• Korean Journal of Materials Research
• /
• v.9 no.3
• /
• pp.288-294
• /
• 1999

In the flip chip interconnection using solder bump, the Under Bump Metallurgy (UBM) is required to perform multiple functions in its conversion of an aluminum bond pad to a solderable surface. In this study, various UBM systems such as $Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 5\mu\textrm{m}, Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}, al 1\mu\textrm{m}/Ni 0.2\mu\textrm{m} / Cu 1\mu\textrm{m} and Al 1\mu\textrm{m}/Pd 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}$ for flip chip interconnection using the low melting point eutectic 63Sn-37Pb solder were investigated and compared to their metallurgical properties. $100\mu\textrm{m}$ size bumps were prepared for using an electroplating process. The effects of the number of reflows and aging time on the growth of intermetallic compounds(IMC) were investigated. $Cu_6Sn_5$ and $Cu_3Sn$ IMC were abserved after aging treatment in the UBM system with thick coper $(Al 1\mu\textrm{m}/Ti 0.2\mu\textrm{m}/Cu 5\mu\textrm{m})$. However only the $Cu_6Sn_5$ was detected in the UBM system with $1\mu\textrm{m}$ thick copper even after 2 reflow and 7 day aging at $150^{\circ}C$. Complete Cu consumption by Cu-Sn IMC growth gives rise to a direct contact between solder inner layer such as Ti, Ni and Pd, and hence to possibly cause reactions between two of them. In this study, however, only for the Pd case, IMC of PdSn. was observed by Cu consumption. UBM interfacial reactions with s이der affected the adhesion strength ot s이der balls after s이der reflow and annealing treatment.

• International Journal of Highway Engineering
• /
• v.7 no.4 s.26
• /
• pp.113-123
• /
• 2005

In this study, calcium chloride$(CaCl_2)$, sodium chloride (NaCl), organic acids-containing deicer(NS 40, NS 100), mixed deicier$(NaCl\;70%+CaCl_2\;30%,\;NS\;40\;70%+CaCl_2\;30%,\;NaCl\;70%+NS\;40\;30%,\;NS\;40\;70%+NaCl\;30%)$ is investigated based on the laboratory test for deicing performance, freez-thaw resistance of concrete, and corrosion rate of metal. Test items for deicing performance were ice melting and ice penetration, freezing point depressions and eutectic point, pH, thermal properties for selected deicing chemicals as well as their compatibility with concrete and metal were experimentally investigated. As a test results, in case of the use chloride-containing deicier in area that concrete structures has subjected to freez-thaw reaction in winter season, it showed that mixed deicing chemicals with optimum ratio has desirable method than use one deicing chemicals when is consider to deicing performance and effects, corrosion of steel materials, and freez-thaw resistance of concrete. When use various deicing chemicals mixed, NS40(70%)+calcium chloride(30%) showed the best effective method.

• Fisheries and Aquatic Sciences
• /
• v.2 no.1
• /
• pp.12-16
• /
• 1999

Denaturation of actomyosin from the obliquely striated mantle muscle of squids (Todarodes pacificus) was studied by measuring the changes in $Ca^{2+}$-ATPase activity, relative viscosity, and solubility during frozen storage at three different temperature zones of maximum ice crystal formation $(-3^{\circ}C,\;-\;-5^{\circ}C)$, the eutectic point $(-11^{\circ}C)$, and $-20^{\circ}C$. The logarithms of $Ca^{2+}$-ATPase activity, relative viscosity and solubility of the actomyosin solutions (0.6 M KCl) and suspensions (0.05 M KCl) tended to decrease during frozen storage. The denaturation of squid actomyosin at the zone of maximum ice crystal formation significantly differed by only two degree of temperature difference between $-3^{\circ}C$ and $-5^{\circ}C$, and it (0.05 M KCl) at $-3^{\circ}C$ was less than those of other temperature. The denaturation at $-11^{\circ}C$ was more rapid than at $-5^{\circ}C$. The logarithms of $Ca^{2+}$ -ATPase activity, relative viscosity, and solubility were changed slower in the suspensions (0.05 M KCl) than the solutions (0.6 M KCl) at all experimental temperatures.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1740-1743
• /
• 2007

In this study, two types of fatigue tests were conducted. First, cyclic bending tests were performed using the micro-bending tester. A four-point bending test method was adopted, because it induces uniform stress fields within a loading span. Second, thermal fatigue tests were conducted using a pseudo power cycling machine which was newly developed for a realistic testing condition. The pseudo-power cycling method makes up for the weak points in a power cycling and a chamber cycling method. Two compositions of solder are tested in all test condition, one is lead-free solder (95.5Sn4.0Ag0.5Cu) and the other is eutectic lead-contained solder (63Sn37Pb). In the cyclic bending test, the solder that exhibits a good reliability can be reversed depending on the load conditions. The lead-contained solders have a longer fatigue life in the region where the applied load is high. On the contrary, the lead-free solder sustained more cyclic loads in the small load region. A similar trend was detected at the thermal cycling test. A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. A constitutive model which includes both creep and plasticity was employed. Thermal fatigue was occurred due to the creep. And plastic deformation is main damage for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.726-731
• /
• 2002

