• 해양환경안전학회지
• /
• 제7권3호
• /
• pp.75-84
• /
• 2001

Ultrasonic vibrator is an equipment which atomizes and homogenizes the oils by breaking the oil particles with ultrasonic vibration cavity, and possibly improves the properties. There are various parameters on the effect of ultrasonic irradiation. Especially, this study intended to investigate the matrix structure of sludge oils and the erosion damages for horn disc SS41 according to the variation of the oil temperature and the immersing depth of horn disc. Sludge oils were irradiated with ultrasonic vibration and then observed the aspects of the change of oil particles. From these, the recycling feasibility of sludge oil for useable oil to be burnt was determined. The erosion damages for horn disc SS41 were examined with weight loss, weight loss rate and the irradiation time to max. erosion rate. These data will be useful to the development of ultrasonic breaking systems to recycle sludge oil and to consider a countermeasure for the prevention of erosion damages.

• Corrosion Science and Technology
• /
• 제11권3호
• /
• pp.89-95
• /
• 2012

U.S. Electric Power Research Institute (EPRI) has developed CHECWORKS program and applied it to power plant piping lines since some lines were ruptured by flow-accelerated corrosion (FAC) in 1978. Nowadays the CHECWORKS program has been used to manage pipe wall thinning phenomena caused by FAC. However, various erosion mechanisms can occur in carbon-steel piping. Most common forms of erosion are cavitation, flashing, liquid droplet impingement erosion (LDIE), and Solid Particle Erosion (SPE). Those erosion mechanisms cause pipe wall thinning, leaking, rupturing, and even result in unplanned shutdowns of utilities. Especially, in two phase condition, LDIE damages a wide scope of plant pipelines. Furthermore, LDIE is the major culprit to cause such as power runback by pipe leaking. This paper describes the methodologies that manage wall thinning and also predict LDIE wall thinning area. For this study, current properties of two-phase condition are investigated and LDIE areas are selected. The areas are checked by B-Scan method to detect the effect of wall thinning phenomena.

• 한국제4기학회지
• /
• 제19권1호
• /
• pp.41-46
• /
• 2005

This study discusses the soil erosion on hillslopes and sediment deposition in lakes within catchments in South Korea. In order to determine seasonal variations of sedimentation in Yeongcheon and Seondong lakes, the sediment traps were set in the deep part of both lakes and lake sediments have been sampledmonthly from July 2004 to August 2005. Some properties such as highmineral content, fine particle size and high particle density in the Yeongcheon Lake indicate intensive soil erosion, sediment transportation and deposition throughout the catchment for a long time. The high sediment yield in the Seondong Lake is related with higher weathering intensity and extreme soil erosion by running water due to higher seasonal rainfall amount. Rates of erosion and sedimentation in the Seondong Lake are estimated to be higher than those of the Yeongcheon Lake, suggesting that the Seondong Lake is associated with higher precipitation, smaller catchment area, and extreme soil vulnerability to ephemeral erosion by overland flow during the heavy rainfall event. Consequently, both catchments are characterized by different erosion and sedimentation processes, as well as different geomorphic factors (bedrock, soil structure, rainfall intensity and catchment area).

• 한국세라믹학회지
• /
• 제32권9호
• /
• pp.1003-1008
• /
• 1995

CVD-Si3N4/CVD-SiC/pack-SiC/pyro-carbon/(3-D C/C composite) multilayer coating was performed to improve the oxdiation resistance and erosion resistance properteis of the 3-D carbon/carbon composite, and the plasma test was performed to measure the oxidation resistance and erosion resistance properties. The thicknesses of each film layer were about 10${\mu}{\textrm}{m}$ for pack-SiC, 5${\mu}{\textrm}{m}$ for CVD-SiC and 40${\mu}{\textrm}{m}$ for CVD-Si3N4. When the multilayer coated specimen was exposed to the plasma flame with temperature of 500$0^{\circ}C$ for 20 seconds, it showed the weight loss five times less than that of the only pyro-carbon coated specimen.

• 한국해안해양공학회지
• /
• 제18권4호
• /
• pp.283-293
• /
• 2006

본 연구의 목적은 금강 하구역 표층에 분포하는 점착성 퇴적물의 침식특성을 정량적으로 산정하고, 그 침식특성의 계절적 변화와 타 지역 침식특성 결과와의 비교/분석을 통한 공간적 변화를 해석하는데 있다. 또한 점착성 퇴적물의 침식특성은 퇴적물 자체의 물리 화학적 기본특성에 의해 크게 영향을 받으므로, 본 연구에서는 이러한 퇴적물의 기본특성이 침식특성에 미치는 영향에 대해서도 해석하였다. 침식실험은 균일저면 조건에서 1개 지점에 대해 계절별로(가을과 겨울) 4회씩 총 8회의 실험이 환형수조를 사용하여 수행되었으며 그 결과 저면밀도 $1.15{\sim}1.34g/cm^3$ 범위에서 침식한계전단응력(${\tau}_{ce.s}$)은 $0.12{\sim}0.36N/m^2$, 침식률 계수(${\varepsilon}_{M.S}$)는 $120.91{\sim}6.72mg/cm^2{\cdot}hr$ 범위의 값을 갖는 것으로 확인되었으며, 산정된 침식특성 매개변수들은 다른 점착성 퇴적물(Okeechobee호, Kaolinite)과 비교해 정량적으로 상당한 차이를 보였으나 금강 하구역 내에서의 계절적 변화는 미미한 것으로 나타났다.

