• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.13-22
• /
• 2010

The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. $\beta$-SiC powder with 0, 2, 6, 10 wt% of $\alpha$-SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at $1700-1850^{\circ}C$ for 10 min. The heating rate, applied pressure and sintering atmosphere were kept at $100^{\circ}C/min$, 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to $1700^{\circ}C$ consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at $1750^{\circ}C$ and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of $\alpha$-SiC seeds into $\beta$-SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the $\alpha$-SiC seeds added in $\beta$-SiC, the rate of grain growth decreased with $\alpha$-SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.281-284
• /
• 2003

The microstructural changes of Al-Zn-Mg-Cu alloy containing Sc during hot extrusion and post heat treatment is investigated. Two kinds of Al-Sc alloys with different alloying elements (B1, B2) are hot extruded to make I-shape bars at 380$^{\circ}C$, then the bars are solution treated at 480$^{\circ}C$ for 2hrs followed by artificial aging at 120$^{\circ}C$ for 24hrs. The interior microstructure of as extruded bar consists of elongated grains, however, fine equiaxed grains are mainly observed around surface. The microstructural gradient suggests that different restoration process can proceed during the hot extrusion. For B1 and B2, different grain growth behaviors are found around the surface during the post heat treatment. Rapid grain growth behavior around the surface is discussed related with the crystallographic orientation of the grain.

• Korean Journal of Materials Research
• /
• v.16 no.1
• /
• pp.68-74
• /
• 2006

2024 Al alloys were severely deformed by equal channel angular pressing(ECAP) to obtain an ultrafine grain structure. The more deformation amount increased, the more grain size decreased. Most of the grain structure were changed from elongated to equiaxed shape with increasing pass number. The morphology of S' phases was also changed from rod-type to spherical type. The grain size of 6 passed specimen was 100 to 200 nm, and the size of S' phases was about 10 nm in the microstructure. XRD measurements have revealed that the texture formed by plastic deformation disappeared in the 6 passed specimen. SP test results described that the start of crack propagation occurred at the transition zone between plastic bending and membrane stretching because of small elongation. The maximum strength of ECA pressed specimen increased 1.9 GPa to 2.9 GPa with increasing pass number.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.118-122
• /
• 2003

Alpha-SiAlON ceramics having various compositions and modifying cations were investigated with respect to their phase stability, transformation kinetics. and resulting microstructures. Each composition was heat treated at 150$0^{\circ}C$ for 1h and measured the $\alpha$-SiAlON transformation. The phase-boundary composition in the single-phase $\alpha$-SiAlON region showed sluggish transformation from $\alpha$-$Si_3N_4$ to $\alpha$-SiAlON compared to the phase-center composition in the diagram. Using the different rare earth modifying cations, dependence of transformation kinetics on the phase stability in a fixed composition was also explained. By changing size of the stable u-phase region with exchanging cations, systematic change in transformation was observed. Transformation rate of $\alpha$-SiAlON at low temperature has an important role on controlling the final microstructure. Less transformation gives more chances to develop elongated grain in the microstructure.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.83-89
• /
• 2000

$Si_3N_4$ powder with 2wt% $Al_2O_3$ and 6wt% $Y_2O_3$ additives was sintered by gas pressure sintering (GPS) technique. The variations in the unlubricated wear behavior depending on sintering time were compared. Tribological properties depending on sintering time are associated with fracture toughness as well as flexural strength of materials. When increasing the sintering time, the larger elongated grains were formed as a result of exaggerated grain growth. As the fracture toughness and flexural strength decreased, the wear volume increased. On the basis of these experimental results, the unlubricated wear properties of silicon nitride were found to be governed mostly by both the fracture toughness and the flexural strength of the material.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.499-504
• /
• 2002

The microstructural change associated with the hardness profile in friction stir welded, age-hardenable 6005 Al alloy had been evaluated. Frictional heat and plastic flow during friction stir welding created the fine recrystallized grain (Stir Zone, SZ), the elongated and recovered grain (Thermo-Mechanical Affected Zone, TMAZ) in the weld zone. Heat affected zone (HAZ), which could be only identified by hardness test because there is no difference in the grain structure compared with that of the base metal, was formed beside the weld zone. A softened region had been formed near the weld zone during friction stir welding process. The softened region was characterized by the dissolution and coarsening of the strengthening precipitate during the friction stir welding. The sound joints of 6005 Al alloys were successfully formed under a wide range of the friction stir welding conditions.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.429-433
• /
• 2013