Reaction synthesis is a process to form ceramics, intermetallics and their composites from elemental powder mixture. Application of this process to a surface modification techniques has a possibilities to enable the process at a lower temperature or for a shorter time, although synthesized materials are likely to include voids and unreacted elements. This paper intend to examine the effect of Si addition to the mixture of Al and Ni on the densification of synthesized Ni-Al intermetallic compounds and to evaluate the surface properties of obtained coatings. By the Si addition, exothermic reaction temperature to form Ni-Al intermetallic was lowered to be below the melting point of Al. Si soluted $Al_3$Ni$_2$, $Al_3$Ni and $Al_{6}$Ni$_3$Si were mainly formed in the coating layer when powder mixture was heated to 973K for 300s. Besides, densification was enhanced by increasing hot press pressure, Si additions and heating rate. When the composition of eutectic Al-Si reaches 78%, void ratio of sintered compact reduced to 0.4%. It is caused by higher flowability of Al-Si liquid phase generated and its infiltration into the void. Since the hardness of NiAl(Si) compound (about 600HV) formed in the coating layer is higher than that of Ni-Al compound (about 400HV), coating layer with high density and superior wear property is obtained by hot press using reaction synthesis from Al-Ni-Si powder mixture.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.4
• /
• pp.369-376
• /
• 2012

In this study, to reduce the hydration heat velocity (HHV) of high-strength mass concrete at early ages, phase change materials (PCM) that could absorb hydration heat were applied, and the changes in autogenous shrinkage were investigated, as well as the relationship between the hydration temperature and autogenous shrinkage. The acceleration of the cement hydration process by the PCM leads to an early setting and a higher development of the compressive strength and elastic modulus of concrete at very early ages. The function of PCM could be worked below the original melting point due to the eutectic effect, while the hydration temperature and HHV of high-strength mass concrete can be decreased through the use of the PCM. A close relationship was found between the hydration temperature and autogenous shrinkage: the higher the HHV, the greater the ultimate autogenous shrinkage.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.19 no.2
• /
• pp.161-176
• /
• 2021

In this study, the electrochemical behavior of Sm on the binary liquid Al-Ga cathode in the LiCl-KCl molten salt system is investigated. First, the co-reduction process of Sm(III)-Al(III), Sm(III)-Ga(III), and Sm(III)-Ga(III)-Al(III) on the W electrode (inert) were studied using cyclic voltammetry (CV), square-wave voltammetry (SWV) and open circuit potential (OCP) methods, respectively. It was identified that Sm(III) can be co-reduced with Al(III) or Ga(III) to form Al_zSm_y or Ga_xSm_y intermetallic compounds. Subsequently, the under-potential deposition of Sm(III) at the Al, Ga, and Al-Ga active cathode was performed to confirm the formation of Sm-based intermetallic compounds. The X-ray diffraction (XRD) and scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) analyses indicated that Ga₃Sm and Ga₆Sm intermetallic compounds were formed on the Mo grid electrode (inert) during the potentiostatic electrolysis in LiCl-KCl-SmCl₃-AlCl₃-GaCl₃ melt, while only Ga₆Sm intermetallic compound was generated on the Al-Ga alloy electrode during the galvanostatic electrolysis in LiCl-KCl-SmCl₃ melt. The electrolysis results revealed that the interaction between Sm and Ga was predominant in the Al-Ga alloy electrode, with Al only acting as an additive to lower the melting point.

• Journal of the Mineralogical Society of Korea
• /
• v.20 no.1 s.51
• /
• pp.7-19
• /
• 2007

