplement shortcomings of the Shielded Metal Arc Welding (SMAW). FCAW has an advantage in that it can weld regardless of postures and give good quality results in the filed with many different working conditions. In this study, SM490A (rolled steel for welding structural purpose) with different thicknesses (L:25T+R:30T) were welded using FCAW. Then the mechanical properties (tension test, bending test, hardness test, impact test and macro test) were analyzed and the following conclusions were drawn. In the tensile test, it exceeds the KS standard tensile strength range (400~510) in all welding positions, which means there is a problem in the tensile force transmission performance. In the bending test, it was found that most of the specimens did not exhibit surface rupture or other defects during bending test and they exhibit sufficient toughness even after plastic deformation. In the hardness test, all the results were lower than the standard value of 350 Hv of KS B 0893, which means they have good hardness. In the impact test, all results were larger than the KS reference value of 27J. In the macro test, they showed uniform structure state by the shape of the weld, and there was risk of lamination because no internal defects, bubbles, or impurities were found on the surface of the weld.

• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.118-120
• /
• 2005

대형구조물 제작 시에는 세라믹백킹재 등 백킹재를 이용한 편면용접법이 많이 채용되고 있다. 이처럼 백가우징이 적용되지 않는 편면용접법으로 용접 시공 시, 표면부에 비해 루트부의 충격성능이 열화되는 경향이 있다. 본 연구에서는 세라믹백킹재를 채용한 편면용접법의 루트부의 저온 충격성능을 확보할 수 있는 용착금속의 Ni 함량에 대해 고찰하고자 한다.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.65-73
• /
• 2011

Microstructural characteristics of two high strength (600 MPa & 800 MPa) weld metals produced by flux-cored arc welding process (FCAW) were evaluated. The 600 MPa grade weld metal was consisted of 75% acicular ferrite and 25% ferrite which was formed at relatively high temperature (grain boundary ferrite, widmanstatten ferrite, polygonal ferrite). However, the 800 MPa grade weld metal was composed of about 85% acicular ferrite and 15% low temperature forming phases (bainite, martensite). The prior austenite grain size of 800 MPa grade weld metal was decreased by solute drag force. The compositions and sizes of inclusions which are the dominant factors for the formation of acicular ferrite were analyzed by a transmission electron microscopy (TEM). In both 600 MPa and 800MPa grade weld metals, the inclusions were mainly consisted of Ti-oxide and Mn-oxide, and the average size of inclusions was $0.7{\mu}m$. The 800 MPa grade weld metal exhibited higher tensile strength and similar toughness compared with the 600 MPa grade weld metal. This result is mainly due to a higher fraction of low temperature products and a lower fraction of grain boundary ferrite in the 800 MPa grade weld metal.