• 한국세라믹학회지
• /
• 제29권6호
• /
• pp.463-470
• /
• 1992

Corundum single crystals were grown in cryolite flux with the composition of Na3AlF6:Al2O3=80:20 wt%. This mixture was melted at 115$0^{\circ}C$, followed by slow cooling at a rate of 2$^{\circ}C$/hr to 96$0^{\circ}C$. And by adding of La2O3 to the flux, the change of crystal forms were observed. Crystal forms of corundum grown in cryolite flux had the habits of hexagonal plate which consist of well developed {0001} face and small {101} face. As La2O3 was added and its content was increased, {223} and {110} faces were developed, and crystal habits of equidimensional forms changed into hexagonal prism form. In a charge of 8 mole% B2O3, Al2O3:La2O3=15:1, transparent corundum single crystals of equent form were grown. As the content of B2O3 was increased, twineed crystals which have twin law of 2-fold parallel to [0001], and composition plane of (110) were grown.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권1호
• /
• pp.21-26
• /
• 1995

Highly sensitive and mechanically stable gas sensors have been fabricated using the microfabrication and micromaching techniques. The sensing material used to detect the offensive trimethylarnine ((CH$_{3}$)$_{3}$N) gas is 6 wt% $Al_{2}$O$_{3}$-doped, 1000.angs.-thick ZnO deposited by r. f. magnetron sputtering. The optimum operating temperature of the sensor is 350.deg.C and the corresponding heater power is about 85mW. Excellent thermal insulation is achieved by the use of a double-layer structure of 0.2.mu.m -thick silicon nitride and 1.4.mu.m-thick phosphosilicate glass(PSG) prepared by low pressure chemical vapor deposition(LPCVD) and atmospheric pressure chemical vapor deposition(APCVD), respectively. The sensors are mechanically stable enough to endure at least 43, 200 heat cycles between room temperature and 350.deg. C.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 추계학술대회 논문집
• /
• pp.138-138
• /
• 2015

In this study, highly ordered nanotubular surface of Ti-25Ta-xHf alloys for dental applications was researched. Ti-25Ta-xHf alloys were contained from 0% to 15% Hf content. Formation of nanotubular structure was achieved by an electrochemical method in 1M $H_3PO_4$ electrolytes containing 0.8%wt. % NaF.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1487-1489
• /
• 1994

$(Zr_{0.65}Sn_{0.35})Ti_{1.04}O_4$ system which has a dielectric constant, low dielectric loss and temperature coefficient was investigated. Temperature coefficient varied from positive to negative with increasing of NiO. For the NiO content 1.0wt%. i.e $(Zr_{0.65}Sn_{0.35})Ti_{1.04}O_4$, the ceramic showed very good dielectric properties such as ${\epsilon}$=37.8, $Q{\times}f_o=49.000$ and ${\tau}_r= 4{\pm}1ppm/^{\circ}C$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.510-514
• /
• 1997

The thin film that is electrically conductive and optically transparent is called conductive transparent thin film. ITO(Indium-Tin Oxide) which is a kind of conductive transparent thin film has been widely used in solar cell, transparent electrical heater, selective optical filter, FDP(Flat Display Panel) such as LCD(Liquid Crystal Display), PDP(Plasma Display Panel) and so on. Especially in PDP, ITO films is used as a transparent electrode in order to maintain discharge and decrease consumption power through the improvement of cell structure. In this study, we prepared ITO by reactive r.f. sputtering with indium-tin(Sn 10wt%) alloy target instead of indium-tin oxide target. The ITO films deposited at low temperature 15$0^{\circ}C$ and 8% $O_2$. Partial pressure showed about 3.6 Ω/$\square$. At the end of firing, the resistance of ITO was decreased, the optical transparence was improved above 90%.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.108-108
• /
• 2015

In order to investigate on hydroxyapatite precipitation phenomena on nanotubular Ti-29Nb-xHf ternary alloys, Ti-29Nb-xHf alloys contained (0% to 15%) Hf were manufactured using arc melting furnace. Formation of nanotubular structure was achieved by an electrochemical method in 1M $H_3PO_4$ electrolytes containing 0.8%wt. % NaF. Electrochemical deposition was carried out using cyclic and voltammetry(CV) method at $85^{\circ}C$ in $5mM\;Ca(NO_3)_2+3mM\;NH_4H_2PO_4$. HA coating on nanotube formed Ti-29Nb-xHf ternary alloys showed a good wettability.

• 한국정밀공학회지
• /
• 제16권11호
• /
• pp.148-157
• /
• 1999

The objective of this study is to investigate the effect of three main chemical compositions(Mg, Zn, Si) on extrudability of 7xxx Al alloy with high tensile strength. A few Al alloys based on 7xxx alloys were metal mold cast with various weight*%) of Mg 0.3-1.2%, Zn 5.0-8.0% and Si 0.4-0.7%, to envestigate the effects of extrudability, as well as mechanical properties. To measure the extrudability of cast billets, maximum extrusion pressure and surface temperature at die exit before tearing occurs were obtained by experiment and simulation of thermo-viscoplastic F.E.M. Also the yield and tensile strength of extruded products were tested.

