• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.208-211
• /
• 2002

In RC beams strengthened with Epoxy-Bonded Fiber, debonding failure happens frequently. Moreover, through the life cycle, it is difficult to recognize clacks and deflections on the surface of concrete members strengthened with Epoxy- Bonded Fiber. For these reasons, we must always monitor the state of RC beams. The Optical FBG sensor is broadly accepted as a structural health monitoring device. The main objective of this paper is that it's possible to monitoring the debonding failure of R.C. beams strengthened with Epoxy-Bonded Fiber. For that, we fixed two Optical FBG sensors at the center of the beam and another two sensors in the end of Epoxy-Bonded Fiber, According to the comparison micro-strain between embeded sensor in concrete and that on the fiber surface, we can find the point which debonding failure occurs

• 대한기계학회논문집A
• /
• 제24권11호
• /
• pp.2853-2865
• /
• 2000

During the curing process of thick glass/epoxy laminates, a substantial amount of temperature lag and overshoot at the center of the laminates is usually experienced due to the large thickness and low thermal conductivity of the glass/epoxy composites. Also, it takes a longer time for full and uniform consolidation. In this work, temperature, degree of cure and consolidation of a 20 mm thick unidirectional glass/epoxy laminate were investigated using an experiment and a 3-dimentional numerical analysis. From the experimental and numerical results, it was found that the experimentally obtained temperature profile agreed well with the numerical one, and the cure cycle recommended by the prepreg manufacturer should be modified to prevent a temperature overshoot and to obtain full consolidation.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2006년 창립20주년기념 정기학술대회 및 국제워크샵
• /
• pp.223-225
• /
• 2006

In this study, the graphite/epoxy prepregs were surface-treated using oxygen plasma, and optimal treatment time was determined measuring the contact angle en the prepreg surface. Interlaminar fracture behavior of surface-treated graphite/epoxy composite was compared with that of regular (untreated) graphite/epoxy composites. The results showed that the contact angle was a minimum when treated for 30 minutes. The interlaminar fracture toughness of surface-treated specimen was improved about 15% compared with that of regular specimen.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2009년도 춘계학술대회 논문집
• /
• pp.239-246
• /
• 2009

The Mode I interlaminar fracture toughness of woven fabric carbon/epoxy and glass/epoxy composites for a train carbody was measured and FEM analysis was conducted. The woven fabric epoxy composite manufactured by hand lay-up, has high stiffness and strength, good resistance for impact, fatigue, corrosion and in-plane failure. The DCB(Double Cantilever Beam) specimen made of woven fabric epoxy composite had the size of 180mm $\times$ 25mm $\times$ 5mm and the insert of 65mm. The Mode I interlaminar toughness of specimen was measured according to ASTM 5528-01. The crack propagation behavior of the DCB specimen was simulated using FEA with cohesive elements that model the adhesive layer between woven fabric plies.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1323-1326
• /
• 1994

the application of epoxy composite materials for outdoor insulating systems has some significant advantages compared with conventional inorganic materials, that is low weight in combination with high mechanical strength, small dimensions and design versatility. The experimental results for the basis composition and interlace characteristics of the matrix resin/inorganic fillers($SiO_2$) which are the composite materials have been studied. The electrical characteristics(electrical breakdown, dielectric, insulating resistivity, tracking) and mechanical characteristics( tensile strength, elongation, flexible strength) in the epoxy composite materials have been studied. The life of the epoxy composite material was evaluated by accelerated Weather-Ometer test and the degradation process due to outdoor exposure condition is discussed with respect to the mechanical and electrical properties.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.406-409
• /
• 2004

In this study, we investigated compressive characteristics of seawater-absorbed carbon-epoxy composite under hydrostatic pressure environment. The hydrostatic pressures applied were 0.1 MPa, 100 MPa, 200 MPa, and 270 MPa. The results showed that the compressive elastic modulus increased about 10 % as the hydrostatic pressure increased from 0.1 MPa to 200 MPa. The modulus increased 2.3 % more as the pressure increased to 270 MPa. Fracture strength and fracture strain increased with pressure in a linear fashion. Fracture strength increased 28 % and fracture strain increased 8.5 % as the hydrostatic pressure increased from 0.1 MPa to 270 MPa.

• Fibers and Polymers
• /
• 제5권4호
• /
• pp.259-263
• /
• 2004

Rubber-modified epoxy resins have been employed as adhesive and matrix materials for glass and corbon-fiber composites. The behavior of fracture around a crack tip for rubber-modified epoxy resin is investigated through the acoustic emission (AE) analysis of compact tension specimens. Damage zone and rubber particles distributed around a crack tip were observed by a polarized optical microscope and an atomic force microscope (AFM). The damage zone in front of pre-crack tip in rubber-modified specimen $(15wt\%\; rubber)$ began to form at about $13\%$ level of the fracture load and grew in size until $57\%$ load level. After that, the crack propagated in a stick-slip manner. Based on time-frequency analysis of AE signals and microscopic observation of damage zone, it was thought that AE signals with frequency bands of 0.15-0.20 MHz and 0.20­0.30 MHz were generated from cavitation in the damage zone and crack propagation, respectively.

• 대한기계학회논문집
• /
• 제13권4호
• /
• pp.625-635
• /
• 1989

본 논문에서는 이 방법을 사용하여 glass/epoxy와 graphite/epoxy 유한평판이 균일응력과 균일변위 경계조건을 받을 때 평판 종횡비 H/W를 1,2,3, 균열길이와 폭의 비 L/W를 0.1부터 0.7까지, 균열각도를 0, 30, 45, 60으로 변화 시키면서 응력강도수정계수를 구하려고 한다.

• Transactions on Electrical and Electronic Materials
• /
• 제14권2호
• /
• pp.101-104
• /
• 2013

The effect of the mixing ratio of spherical silica on the electrical insulation breakdown strength in an epoxy/silica composite was studied. Spherical silicas with two average particle sizes of $5{\mu}m$ and $20{\mu}m$ were mixed in different mixing ratios, and their total filling content was fixed at 60 wt%. In order to observe the dispersion of the silicas and the interfacial morphology between silica and epoxy matrix, scanning electron microscopy (SEM) was used. The electrical insulation breakdown strength was estimated in sphere-sphere electrodes with different insulation thicknesses of 1, 2, and 3 mm. Electrical insulation breakdown strength decreased with increasing mixing ratio of $5/20{\mu}m$ and the thickness dependence of the breakdown strength was also observed.

• 한국진공학회지
• /
• 제9권3호
• /
• pp.279-284
• /
• 2000

본 연구는 옥외용 epoxy/glass fiber의 열화과정을 분석하기 위하여 FRP 적층판을 고온과 수에 노출시켰다. 열화과정은 접촉각, 표면전위감쇠, 표면저항률의 비교에 의해 평가하였다. 젖음성의 변화는 열처리 시료에서 $200^{\circ}C$까지 접촉각이 증가하였지만 수분처리 시료는 감소하였다. 표면전위감쇠 특성은 수분처리 시료에서는 감소하지만, 열처리 시료는 미 처리와 비교해서 증가하였다. 또한, 표면저항률은 접촉각의 변화와 같은 경향을 보이고 있다.