• Journal of Adhesion and Interface
• /
• 제4권3호
• /
• pp.14-20
• /
• 2003

In order to study the radiation curing behavior of poly(ethylene glycol 400) dimethacrylate and ethylene glycol dimethacrylate, we investigated the influence of temperature and photoinitiator concentration by photo-DSC. As the number of ethylene glycol unit, the concentration of photoinitiator, and the reaction temperature increased, the reaction speed of PEG400DMA and EGDMA increased. Although the reaction speed of PEG400DMA was lower than EGDMA, the overall conversion of PEG400DMA was high.

• Polymer(Korea)
• /
• 제33권2호
• /
• pp.153-157
• /
• 2009

The resin matrix in the dental composite is generally composed of 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) as a base resin and triethylene glycol dimethacrylate (TEGDMA) as a diluent for the reduction of viscosity. The applications of dental composite were often limited in dentistry due to the relatively large amounts of volumetric shrinkage during polymerization and water uptake caused by the addition of TEGDMA to the resin matrix. In this study, in order to solve problems stemmed from the TEGDMA by reducing amount of diluent added to resin matrix, diethylene glycol dimethacrylate (DEGDMA) and ethylene glycol dimethacrylate (EGDMA) were explored as new diluents. A decrease in the volumetric shrinkage and an increase in the mechanical strength were observed by replacing TEGDMA in the dental composite to DEGDMA (or EGDMA). Reduction in the mechanical strength of the dental composite containing DEGDMA (or EGDMA), was not serious in comparison with that of the dental composite containing TEGDMA after water uptake.

• Journal of the Korean Chemical Society
• /
• 제54권1호
• /
• pp.105-109
• /
• 2010

HEMA (2-hydroxyethyl methacrylate), EGDMA (ethylene glycol dimethacrylate) and propylene glycol was copolymerized in the presence of AIBN (azobisisobutyronitrile) initiator in a mould. The physical properties of the contact lens were measured. The water content of 37.06~38.71%, refractive index of 1.492~1.432, visible transmittance of 89.4~91.5%, tensile strength of 0.1416~0.2302 kgf, and contact angle of $38.60{\sim}53.53^{\circ}$ were obtained. Therefore, the contact lens material produced using propylene glycol as an additive satisfied the basic physical properties required for contact lenses application. It is interesting to note that an increase in wettability and tensile strength while having no significant changes in water content.

• Journal of Integrative Natural Science
• /
• 제17권2호
• /
• pp.53-58
• /
• 2024

This study explores the enhancement of mechanical properties in Polymethyl Methacrylate (PMMA) composites through the incorporation of Methyl Methacrylate (MMA) and Ethylene Glycol Dimethacrylate (EGDMA). Utilizing Digital Light Processing (DLP) technology, we conducted a series of experiments to analyze the impact of varying concentrations of MMA and EGDMA on PMMA. The results indicate that while MMA demonstrates non-linear and variable mechanical strength across different PMMA concentrations, EGDMA consistently improves mechanical strength as PMMA concentration increases. This consistent enhancement by EGDMA suggests a stable and predictable reinforcement effect, which is critical for applications requiring high mechanical strength. Our comparative analysis highlights that EGDMA is a more effective additive than MMA for optimizing the mechanical performance of PMMA composites. Specifically, EGDMA's ability to provide uniform reinforcement across various PMMA concentrations makes it ideal for high-strength applications. These findings are significant for material scientists and engineers focused on the design and development of advanced PMMA-based materials. In conclusion, this research underscores the importance of selecting appropriate additives to enhance the mechanical properties of PMMA composites. The superior performance of EGDMA in reinforcing PMMA suggests its potential for broader applications in fields such as automotive, construction, medical devices, and 3D printing. This study provides valuable insights that can guide future research and development in high-performance composite materials, paving the way for innovative applications and improved material efficiency.

• Journal of the Korean Chemical Society
• /
• 제55권2호
• /
• pp.283-289
• /
• 2011

This study used glycerol dimethacrylate with the cross-linker EGDMA (ethylene glycol dimethacrylate), HEMA (2-hydroxyethyl methacrylate), MMA (methyl methacrylate), MA (methacrylic acid) and the initiator AIBN (azobisisobutyronitrile) for copolymerization. Measurement of the physical properties of the copolymerized polymer showed that the water content was 22~32%, refractive index was 1.442~1.463 and visible ray transmittance 90.0~90.5% while the contact angle showed a distribution between 56 and $65^{\circ}$. Also, the measurement showed that the decreased amount of contact angle of the copolymer measured using the sessile drop method ranged between $9.89^{\circ}$ and $18.99^{\circ}$ with increase of glycerol dimethacrylate. Based on the results of this study, the produced copolymer is suitable for use as a material to high wettability ophthalmic lenses.

