• Korean Journal of Crystallography
• /
• v.12 no.4
• /
• pp.197-206
• /
• 2001

A stoichiometric mixture of evaporating materials for AgInS₂ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films. AgInS₂ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy(HWE)system. The source and substrate temperatures were 680℃ and 410℃, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of AgInS₂ single crystal thin film mea-sured from Hall effect by van der Pauw method are 9.35×10/sup 16/㎤ and 294㎠/V·s at 293K respectively. The temperature dependence of the energy band gap of the AgInS₂ obtained from the absorption spectra was well described by the Varshni's relation , E/sub g/(T)=2.1365eV-(9.89×10/sup-3/eV/K/)T²(T+2930K). The crystal field and the spin-orbit splitting energies for the valence band of the AgInS₂ have been estimated to be 0.1541eV and 0.0129 eV, respectively, by means of the photocur-rent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the Δso definitely exists in the Γ/sub 5/ states of the valence band of the AgInS₂ /GaAs epilayer. The three photo-current peaks ovserved at 10K are ascribed to the A₁-, B-₁and C₁-exction peaks for n=1.

• Journal of Sensor Science and Technology
• /
• v.13 no.2
• /
• pp.157-167
• /
• 2004

A stoichiometric mixture of evaporating materials for $CuAlSe_{2}$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CuAlSe_{2}$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $680^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuAlSe_{2}$ single crystal thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}cm^{-3}$ and $295cm^{2}/V{\codt}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuAlSe_{2}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}(T)$ = 2.8382 eV - ($8.68{\circ}10^{-4}$ eV/K)$T^{2}$/(T + 155 K). The crystal field and the spin-orbit splitting energies for the valence band of the $CuAlSe_{2}$ have been estimated to be 0.2026 eV and 0.2165 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_{5}$ states of the valence band of the $CuAlSe_{2}$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1-}$, $B_{1-}$, and $C_{1-}$ exciton peaks for n = 1.

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.889-894
• /
• 2001

2wt% $Al_2O_3-doped$ ZnO (AZO) thin films were deposited on sapphire (0001) single crystal substrate by parellel type rf magnetron sputtering at 55$0^{\circ}C$. The as-grown AZO thin films was polycrystalline and showed only broad deep defect-level photoluminescence (PL). In order to examine the change of PL property, AZO thin films were annealed in $N_2$ (N-AZO) and $H_2$ (H-AZO) at the temperature of $600^{\circ}C$~$1000^{\circ}C$ through rapid thermal annealing. After annealed at $800^{\circ}C$, N-AZO shows near band edge emission (NBE) with very small deep-level emission, and then N-AZO annealed at $900^{\circ}C$ shows only sharp NBE with 219 meV FWHM. In Comparison with N-AZO, H-AZO exhibits very interesting PL features. After $600^{\circ}C$ annealing, deep defect-level emission was quire quenched and NBE around 382 nm (3.2 eV) was observed, which can be explained by the $H_2$passivation effect. At elevated temperature, two interesting peaks corresponding to violet (406 nm, 3.05 eV) and blue (436 nm, 2.84 eV) emission was firstly observed in AZO thin films. Moreover, peculiar PL peak around 694 nm (1.78 eV) is also firstly observed in all the H-AZO thin films and this is believed good evidence of hydrogenation of AZO. Based on defect-level scheme calculated by using the full potential linear muffin-tin orbital (FP-LMTO), the emission 3.2 eV, 3.05 eV, 3.84 eV and 1.78 eV of H-AZO are substantially deginated as exciton emission, transition from conduction band maximum to $V_{ Zn},$ from $Zn_i$, to valence band maximum $(V_{BM})$ and from $V_{o} to V_BM}$, respectively.