• Bulletin of the Korean Chemical Society
• /
• 제35권8호
• /
• pp.2342-2348
• /
• 2014

Poly(lactic-co-glycolic acid) (PLGA) were grafted to both ends of Pluronic$^{(R)}$ F68 ($(EO)_{75}(PO)_{30}(EO)_{75}$) triblock copolymer to produce poly{(lactic acid)$_m$-co-(glycolic acid)$_n$}-b-poly(ethylene oxide)$_{75}$-b-poly(propylene oxide)$_{30}$-b-poly(ethylene oxide)$_{75}$-b-poly{(lactic acid)$_m$-co-(glycolic acid)$_n$} (PLGA-F68-PLGA) pentablock copolymers. Molecular weights of PLGA blocks were controlled and five kinds of pentablock copolymers with different PLGA block lengths were synthesized using in-situ ring-opening polymerization of D,L-lactide and glycolide with tin(II) 2-ethylhexanoate ($Sn(Oct)_2$) catalyst. PLGA-F68-PLGA pentablock copolymers were characterized by $^1H$- and $^{13}C$-NMR, GPC, and TGA. The numbers (2m, 2n) of repeating units for lactic acid and glycolic acid inside PLGA segments were obtained as (48, 17), (90, 23), (125, 40), (180, 59), and (246, 64), with $^1H$-NMR measurement. From NMR data, the resultant molecular weights were determined in the range of 12,700-29,700, which were similar to those obtained from GPC. Polydispersity index was increased in the range of 1.32-1.91 as the content of PLGA blocks increased. TG and DTG thermograms showed discrete degradation traces for PLGA and F68 blocks, which indicate the weight fractions of PLGA blocks in pentablock copolymers can be calculated by TG profile and it is possible to remove PLGA block selectively. Hydrodynamic radius and radius of gyration of pentablock copolymer micelle were obtained in the range of 46-68 nm and 31-49 nm, respectively, in very dilute (i.e. 0.005 wt %) aqueous solution of THF:$H_2O$ = 10:90 by volume at $25^{\circ}C$.

• 한국환경농학회지
• /
• 제33권4호
• /
• pp.245-253
• /
• 2014

패화석에 의한 카드뮴의 용출특성과 부동화 기작을 구명하기 위해 우리나라의 대표적인 석회비료인 소석회를 비교구로 선정하여 실내에서 비교시험을 실시하였다. 두 칼슘제재의 처리량을 증가시킴에 따라 토양의 pH와 음하전도는 증가하는 결과를 나타내었으나 소석회가 패화석에 비해 토양의 pH와 음하전도를 증대시키는 효과가 더욱 우수하였다. 소석회는 패화석에 비해 1 N $NH_4OAc$ extractable Cd의 함량을 감소시키는 효과가 더욱 우수한 것으로 조사된 반면 패화석은 소석회에 비해 0.1 N HCl extracble Cd의 함량을 감소시키는 효과가 더욱 우수한 것으로 조사되었다. 본 연구에서 소석회에 의한 카드뮴의 부동화기작은 주로 토양의 음하전도의 증대에 기인된 카드뮴의 흡착에 의한 것으로 판단된다. 그러나 패화석에 의한 카드뮴의 부동화기작은 음하전도의 증대에 기인된 카드뮴의 흡착 이외에 부가적으로 다공성의 패화석 내부에 카드뮴이 물리적으로 흡착되어지는 것에 기인되는 것으로 판단된다. 결과적으로 패화석은 토양 내 식물이 이용하기 쉬운 형태의 카드뮴의 함량(F2)을 저감시키고 식물이 거의 이용하기 힘든 형태의 카드뮴의 함량(F5)을 증가시켜 카드뮴으로 오염되어진 농경지에서 식물의 카드뮴 흡수를 저감시키기 위한 토양개량제로써의 활용가능성이 높은 것으로 평가되었다.

• 한국건설순환자원학회논문집
• /
• 제10권3호
• /
• pp.185-194
• /
• 2022

커피는 세계에서 가장 많이 소비되는 음료 중 하나이며 석유에 이어 두 번째로 많이 거래되는 상품이다. 커피의 수요가 많은 만큼 커피 산업에서는 독성이 있고 심각한 환경문제를 일으키는 다량의 폐기물이 생성된다. 본 연구는 사용된 커피찌꺼기(SCG)를 재활용하여 콘크리트 제조 시 시멘트를 대체하는 혼화재로써의 활용가능성을 확인하는 것을 목표로 한다. 커피찌꺼기를 재활용하기 위해서 커피찌꺼기는 수분 제거를 위해 건조되고 850℃의 소성로에서 8시간 동안 소성하며, 탄화된 커피찌꺼기는 볼밀 분쇄를 통해 커피찌꺼기 애시(CGA)로 제조된다. 제조된 커피찌꺼기 애시의 화학성분 분석은 XRF로 수행하였으며, 화학성분 분석결과 커피찌꺼기 애시의 주요 성분은 K₂O(51.74 %), CaO(15.92 %), P₂O₅(14.39 %)이며 MgO(7.74 %), SO₃(6.89 %)의 부성분과 소량의 F₂O₃(0.66 %), SiO₂(0.59 %), Al₂O₃(0.31 %)가 함량되어 있다. 물리 역학적 특성을 평가하기 위해 커피찌꺼기 애시를 5 %, 10 %, 15 % 중량 치환하여 수행하였다. 품질 시험결과, 커피찌꺼기 애시가 5 % 치환된 CGA 5의 28일 활성지수는 80 %이며, 플로 값 비는 96 %로 플라이 애시 2종의 품질기준을 만족하는 것으로 나타났다. 모르타르의 역학적 시험결과로부터 커피찌꺼기 5 %가 포함된 시편에서 최적의 결과를 확인할 수 있었으며, 우수한 기계적, 물리적 특성을 보여주었다.