• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.277-285
• /
• 1999

Mechanical properties of nanocrystalline Al-5at.%Ti alloy were investigated through high temperature compression test. Al-5at.%Ti nanocrystalline metal powders, which had finer and more equiaxed shape than those produced at room temperature, were produced by mechanical alloying at low temperature. The powders were successfully consolidated to 99fo of theoretical density by vacuum hot pressing. XRD and TEM analysis revealed that $Al_3Ti$ intermetallic compounds formed inside powders and pure Al region with coarse grains formed between powders, especially at triple junction. Mechanical properties in terms of hardness and strength were improved by grain size refinement, but ductility decreased presumably due to the formation of the weak interfaces between Al pool and powders.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.392-398
• /
• 1996

$Si_{3}N_{4}/SiC$ nanocomposites reinforced with tow different mean particle size were fabricated by hot press. Grain growth of matrix gran was inhibited by adding of SiC particles, and then number of equiaxed and fine grains were increased. The effect of grain growth inhibition was higher in the nanocomposites dispersed small size SiC. herefore fracture strength and hardness were increased, but fracture toughness was decreased in small size SiC dispersed samples.

• Korean Journal of Materials Research
• /
• v.9 no.2
• /
• pp.132-138
• /
• 1999

In order to investigate the toughening characteristic by microcrack formation in ceramic composites, $Al_2$O$_3$/(0~20)vol% YAG composites containing equiaxed second grains were fabricated using$ Al_2$$O_3$ during hot-pressing. AE(acoustic emission) measurements have been coupled with fracture toughness experiments of SENB method, to evaluate the microcrack formation and the improvement in fracture toughness of ceramic composites. Formation of microcrack was detected by Ae. The generation of AE events increased with increasing of load when load was applied at specimen. The AE events are generated mainly around at maximum load. Specially, the detected AE evetns of composites are many as compared with monolithic $Al_2$$O_3$. Fracture toughness of composites was improved than that of monolithic alumina. $Al_2$O$_3$/YAG composites exhibit main toughening effects by microcracking, results from mutual coalesence of microcracks being generated under applied load. However, there are few toughening mechanism like microcracking in monolithic alumina.

• Transactions of Materials Processing
• /
• v.18 no.6
• /
• pp.476-481
• /
• 2009

The present work demonstrates the mechanical and electrical responses of submicrocrystalline Cu-3%Ag alloy as a function of strain imposed by equal channel angular pressing(ECAP). From transmission electron microscope observation, the resulting microstructures of Cu-3%Ag alloy deformed by ECAP for 8-pass or more consist of reasonably fine, equiaxed grains without having a strong preferred orientation, suggesting that microstructure evolution is slower than that of pure-Al and its alloys owing to low stacking fault energy. The results of room temperature tension tests reveal that, as the amount of applied strain increases, the tensile strength of submicrocrystalline Cu-3%Ag alloy increases whereas losing both the ductility and the electrical conductivity. Such phenomenon can be explained based on microstructure featured by the non-equilibrium grain boundaries.

• Journal of Korea Foundry Society
• /
• v.6 no.1
• /
• pp.36-46
• /
• 1986

The effects of various kind of molds on cast structures were studied in Al-4.5% Cu and Al-8% Cu alloys. Five kinds of sand molds which were mixed with different binders and a metal mold were used. Density, dendrite arm spacing and dendrite arm length of the cast alloys were greatly affected by quantities and materials of mold binders. The macrostructures examined were entirely equiaxed grains with little influences of types of molds. It is possibly due to the separation of growing crystals from the mold wall at the inital stage of solidification.