• Polymer(Korea)
• /
• 제31권5호
• /
• pp.410-416
• /
• 2007

Monodisperse polymer particles were prepared via one- step seeded polymerization using PMMA as seed particles, and HDDA, triEGDMA or EGDMA as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer to the seed polymer particles (swelling ratio), 2) the characteristics of crosslinking monomer, 3) electroless Ni plating, and 4) electroless Au Plating on the variation of mechanical properties of polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement were investigated by using MCT (micro compression test). It was observed that swelling ratio of polymer particles influenced only on breaking strength of polymer Particles, while electroless plating did on recovery rate, K-values ($K_{10}\;and\;K_{20}$) and breaking strength of electroless plated polymer particles. However, breaking displacement and K-values ($K_{30}{\sim}K_{50}$) were more or less insensitive to electroless plating.

• Journal of the Korean Chemical Society
• /
• 제53권3호
• /
• pp.340-344
• /
• 2009

HEMA/vinyl-substituted polyphosphazene was prepared by the ring-opening polymerization of phosphonitrillic chroride trimer at $200{\sim}300\;{^{\circ}C}$, followed by Grignard reaction with vinyl magnesium bromide and then by the reaction with HEMA(2-hydroxyethyl methacrylate). HEMA/vinyl-substituted polyphosphazene was copolymerized with EGDMA(ethylene glycol dimethacrylate; used as a cross-linker for the free-radical copolymerization), NVP (N-vinyl-pyrrolidone) in the presence of AIBN (azobisisobutyronitrile) as a radical initiator. The oxygen transmissibility, water content and visible-ray transmissibility of the resulting copolymer were measured to be Dk/t 88, 30.89% and 87%, respectively, indicating that the copolymer can be used as a good contact lens material.

• Polymer(Korea)
• /
• 제36권2호
• /
• pp.208-215
• /
• 2012

To study the effect of surface crosslinked layer on the crosslinked poly(sodium acrylate) (cPSA) absorbent, we synthesized several surface crosslinked cPSAs with 5, 10 and 20 g of ethylene glycol dimethacrylate (EGDMA) by an inverse emulsion polymerization method to delay the absorption of excess water in concrete. We measured the compressive and flexural strength of mortars having 0.5, 1.0 and 1.5 wt% cPSA-EGDMA. We observed the increase of compressive and flexural strength of the cPSA-EGDMA added cement mortars except for the 0.5 wt% cPSA-EGDMA (20 g) added cement mortar. 1.0 wt% cPSA-EGDMA (5 g) added cement mortar showed about 16% and 10% increased compressive and flexural strength than those of plain cement mortar. To study the effect of porosity on compressive and flexural strength, we used FE-SEM and porosimeter. FE-SEM analysis showed swollen cPSMAEGDMA (5 g) filled between calcium silicate hydrate (C-S-H) crystals. We observed the decreased porosity of the cPSA-EGDMA added cement mortars than that of plain cement mortar. 1.0 wt% cPSA-EGDMA (5 g) cement mortar showed the lowest porosity of 16.5%.

• Journal of the Korean Applied Science and Technology
• /
• 제36권1호
• /
• pp.305-311
• /
• 2019

The acrylic copolymer was designed and prepared for soft lens with high content. The copolymers were prepared using 2-hydroxyethyl methacrylate(HEMA) as a monomer and ethylene glycol dimethacrylate(EGDMA), glycerol dimethacrylate(GD), or glycerol 1,3-diglycerolate diacrylate (GDD) as a cross linking agent. The water content for high water content lens was 46%, which was higher compared to general purpose of 36%. The contact angle decreased from 38.6 to 34.4, which appears hydrophilic surface. The tensile strength decreased from 0.1 Mpato 0.08, then again to 0.05 as hydrophilic properties of cross linking agents increased. No phase separation was observed in the cross section of lens using scanning electron microscope. The real-time infrared technique was used in photo-polymerization. The initial polymerization rate increased from 0.6 to 0.9, depending on crosslinking agent.

• Proceedings of the SCSK Conference
• /
• 대한화장품학회 2003년도 IFSCC Conference Proceeding Book I
• /
• pp.686-697
• /
• 2003

A new colloidal silver (Ag) system is present in which a fine colloidal Ag is in situ deposited onto functionalized porous poly (ethylene glycol dimethacrylate) (poly (EGDMA)) microspheres. The effectiveness of Ag deposition was investigated considering the surface characteristics of poly (EGDMA) microspheres. The result reported in this study illustrates that the control of surface area and surface functionality (in this study, a hydroxyl group) of poly (EGDMA) microspheres is an important factor that determines practically the degree of deposition of colloidal Ag. The x-ray analysis showed that Ag nanoparticles were dispersed evenly inner and outer surfaces and had a face center cubic (fee) phase. In the preservative efficacy test, the Ag-containing poly (EGDMA) microspheres had a powerful anti-bacterial activity, showing a high potential for a new preservative in cosmetic industry.