• 소성∙가공
• /
• 제22권5호
• /
• pp.264-268
• /
• 2013

Aluminum clad sheets for brazing materials in the automotive heat exchangers are required to exhibit both high strength and excellent erosion resistance. In this study, the effects of microstructural changes on the property of clad sheets due to thermomechanical treatment were investigated. The clad sheets were fabricated by roll bonding of twin-roll-cast AA3527 and AA4343 alloys followed by cold rolling down to a thickness of 0.22mm. Partial or full annealing was conducted at the final thickness in order to improved the erosion resistance while keeping the proper strength. Since full annealing was achieved for a temperature of $400^{\circ}C$, annealing treatments were performed at 360, 380, and $400^{\circ}C$, respectively. The tensile strength of 3527/4343 clad material was found to be inversely proportional to the annealing temperature before the brazing heat treatment. After this latter treatment, however, the tensile strength of the clad material was about 195~200MPa regardless of the annealing temperature. The erosion depth ratio of the clad annealed at $400^{\circ}C$ was 8.8% (the lowest), while that of the clad annealed at $380^{\circ}C$ was 17% (the highest). The effect of annealing temperature on the tensile and erosion properties of 3527/4343 aluminum clad sheets was elucidated by means of microstructural analyses.

• 한국해양공학회지
• /
• 제25권1호
• /
• pp.14-21
• /
• 2011

The purpose of this study is to quantify the erosional parameters, such as the critical shear stress for erosion and the erosion rate coefficient for cohesive sediments from the Mokpo coast. Using Chonbuk annular flume, five erosion tests were conducted under the uniform bed condition but a different bed density respectively. Erosion test results for Mokpo sediments have shown increases in the range of $0.16{\sim}0.43\;N/m^2$ but decreases exponentially in the range of $272{\sim}4.64\;mg/cm^2{\cdot}hr$ for the given bed shear stress of $1.14{\sim}1.34\;g/cm^3$. The erosional parameters of Mokpo sediments are found to vary remarkably in quantity compared with those for cohesive sediments from other sites. On the whole, the value of Mokpo coast sediments appears to be similar to Kunsan sediments but smaller than Saemankeum and Okeechobee sediments. On the other hand, Mokpo sediments have been shown to be larger than Saemankeum and Okeechobee sediments but smaller than Kunsan sediments.

• Journal of Advanced Marine Engineering and Technology
• /
• 제20권2호
• /
• pp.92-92
• /
• 1996

Recently, with the rapid development in the oceanic systems such as the oceanic structures and vessel, there occurs much interest in the impingement erosion-corrosion. In this paper, Cu-metal was tested by using of erosion apparatus with water-jet type and was investigated under the behaviour of impingement erosion-corrosion according to various environmental conditions, and the properties of Cu-metal were evaluated through the measurement by weight loss, weight loss rate, protective efficiency. The results were compared with those obtained using Cu-metal applied to cathodic protection and Cu-alloys added to Zn or Al-metal. As a basis of those results, the best protective efficiencies could be taken as using cathodic protection method and Cu-alloy with Al & Zn material addings, and will be suggested as the fundamental data of the anti-impingement erosion-corrosion on Cu-metal of impeller material for oceanic centrifugal pump.

• Journal of Advanced Marine Engineering and Technology
• /
• 제20권2호
• /
• pp.24-31
• /
• 1996

Recently, with the rapid development in the oceanic systems such as the oceanic structures and vessel, there occurs much interest in the impingement erosion-corrosion. In this paper, Cu-metal was tested by using of erosion apparatus with water-jet type and was investigated under the behaviour of impingement erosion-corrosion according to various environmental conditions, and the properties of Cu-metal were evaluated through the measurement by weight loss, weight loss rate, protective efficiency. The results were compared with those obtained using Cu-metal applied to cathodic protection and Cu-alloys added to Zn or Al-metal. As a basis of those results, the best protective efficiencies could be taken as using cathodic protection method and Cu-alloy with Al & Zn material addings, and will be suggested as the fundamental data of the anti-impingement erosion-corrosion on Cu-metal of impeller material for oceanic centrifugal pump.

• 동력기계공학회지
• /
• 제2권2호
• /
• pp.35-40
• /
• 1998

In this study, the author investigated the effects of strengthening treatments on the mechanical properties of plasma sprayed Ni-base self fluxing alloy. Strengthening treatments for sprayed specimens were carried out in 4 different temperature conditions in vacuum furnace. The mechanical properties, such as microhardness, thermal shock resistance and erosion resistance were tested for the sprayed specimens after strengthening treatments. And it was proved that the mechanical properties of coating layer were much improved by strengthening treatments.