• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2010년도 춘계학술발표대회 초록집
• /
• pp.61-61
• /
• 2010

The purpose of this study is to prevent the unstable fracture at the FCA butt weldment of hatch coaming deck in the ultra large containership during service life. In order to do it, the behavior of the embedded crack at the weldment under design loading conditions was evaluated in accordance with BS7910. Here, the level of primary stress induced by ship motion was evaluated by the design code of classification society and FEA. The level of residual stress as secondary stress was calculated in consideration of the restraint degree of weldment and welding heat input by using the predictive equation proposed by authors in the previous study. The fatigue crack growth rate at the weldment was evaluated using CT specimen in accordance with ASTM E647. According to the results, although the allowable defect for embedded crack specified in the classification society exists at the weldment, the occurrence possibility of unstable fracture at the weldment could not be negligible, regardless of CTOD value given in this study. So, in this study, the effect of initial defect size, welding heat input, restraint degree and CTOD on the fracture mechanical characteristics of embedded crack at the weldment was evaluated by the comprehensive fracture assessment. Based on the results, the design criteria including allowable defect, residual stress level and CTOD value was established to prevent the unstable fracture at the FCA butt weldment of hatch coaming deck in an ultra large containership during service life of 20years.

• Journal of Welding and Joining
• /
• 제32권2호
• /
• pp.48-53
• /
• 2014

This study was carried out to investigate the effect of postweld heat treatment(PWHT, 930, 1080, $1230^{\circ}C$) on the microstructure, phase formation, pitting corrosion and mechanical properties such as hardness, tensile strength and impact values of super duplex stainless steel(UNS S32750) multipass welds. Based on the microstructural examination and X-ray diffraction analysis, it was found that the ${\sigma}$ phase was formed in the welds heat treated at $930^{\circ}C$ in which the ferrite content greatly decreased into 5~10% in the welds. The secondary austenite was formed in the reheated zone of welds and redissolved into ferrite with increasing heat treatment temperatures. The tensile strength and impact values of welds heat treated at $930^{\circ}C$ were the lowest and revealed the brittle fracture surface. The weight loss by pitting corrosion increased with test temperatures. It was confirmed that pitting corrosion occurred mainly in secondary austenite of reheated zones. The postweld heat treatment temperature is recommended to be in the range of $1050{\sim}1150^{\circ}C$.

• Journal of Welding and Joining
• /
• 제26권3호
• /
• pp.23-29
• /
• 2008

The purpose of this study is to propose the proper fillet welding process for preventing the buckling distortion in thin panel welded structure. In order to do it, a heat input model for laser hybrid welding process was developed using FEA and experiment. The principal factors controlling the angular distortion and longitudinal shrinkage force caused by FCA and laser hybrid welding were identified as the welding heat input and weld rigidity using FEA. The predictive equations of angular distortion and longitudinal shrinkage force for each welding process were formulated as a function of the principal factors proposed. With the predictive equations, the buckling distortion at the thin panel welded structure with welding process was evaluated and compared using nonlinear buckling analysis and STEM(simplified thermo elastic method). Based on the results, the best way to prevent the buckling distortion at the given welded panel structures was identified as an intermittent FCA welding.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.102-102
• /
• 2009

The purpose of this study is to establish the predictive equation of transversal residual stress at the thick weldment of large container ship. In order to do it, the variables used for this study were restraint degree, yield strength of base material, thickness of weldment and welding heat input. Here, the level of restraint degree at the thick weldment of container ship having the various welding sequence was calculated using FEA. From the result, the h-type specimen was designed to simulate the level of restraint degree at the actual weldment of containership. With H-type test specimen designed, the effect of the variables on the distribution of transversal residual stress at the weldment in a container ship was evaluated using the comprehensive FEA. Based on the results, the predictive equations of mean value and the distribution of transverse residual stress in each location of residual stress were established using dimensional analysis and multiple-regression method. The validation of predictive equations was verified by comparing with measured results by XRD in the actual weldment of the ship.

• Journal of Welding and Joining
• /
• 제23권4호
• /
• pp.27-33
• /
• 2005

Quantitative evaluation was performed on the microstructure of flux-cored arc(FCA) weld metal using a method blown as IIW scheme. It was mainly intended to figure out any practical difficulties in applying this method and also to provide the consumable makers with basic guide line in developing FCA welding consumables far better properties. Assessment of the experimental results showed IIW scheme was quite reliable in the low heat input range where the acicular ferrite was a major constituent. However, in the high heat input range, some scatter was noticed as the other phases like grain boundary ferrite and Widmansttaten ferrite become dominant. It implies that the accuracy of IIW scheme depends on the faction of microstructural constituents and it become worse as the fraction of latter two phases increases. This tendency was discussed in terms of the characteristics of those two phases. In addition, base line microstructure of rutile type FCA weld metal was addressed for developing new FCA welding consumables intended for higher heat input welding.

