• Journal of Powder Materials
• /
• v.23 no.2
• /
• pp.108-111
• /
• 2016

$Y_2O_3-H_3BO_3:Eu^{3+}$ powders are synthesized using a mechanical alloying method, and their photoluminescence (PL) properties are investigated through luminescence spectrophotometry. For samples milled for 300 min, some $Y_2O_3$ peaks ([222], [440], and [622]) and amorphous formations are observed. The 300-min-milled mixture annealed at $800^{\circ}C$ for 1 h with Eu = 8 mol% has the strongest PL intensity at every temperature increase of $100^{\circ}C$ (increasing from 700 to $1200^{\circ}C$ in $100^{\circ}C$ increments). PL peaks of the powder mixture, as excited by a xenon discharge lamp (20 kW) at 240 nm, are detected at approximately 592 nm (orange light, $^5D_o{\rightarrow}^7F_1$), 613 nm, 628 nm (red light, $^5D_o{\rightarrow}^7F_2$), and 650 nm. The PL intensity of powder mixtures milled for 120 min is generally lower than that of powder mixtures milled for 300 min under the same conditions. PL peaks due to $YBO_3$ and $Y_2O_3$ are observed for 300-min-milled $Y_2O_3-H_3BO_3$ with Eu = 8 mol% after annealing at $800^{\circ}C$ for 1 h.