• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.331-331
• /
• 2012

In this study, we investigated morphology observation of nanostructured Ti-25Ta-xZr alloys. Ti-25Ta-(3wt%~15 wt%) Zr alloys were prepared by a vacuum arc-melting furnace. Formation of nanotubular structure was achieved by an electrochemical method in 1M $H_3PO_4$ electrolytes containing 0.8%wt.% NaF. Nanotube morphology depended on alloying elements.

• The Korean Journal of Ceramics
• /
• 제4권3호
• /
• pp.249-253
• /
• 1998

The influence of PbO additive on dielectric properties and sintering behavior of $(Pb_{0.46}Ca_{0.55})$ {$(Fe__1/2}Nb_{1/2}){0.9}Sn_{{0.1}$}$O_3$ ceramics has been investigated. The incorporation of a limited excess PbO ($\leq$2.0 wt. %) in the starting materials is quite beneficial for densification in the temperature range of 1150~$1175^{\circ}C$ in air. At a small doping level (0.8 wt. %) the ceramics prepared from powders calcined at $900^{\circ}C$ showed the best dielectric properties. The dielectric constants ($\varepsilon_r$) and Q.f were found to be 85.8~85.6 and 8530~8600 GHz, respectively. The temperature coefficient of resonant frequency ($\tau_f$) varied in the range of -2~4 $ppm/^{\circ}C$. Examination of the microstructure as well as analysis of the second phases in these materials revealed the presence of the pyrochlore-type phase which is detrimental to the dielectrics.

• 자원리싸이클링
• /
• 제10권4호
• /
• pp.42-47
• /
• 2001

알루미늄 드로스와 장석을 이용하여 무기발포재의 제조 가능성을 검토하여 폐기물인 알루미늄 드로스의 재활용 및 자원화의 다양성을 제시하기 위한 실험을 행하였다. 소성한 발포재의 경우 장석은 소성온도에서 용해되어 비정질상으로 전이하고 드로스 중의 성분들이 Spinel($MgA1_2$$O_4$)을 형성한다. 장석 55 wt%, 드로스 40 wt%, 벤토나이트 5 wt% 시료의 경우 소성온도 $1220^{\circ}C$에서 소성시간이 증가할수록 밀도는 0.91에서 0.65까지 감소하고, 흡수율은 약 2.5에서 1.7%의 범위의 값을 나타냈다. $1220^{\circ}C$에서 30분 소성할 경우 굽힘강도는 10.8 MPa이며, 열전도도는 0.34 W/m.K로서 최대치를 나타냈다.

• 한국환경과학회지
• /
• 제22권8호
• /
• pp.1019-1027
• /
• 2013

Sulfur hexa-fluoride has been used as a etching gas in semiconductor industry. From the globally environmental issues, it is urgent to control the emissions of this significant greenhouse gas. The main objective of this experimental investigation was to find the effective catalyst for $SF_6$ decomposition. The precursor catalyst of hexa-aluminate was prepared to investigate the catalytic activity and stability. The precursor catalyst of hexa-aluminate was modified with Ni to enhance the catalytic activities and stability. The catalytic activity for $SF_6$ decomposition increased by the addition of Ni and maximized at 6wt% addition of Ni. The addition of 6wt% Ni in precursor catalyst of hexa-aluminate improved the resistant to the HF and reduced the crystallization and phase transition of catalyst.

• 한국재료학회지
• /
• 제8권12호
• /
• pp.1127-1132
• /
• 1998

본 연구에서는 Al-10wt%Ti-4wt%Fe 복합재료를 in-situ공정으로 제조할 수 있는 가능성 및 2 원계 Al-10wt%Ti 복합재료의 낮은 기계적 성질(탄성계수, 상온 고온강도, 내마모특성 등)을 PM SiC/2124 복합재료 수준 흑은 그 이상으로 향상시킬 수 있는 가능성을 조사하였다. 제조된 Al-10wt%Ti-4wt%Fe 합금은 불연속 SiC 강화상으로 보강된 Al-기지 복합재료($SiC{w}$/2124)와 유사한 미세구조를 보여주었으며, 탄성계수 및 인장강도, 내마모성질 등의 기계적 특성이 2원계 Al-10%Ti 합금각 비교해 현저하게 향상되었음이 관찰되었다. 위의 결과는 초정 $Al_3Ti$상 외에도 Fe 원소의 첨가를 통한 추가적인 $Al_{x}Fe$의 분산강화 효과에 기인한 것으로 해석된다.

• The Journal of Korean Physical Therapy
• /
• 제29권5호
• /
• pp.246-254
• /
• 2017

Purpose: Previous studies have reported that action observation training has beneficial effects on enhancing the motor task, such as balance and gait functions. On the other hand, there have been few studies combined with action observation training and auditory feedback. The purpose of this study was to determine the effects of action observation training with auditory feedback on the gait function in stroke patients with hemiparesis Methods: A total of 24 inpatients with post-stroke hemiparesis were assigned randomly to either an experimental group 1 (EG 1, n=8), experiment group 2 (EG 2, n=8), control group (CG, n=8, EG 1). The EG 2 and CG watched video clip demonstrating three functional walking tasks with auditory feedback, without auditory feedback, and showing a landscape image, respectively. The exercise program consisted of 30 minutes, five times a week, for four weeks. The participants were measured to 10MWT (10 m walk test), 6MWT (6 minutes walking distance test), TUG (timed up and go test), DGI (dynamic gait index), time and steps of F8WT (figure-of-8 walk test). Results: In the intra-group comparison after the intervention, EG 1 and EG 2 showed a significantly different gait function (10MWT, 6MWT, DGI, TUG, F8WT) (p<0.05). In the inter-group comparison after intervention, EG 1 showed significant improvements in the entire gait parameters and EG 2 only showed significant improvement in DGI and TUG compared to CG (p<0.05). Conclusion: These findings show that action observation training with auditory feedback may be used beneficially for improving the gait function of stroke patients with hemiparesis.