• Journal of Welding and Joining
• /
• 제34권3호
• /
• pp.61-68
• /
• 2016

Characteristics of dissimilar metal welds between alloy steel ASTM A387 Gr. 91 and carbon steel ASTM A516 Gr.70 made with Flux cored arc welding(FCAW) have been evaluated in terms of microstructure, mechanical strength, chemical analysis by EDS as well as corrosion test. Three heat inputs of 15.0, 22.5, 30.0kJ/cm were employed to make joints of dissimilar metals with E91T1-B9C wire. Post-weld heat treatment was carried out at $750^{\circ}C$ for 2.5 h. Based on microstructural examination, tempered martensite and lower bainite were formed in first layer of weld metal. The amount of tempered martensite was decreased and the amount of lower bainite was increased with increasing heat input and layer. Heat affected zone of alloy steel showed the highest hardness due to the formation of tempered Martensite and lower Bainite. Tensile strengths of dissimilar welds decreased with increasing heat inputs. Dissimilar welds seemed to have a good hot cracking resistance due to the low HCS index below 4. The salt spray test of dissimilar metals showed that the corrosion rate increased with increasing heat inputs due to the increase of the amount of lower Bainite.

• Journal of Welding and Joining
• /
• 제35권3호
• /
• pp.68-74
• /
• 2017

Characteristics of dissimilar metal welds between alloy steel ASTM A387 Gr. 91 and carbon steel ASTM A516 Gr.70 made with Flux cored arc welding(FCAW) have been evaluated in terms of microstructure, mechanical strength, chemical analysis by EDS as well as corrosion test. Three heat inputs of 15.0, 22.5, 30.0kJ/cm were employed to make joints of dissimilar metals with E71T-1C wire. Post-weld heat treatment was carried out at $750^{\circ}C$ for 2.5 h. Based on microstructural examination, Intragranular polygonal ferrite and grainboundary ferrite were formed only in first layer of weld metal. Another layers consisted of acicular ferrite and $Widmannst{\ddot{a}}tten$ ferrite. The amount of acicular ferrite was increased with decreasing heat input and layer. Heat affected zone of alloy steel showed the highest hardness due to the formation of tempered martensite and lower bainite. Lower and upper bainite were formed in heat affected zone of carbon steel. Tensile strengths of dissimilar metal welds decreased with increasing heat inputs. Dissimilar metal welds showed a good hot cracking resistance due to the low HCS index below 4. The salt spray test of dissimilar metals welds showed that the weight loss rate by corrosion below 170 hours was decreased with increasing heat inputs due to the increase of the amount of acicular ferrite.

• Journal of Welding and Joining
• /
• 제27권5호
• /
• pp.42-48
• /
• 2009

Pipe welding is used in various ranges such as civil engineering and ship building engineering. Until now, many technicians work for pipe welding manually under harmful, dangerous and difficult conditions. So it is necessary to install automation process. For automation pipe welding, relation between welding parameters & bead shape should be considered. Using this relation, bead shape could be expected from welding parameters. FCAW was used in this study. Instead of pipe workpiece, fillet joint plate is used, which were inclined 0,45,90,135,180 degree. By analyzing between welding parameters (current, welding speed, voltage) and bead shape parameters with non-linear multiple regression, bead shape parameters could be expected. Piecewise Cubic Hermite Interpolation was used to expect smooth curved bead shape with bead shape parameters. From these processes, bead shape could be expected from welding parameters.

• Journal of Welding and Joining
• /
• 제34권4호
• /
• pp.28-33
• /
• 2016

The purpose of this study is to evaluate the redistribution of transverse residual stress in the multi-pass FCA butt weld of YP47 in the hatch coaming top plate of ultra large size containership under the tensile cyclic load. In order to do it, the configuration of modified H type specimen including restraint length was first designed to simulate the restraint condition of the butt weld in hatch coaming top plate. FE analysis procedure for evaluating the transverse residual stress was verified by comparing the calculated mean and surface residual stresses with the measured results in the test specimen. After that, the effect of the cyclic load on the redistribution of transverse residual stress was evaluated by comprehensive FEA. From the results, it was found that although the maximum transverse residual stress decreased with an increase in the applied maximum load, the effect of the cyclic load on the mean residual stress is small enough to be negligible. It is because the maximum stress of the ship corresponding to the probability of 10E-8 is less than 70% of yield stress of the weld.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.51-53
• /
• 2006

The purpose of this study is to establish the predictive equation of angular distortion and longitudinal shrinkage force at the intermittent fillet weldment using FEA and experiment. The angular distortion and shrinkage force of the intermittent fillet weldment linearly increases with an increase in the ratio of weld length(Lw) to weld span(Ls). Based on the results, The predictive equation of distortion at the intermittent fillet weldment was defined as a linear function of Lw/Ls and the predictive equation of the distortion for continuous fillet weldment.