• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.581-586
• /
• 1994

Effect of excess and deficiency of PbO on the sintering and electrical properties of tetragonal Pb(Zr0.5Ti0.5)O3 were investigated. Fired density revealed maximum value with 4 wt% of excess PbO, and decreased with increasing amount of both excess and deficient PbO. Grain size increased with excess PbO, and decreased with deficiency of PbO. It appeared that excess PbO forms a liquid phase to enhance grain growth and completely volatilizes after sintering, whereas ZrO2 particles formed in PbO-deficient PZT inhibit grain growth. The change in the values of the equivalent circuit elements of PZT corresponded well with thar of porosity formed by excess and deficiency of PbO; kp, Co and Cm decreased while Qm, Rm and Lm increased conosiderably with porosity. This change was more pronounced in PbO-deficient type probably due to change in Zr/Ti ratio of PZT.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.281-288
• /
• 1997

The effects of 0 to 6 mol% excess 91PbO-9WO3 addition on the microstructure and the dielectric pro-perties in 40Pb(Mg1/3Nb2/3)O3-30PbTiO3-30Pb(Mg1/2W1/2)O3 ternary system were investigated. Excess 91PbO-9WO3 addition enhanced densification at relatively lower temperature due to the formation of liquid phase. The dielectric constant of the specimen with standard composition was 16,400 and that of specimen with 1 mol% excess additive was the maximum of 18,500. And more than 2 mol% excess addition decreased dielec-tric constant. Specimens with 2~4 mol% 91PbO-9WO3 addition showed dual peak maxima in the tem-perature dependence of dielectric constant. In the specimens which have more than 5 mol% excess addition a new phase with W-rich composition was formed at grain boundary.

• Journal of the Korean Ceramic Society
• /
• v.32 no.6
• /
• pp.726-734
• /
• 1995

Pb(Zr0.53Ti0.47)O3 (PZT) ceramics having different microstructures were fabricated at low temperatures using calcined PZT powders with addition of excess PbO powder and/or ball milling. The effects of excess PbO and ball milling time on the microstructure, the sintering characteristic, and the mechanical properties of these ceramics were studied. Fine powders with average particle size of 0.38㎛ could be obtained by ball milling with 2.5 mm Ф zirconia balls for 120 hours. By the addition of 2mol% of excess PbO to these powders, it was possible to obtain well-densitified PZT ceramics at low sintering temperature of 980℃. Densification behavior of PZT was affected by the addition of excess PbO powder, while, grain growth was hardly affected by PbO addition. It was observed that Vicker's hardness decreased and fracture toughness increased with the increasing amount of PbO. At 1mol% excess PbO, it was shown that the minimum values of hardness and maximum fracture toughness were achieved. In addition, with increasing sintering time, the fracture toughness decreased and the hardness increased.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.673-680
• /
• 2000

The effect of excess PbO(0, 1, 2, 4, and 8 mol%) on grain growth and densification of (65)Pb(Mg1/3Nb2/3)O3-(35)PbTiO3 [mol%] ceramics has been investigaetd. With increasing the amount of excess PbO and sintering time, densities of sintered samples decreased gradually. The samples containing less than 1 mol% of PbO showed normal grain growth behavior, however abnormal grain growth was observed to occur in the samples with more than 2 mol% of PbO. In the samples with more than 2 mol% of PbO, the number of abnormal grains decreased and thus the average grain size became smaller with increasing the amount of excess PbO. These results demonstrated that the abnormal grain growth started to occur when a critical amount of excess PbO was added to a (65)Pb(Mg1/3Nb2/3)O3-(35)PbTiO3 sample. Since PMN-PT grains in a liquid matrix were angular, the observed abnormal grain growth was explained to proceed through the two dimensional nucleation process.

• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.925-932
• /
• 1993

The perovskite phase in PZN-PMN-PT (Pb(Zn, Mg)1/3Nb2/3O3-PbTiO3) pseudoternary ceramics was stabilized by the addition of excess constituent divalent oxides (PbO, MgO and ZnO). The excess addition of 5mol% MgO or 7.5mol% PbO fully stabilized the perovskite phase. The enhanced diffuse phase transition (DPT) and the decrease in the electrical resistivity observed in the presence of excess ZnO or MgO were interpreted in terms of the additional formation of negatively charged, short-range ordered 1:1 domains with a concomitant generation of charge carriers, holes.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.335-340
• /
• 1992

Undoped PbTiO3 ceramics was successfully prepared by using sol-gel process, which had not been fabricated due to its microcracks created by anisotropic stress during phase transition from cubic to tetragonal phase. Fabrication of undoped PbTiO3 ceramics via sol-gel processing was very much affected by the PbO content of the samples as well as PbO vapor from sintering atmosphere. Excess PbO was found to promote rapid grain growth in PbTiO3 ceramics. After sintering at 1100$^{\circ}C$ average grain size of PbTiO3 ceramics with excess PbO was about 8 times greater than that of stoichiometric composition, which may be due to PbO liquid phase from excess PbO.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.905-910
• /
• 1998

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.629-634
• /
• 1993

Dielectric and electrostrictive properties of 0.99Pb(Mg1/3Nb2/3)O3-0.01Pb(Mn2/3W1/3)O3 system using KCl-NaCl salts have been investigated as a function of the amount of excess MgO. For the specimens calcined at $700^{\circ}C$ for 1h and then sintered at 115$0^{\circ}C$ for 4h, the perovskite phase and the relative density were about 98% and 95%, respectively. With the addition of excess MgO up to 10mol%, the dielectric constant and the electrostrictive strain increased due to the increase of density and grain size, and these properties were degraded by the further addition of excess MgO. For the 10mol% excess MgO added specimen, the maximum electrostrictive strain, Xmax, and the electrostrictive coefficient, Q11, were 4.5$\times$10-4, 3.5$\times$10-2m4/C2, respectively. These results were correlated with the property of PMW and microstructure.

• Journal of the Korean Ceramic Society
• /
• v.22 no.2
• /
• pp.17-24
• /
• 1985

In the composition of $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ the effect of particle size on PbO vaporization were measured, . The initial step of discontinuous vaporization of unreated PbO during the calcining process was depended on the particle size. All additives $La_2O_3Nb_2O_5$ and $Al_2O_3$ inhibited the grain growth of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ +2wt% excess PbO. The dielectric and piezoelectric properties of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ were improved by the addition of 2wt% excess PbO and proper additive. The electromechanical planar coupling factor of 0.65 and mechnical quality factor of 390 could be obtained by adding 5wt% $Nb_2O_5$ to the composition 2wt% excess PbO+$Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$.

• Journal of the Korean Ceramic Society
• /
• v.26 no.4
• /
• pp.568-574
• /
• 1989

Effect of PbO addition on sintering and piezoelectric properties at 0.45Pb(Ni1/3Nb2/3)O3-0.40PbTiO3-0.15PbZrO3 composition which is tetragonal phase was investigated. In this composition, Porosity and dielectric constant were increased with excess PbO addition, but Kp and d31 was not changed. These variation of physical properties could be interpreted as composition change of solid grains from tetragonal to MPB region due to amount of PbO-rich liquid changing.