• Membrane and Water Treatment
• /
• 제8권5호
• /
• pp.483-498
• /
• 2017

Novel mixed matrix membranes of Sodium Alginate (NaAlg) were developed by the incorporation ofunmodified, modified Phosphomolybdic acid (PMA) then cross-linked with glutaraldehyde externally. These membranes were prepared by the solution casting technique. Pervaporation (PV) experiments have been performed with pure NaAlg, unmodified NaAlg-PMA5, NaAlg-PMA10, modified NaAlg-mPMA5, and NaAlg-mPMA10 (wt. % of PMA 5 and 10) at 30, 40 and $50^{\circ}C$, to separate water-isopropanol feed mixtures containing 10-30 wt. % of water. Pervaporation results of NaAlg-mPMA10 produced a highest separation factor of 9028 with a flux of $0.269kg/m^2.h$ for 10 wt. % of water containing feed mixture. Both separation factor and flux for water increased significantly with increasing content of mPMA into NaAlg; a significant improvement in PV performance was observed for NaAlg-mPMA5 and NaAlg-mPMA10 membranes when compared to pure NaAlg& PMA-5, PMA-10 membrane.

• 한국전기전자재료학회논문지
• /
• 제15권12호
• /
• pp.1027-1032
• /
• 2002

(Pb$\_$0.4/Ca$\_$0.6/)(Fe$\_$1/2/Nb$\_$1/2/)O$_3$ system was modified by 10 mol% Pb(Zn$\_$1/2/W$\_$1/2/)O$_3$ addition and their sinterability and microwave properties were investigated as a function of the amount of flux (0.975PbO-0.025SnO$_2$). With increasing flux content, single perovskite phase was maintained up to 3 wt% flux addition and further addition led to the presence of Pb-rich second phase which was confirmed by EDS analysis. The apparent densities of PCFN-PZW specimen increased and showed maximum values at 2.5 wt% flux addition for the Ts=1000$^{\circ}C$ and 2.0wt% flux addition for the Ts=1050$^{\circ}C$, respectively. The dielectric constant and Q$.$f values strongly depended on the variation of density and microstructure, where the optimum values of $\varepsilon$$\_$r/ = 91.95, Q$.$f = 5938GHz, TCF = +8.15ppm/$^{\circ}C$ were obtained for the 2.5wt% flux added PCFN-PZW specimen sintered at 1000$^{\circ}C$ for 4h.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1386-1393
• /
• 2018

The solubility of $TiO_2$ in $NaF-CaF_2-BaF_2$ ternary eutectic melts was investigated at the temperature range of $1025-1150^{\circ}C$. The least-squares equation was obtained from the relationship between the reciprocal temperature and the natural logarithm of the titanium concentration in the melts saturated with $TiO_2$. The corresponding partial molar enthalpy of dissolution of $TiO_2$ was found to be 188 kJ/mol. The titanium saturation concentration was 3.73 wt% at $1100^{\circ}C$. From the titanium concentration change with the added amount of $TiO_2$ at different holding time after a final stirring, it was found that not only complete dissolution of $TiO_2$ but also enough sedimentation of excessive $TiO_2$ should be guaranteed to obtain more reliable solubility data. The holding time of 10 h was found to be enough for the excessive $TiO_2$ particles to settle down in our experimental conditions. It is noteworthy that in case of adding $TiO_2$ in excess of its solubility, the $Ba_{1.12}(Ti_8O_{16})$ phase was observed at the lower and bottom of the solidified salt ingots.

• 한국전기전자재료학회논문지
• /
• 제16권12S호
• /
• pp.1205-1209
• /
• 2003

We investigated the effects of calcination temperatures on the sintering behaviors and microwave dielectric Properties of (Z $n_{0.8}$M $g_{0.2}$)Ti $O_3$ system. Highly densified samples were obtained at the sintering temperatures below 100$0^{\circ}C$ with additions of 0.45 wt.%B $i_2$ $O_3$ and 0.55 wt.% $V_2$ $O_{5}$. From the examination of the existing phases and microstructures before and after sintering of (Z $n_{0.8}$M $g_{0.2}$)Ti $O_3$ system which is calcined at the various temperatures ranging from 80$0^{\circ}C$ to 100$0^{\circ}C$, it was found that higher Q${\times}$ $f_{o}$ values were obtained when unreacted phases in calcined body were reduced. When calcined at 100$0^{\circ}C$ and sintered at 90$0^{\circ}C$, it consists of hexagonal as. a main phase with uniform microstructure and exhibits Q${\times}$ $f_{o}$ value of 42,000 GHz and dielectric constant of 22. 22. 22.