Four types of fluid inclusions are trapped within tourmaline from Daeyou pegmatite, Jangsu-Gun, Jeonllabukdo. They range $5{\sim}100\;{\mu}m$ in size and are grouped into I, II, III, and IV based on the phase behavior at the room temperature: (1) Type I inclusions are liquid-rich and NaCl equivalent salinity ranged $0{\sim}12\;wt%$, and the homogenization temperatures (Th) ranged $181{\sim}230^{\circ}C$ with eutectic temperatures (Te) $-54{\sim}-22^{\circ}C$. (2) Type II inclusions are vapor-rich and salinity ranged $3{\sim}8\;wt%$ NaCl, and Th ranged $177{\sim}304^{\circ}C$ also showing Te $-54{\sim}-29^{\circ}C$. (3) Type III inclusions contain a halite daughter mineral with $31{\sim}40\;wt%$ NaCl, Th $230{\sim}328^{\circ}C$. More than 90% of Type III homogenize by halite dissolution and are spatially associated with silicate melt inclusions. (4) Type IV inclusions are $CO_{2}$-bearing containing various daughter minerals such as sylvite and/or halite. The density of $CO_{2}$ system within the Type IV is $0.80{\sim}0.75\;g/cm^{3}$, Th $190{\sim}317^{\circ}C$, and salinity $2{\sim}35\;wt%$ NaCl. Type III fluid inclusions, considered as the earliest fluid, formed from the fluid exsolved from the crystallizing pegmatite. It is suggested that Type II fluid in the central part of tourmaline were exsolved earlier than Type I fluids in the margin indicating salinity fluctuation during the growth of tourmaline. It implies the fluctuation of the pressure since the salinity of fluid exsolved from the crystallizing melt is governed by the pressure. The last fluid was Type IV, which may be derived from the nearby limestone and metasedimentary rocks. It is suggested that Daeyou pegmatite containing muscovite without miarolitic cavities was formed by the partial melting resulted from the regional metamorphism. Subsequently, the exsolving fluids from the crystallizing melt were trapped in tourmaline at high pressure condition. The exsolved fluids contain various components such as $CaCl_{2}\;and\;MgCl_{2}$ as well as NaCl and KCl. The exsolution began at least at $2.7{\sim}5.3\;kbar\;and\;230{\sim}328^{\circ}C$ with the pressure fluctuation.

• Journal of Radiation Protection and Research
• /
• v.4 no.1
• /
• pp.14-20
• /
• 1979

For accurate and easily shielding irregular shaped organ, its minimized penumbra region and a low melting point alloy 'Lead Y' and synchronizing instrument have been developed. The 'Lead Y' is the quaternary eutectic alloy and it is composed of Lead 30.0% Tin 11.5% Bismuth 48 5% Cadmium 10.0% The density of its at $22^{\circ}C$ is $9.8g/cm^3$ and the melting temperature has $40^{\circ}C\;to\;68^{\circ}C$. The thickness of 'Lead Y' for perfect shielding of Co-60 gamma ray and LINAC 10MeV x-ray is 6cm and 7cm respectively. The 'Lead Y' shielding block is casted directly on the styrofoam from which is cut with hot wire of synchronizer device. The special features and advantages of the Lead Y shielding block could be summarized as follows; 1. The shielding block for radiotherapy is rapidly processed only with boiling water and styrofoam. 2. It is not injure one's health and not danger of a fire, because of not generating of any metals vapor and evil smelling. 3. It is very effective to minimize secondary penumbra for the protection of healthy tissue from unnecessary ionizing radiation regardless of the magnification source to skin distance. 4. The HVL of the Lead Y is 1.2cm for Co-60 gamma ray and it's shielding effect is almost same as the pure lead block. 5. The hardness of Lead Y is 1.5 times higher than lead block. 6. It's reavailability is higher than lead block and then one block of Lead Y is reavailable about 30 to 40 times. 7. It is usefull for shielding of x-ray, gamma ray, beta-ray, electron and neutron radiation. 8. The materials for Lead Y are easy to acquire with reasonable price and tractable.

• Archives of Plastic Surgery
• /
• v.42 no.1
• /
• pp.28-33
• /
• 2015

Background Topical anesthetics, such as eutectic mixture of local anesthetics (EMLA) cream, can be applied to reduce pain before minor procedure. This trial evaluated EMLA as pretreatment for facial lacerations and compared pain, discomfort and overall satisfaction. Methods This trial included consecutive emergency department patients ${\geq}16years$ of age who presented with simple facial lacerations. At triage, lacerations were allotted to either the routine processing group or EMLA pretreatment group according to date of admission. Initially, the emergency department doctors inspected each laceration, which were dressed with saline-soaked gauze. In the pretreatment group, EMLA cream was applied during wound inspection. The plastic surgeon then completed primary closure following the local injection of an anesthetic. After the procedure, all patients were given a questionnaire assessing pain using the 10-point visual analog scale (VAS) ("no pain" to "worst pain"). All questionnaires were collected by the emergency department nurse before discharge. Results Fifty patients were included in the routine processing group, and fifty patients were included in the EMLA pretreatment group. Median age was 39.9 years, 66% were male, and the average laceration was 2.67 cm in length. The EMLA pretreatment group reported lower pain scores in comparison with the routine processing group (2.4 vs. 4.5 on VAS, P<0.05), and lower discomfort scores during the procedure (2.0 vs. 3.3, P=0.60). Overall satisfaction was significantly higher in the EMLA pretreatment group (7.8 vs. 6.1, P<0.05). Conclusions Pretreating facial lacerations with EMLA topical cream aids patients by reducing pain and further enhancing overall satisfaction during laceration treatment.