Silicon, carbon, and B4C powders were used as raw materials for the fabrication of porous SiC. ${\beta}$-SiC was synthesized at $1500^{\circ}C$ in an Ar atmosphere from a silicon and carbon mixture. The synthesized powders were pressed into disk shapes and then heated at $2100^{\circ}C$. ${\beta}$-SiC particles transformed to ${\alpha}$-SiC at over $1900^{\circ}C$, and rapid grain growth of ${\alpha}$-SiC subsequently occurred and a porous structure with elongated plate-type grains was formed. The mechanism of this rapid grain growth is thought to be an evaporation-condensation reaction. The mechanical properties of the fabricated porous SiC were investigated and discussed.

• International Journal of Korean Welding Society
• /
• v.3 no.2
• /
• pp.46-52
• /
• 2003

The refinement of microstructure and phase transformation near the interface of pure copper/carbon steel dissimilar metals joints with various friction welding parameters have been studied in this paper. The microstructure of copper and carbon steel joints were changed to be a finer grain compared to those of the base metals due to the frictional heat and plastic deformation. The microstructure of copper side experienced wide range of deformed region from the weld interface and divided into very fine equaxied grains and elongated grains. Especially, the microstructures near the interface on carbon steel were transformed from ferrite and pearlite dual structure to fine ferrite, grain boundary pearlite and martensite due to the welding thermal cycle and rapid cooling rate after welding. These microstructures were varied with each friction welding parameters. The recrystallization on copper side is reason for softening in copper side and martensite transformation could explain the remarkable hardening region in carbon steel side.

• Journal of Korean Ophthalmic Optics Society
• /
• v.11 no.2
• /
• pp.85-89
• /
• 2006

To research of the improved mechanical properties of materials for spectacle lens cutting, SiC and TiC were used as the main powder. Also, $Al_2O_3$ and $Y_2O_3$ was included as a sintering additive. The weight ratio of the alumina($Al_2O_3$) to yttria($Y_2O_3$) was set to 1:1. The materials for spectacle lens cutting were fabricated by hot-pressing at $1810^{\circ}C$ for 1h and subsequently annealed at $1860^{\circ}C$ for 3, 6 and 12h to initiated grain growth. The longer annealing time is, the bigger the grain size is. The microstructures were observed by scanning electron microscopy (SEM). The SEM images were quantitatively analyzed by image analysis (Image-Pro Plus, Media Cybernetics, Maryland, U.S.A.). Crack deflection by elongated SiC grains was most frequently observed as the dominant toughening mechanism. Crack deflection was generally observed for elongated SiC grains with aspect ratio(AR) > 2.5 and grain thickness < $2.3{\mu}m$. Crack bridging was also observed as one of the operating toughness mechanism.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.11-18
• /
• 2004

Asymmetric rolling, in which the circumferential velocities of the upper and lower rolls are different, can give rise to intense plastic shear strains and in turn shear deformation textures through the sheet thickness. The ideal shear deformation texture of fcc metals can be approximated by the <111> // ND and $\{001\}<110>$ orientations, among which the former improves the deep drawability. The ideal shear deformation texture for bcc metals can be approximated by the Goss $\{110\}<001>\;and\;\{112\}<111>$ orientations, among which the former improves the magnetic permeability along the <100> directions and is the prime orientation in grain oriented silicon steels. The intense shear strains can result in the grain refinement and hence improve mechanical properties. Steel sheets, especially ferritic stainless steel sheets, and aluminum alloy sheets may exhibit an undesirable surface roughening known as ridging or roping, when elongated along RD and TD, respectively. The ridging or roping is caused by differently oriented colonies, which are resulted from the <100> oriented columnar structure in ingots or billets, especially for ferritic stainless steels, that is not easily destroyed by the conventional rolling. The breakdown of columnar structure and the grain refinement can be achieved by asymmetric rolling, resulting in a decrease in the ridging problem.