• Transactions of Materials Processing
• /
• v.13 no.8
• /
• pp.704-709
• /
• 2004

The effect of annealing temperature on microstructures and mechanical properties of the 5052 Al sheets rolled 88% reduction at cryogenic temperature was investigated for the annealing temperature of 150 ~ $300^{\circ}C$, in comparison with those rolled at room temperature. The presence of equiaxed grains, whose size is about 200nm in a diameter, was observed in the alloy deformed 88% and annealed $200^{\circ}C$ for an hour. When compared with the deformation at room temperature, the deformation at cryogenic temperature showed the higher strengths and equivalent elongation after annealing at the annealing temperature below $200^{\circ}C$. However, for annealing above $250^{\circ}C$ materials deformed at cryogenic temperature showed the lower strength than those deformed at room temperature. This behavior might be attributed to the higher rate of recrystallization and growth in materials deformed at cryogenic temperature during annealing, due to the lager density of dislocations accumulated during the deformation.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.228-234
• /
• 1989

Pressureless-sintering of SiC with additions of yttria and alumina was studied. SiC could be densified to about 97% of its theoretical density at 185$0^{\circ}C$ which is about 20$0^{\circ}C$ below the normal sintering temperature of SiC with boron and carbon. Yttria and alumina formed intergranular liquid phases at the sintering temperature and promoted densification by the liquid phase sintering mechanism. The microstructure of sintered specimens was equiaxed and the liquid phase appeared to wet and dissolve SiC grains. The fracture toughness was measured by indentation method and found to be 5.3MPa.m1/2. Processing flaws near the surface of specimens appeared to be the major fracture origin during 3-point bending tests.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.323-324
• /
• 2006

The nanostructure control of $Si_3N_4$ ceramics can be achieved by using fine starting powder and retardation of grain growth. The spark plasma sintering technique is useful to retard the grain growth by rapid heating. In the present work, the change of microstructure was investigated with emphasis on the particle size of starting powder, the amount of sintering additive and the heating schedule. The rapid heating by spark plasma sintering gave the fine microstructure consisting of equiaxed grains with the same size as starting particles. The spark plasma sintering of $Si_3N_4$ fine powder was effective to control the microstrucutre on nano-meter level.

• Nuclear Engineering and Technology
• /
• v.40 no.4
• /
• pp.305-310
• /
• 2008

Based on a composition of 99.4 wt% AISI 316L stainless steel, 0.3wt% Ti and 0.3 wt% $Y_2O_3$, an austenitic ODS steel was fabricated by a process of mechanical alloying, hot isostatic pressing and rolling. Fine oxide particles were observed in the matrix, and their chemical formulations were determined to be $Y_2Si_2O_7$ and TiO. Heat treatment of the cold-rolled sample at $1200^{\circ}C$ induced an isotropic tensile behavior at room temperature and at $700^{\circ}C$. This result would be mainly attributed to the equiaxed grains that form as a result of the heat treatment for recrystallization.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.1
• /
• pp.29-40
• /
• 2005

Formation of nanocrystalline ferrite was investigated using milled powders obtained by planetary ball milling of chips, which were made by high speed mechanical cutting of a low carbon steel(0.15%C-1.1%Mn-0.01%Ti). After 4 hour milling the chips were changed to powders of $50{\mu}m$ in average size, and with increasing milling time the powders were refined to about $3{\mu}m$ for 128 hour and showed more equiaxed shapes. Nanocrystalline(nc) region appeared in the surfaces of powders milled for 1 hour, and the 4 hour milled powders were almost filled with nc region. Hardness of nc region was much higher than that of work-hardened(WH) region. With increasing milling time, ferrite and cementite in pearlite were severely deformed and lamellar spacing was decreased, and then cementites began to disappear after 4 hour milling due to dissolution into ferrite. Deformation bands formed in lightly work-hardened region showed large width and similar crystallographic orientations. Spacing of deformation bands was decreased with deformation and the layered microstructure consisting of narrow deformation bands subdivided into variously oriented small grains was formed by more deformation, and eventually this structure seemed to be evolved to the nc structure by further deformation. It is also conjectured the growth of nc ferrite grains occurred through the coalescence of nanocrystalline ferrites rather than the nucleation and growth of recrystallized grains.