• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.12
• /
• pp.938-943
• /
• 2018

Thin nano-sized fibres were prepared by an electrospinning method. The spinning appratus consisted of pump for polymer injection, nozzle and nozzle rotus, and an aluminum plate collected the polymer fibers. Its surface was chemically modified for selective improved adsorption of carbon monoxide at indoor level. The chemical activation enabled to form the fibres 250-350 nm in thickness with pore sizes distributed between 0.6 and 0.7 nm and an average specific surface area of $569m^2/g$. The adsorption capacities of pure (100%) and indoor (0.3%) $CO_2$, of which level frequently appears, at the ambient condition were improved from 1.08 and 0.013 to 2.2 and 0.144 mmol/g, respectively. It was found that the adsorption amount of $CO_2$ adsorbed by the chemically activated carbon nanofiber prepared through chemical activation would vary depending on the ratio of specific surface area and micropores. In particular, chemical interaction between adsorbent surface and gas molecules could enhance the selective capture of weak acidic $CO_2$.

• Polymer(Korea)
• /
• v.32 no.4
• /
• pp.359-365
• /
• 2008

We have fabricated a novel thermo-responsive nanofibrous surfaces by grafting PIPAAm by electron beam irradiation onto poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV) nanofibrous mats. The electrospun PHBV nanofiber structures revealed randomly aligned fibers with average diameter of 400 nm. Increased atomic percent of nitrogen was observed on the PIPAAm-grafted PHBV mats after electron beam irradiation determined by ESCA. The amounts of PIPAAm-grafted onto PHBV films were $6.49{\mu}g/cm^2$ determined by ATR-FTIR. The PIPAAm-grafted surfaces exhibited decreasing contact angles by lowering the temperature from 37 to $20^{\circ}C$, while ungrafted PHBV surfaces had negligible contact angle change. This result indicates that PIPAAm surfaces, which are hydrophobic at the higher temperature, became markedly more hydrophilic in response to a temperature reduction due to spontaneous hydration of the surface-grafted PIPAAm. Thermo-responsive nanofibers showed good tissue compatibility. Cultured cells were well detached and recovered from the surfaces by changing culture temperature from 37 to $20^{\circ}C$.

• Polymer(Korea)
• /
• v.32 no.2
• /
• pp.131-137
• /
• 2008

We have fabricated polystyrene (PS) nanofibrous scaffold for hepatocyte culture by electrospinning method and subsequently coated with specific ligand of Poly[N-p-vinylbenzyl-O-$\beta$-D-galactopyranocyl-($1{\rightarrow}4$)-D-gluconamide](PVLA) to enhance hepatocytes attachment. Rat hepatocytes behavior on the PVLA-coated and non-coated PS nanofibrous matrices have been investigated. Electrospun PS nanofiber structures revealed randomly aligned fibers with average diameter of 500 nm. It is observed that PS nanofibrous matrix could incorporate many cells into the interior of the matrix probably due to the suitable pore size. Cell viabilities cultured on PVLA-coated PS nanofibrous mats were maintained for 3 weeks, while it was decreased rapidly on PVLA-coated PS dishes. High hepatic functions especially for albumin secretion and ammonia removal were maintained at least for 2 weeks on nanofibrous mats but rapidly decreased on flat PS dishes. These results indicate that nanofibrous structure enabled 3-D culture with high level of cell-cell contact results in providing cell-cell communications and subsequent long-term maintenance of specific cell functions.

• Applied Chemistry for Engineering
• /
• v.23 no.1
• /
• pp.47-52
• /
• 2012

Porous carbon nanofibers were prepared as a gas sensor electrode to study the $CO_2$ sensing property based on effects of porosity and introduced amine functional groups. Electrospun fibers were obtained by using electrospinning method with polyacrylonitrile precursor and they were treated by the thermal treatment and chemical activation. Amine functional groups were introduced by the liquid state treatment using diethylenetriamine. The specific surface area increased up to $2000m^2/g$ by the chemical activation. The Introduced amine functional group was identified using FT-IR spectroscopy. $CO_2$ gas sensing property was improved as four folds via introduced amine functional groups on the activated carbon nanofiber. In conclusion, the gas sensing property was improved based on the developed porosity by the chemical activation and the chemical attraction of $CO_2$ gas by introduced functional groups.

• Applied Chemistry for Engineering
• /
• v.19 no.4
• /
• pp.413-420
• /
• 2008

Over the past decade, there have been significant advancement in the field of electrospinning area. This study has focused on preparing yarn using polycarbonate (PC) nanofibers including modified multi-walled carbon nanotube (mMWNT) by solution electrospinning process using the mixture of solvents consisting of tretrahydronfuran (THF) and N,N-dimethylformamide (DMF). In order to enhance the dispersion, MWNT was chemically modified. TEM analysis for the prepared PC/mMWNT nanofibers reveals that mMWNT was well-dispersed into the PC nanofiber matrix. Also with increasing contents of mMWNT, thermal stability of PC/mMWNT nanofibers was improved than that of PC nanofibers. Moreover when 3 to 5 wt% of mMWNT was added, the nanofibers showed good electrical properties expecting antistatic effect, ranging 109.1~109.5 ${\Omega}$. It was confirmed that the multi-filament fibers using PC/mMWNT had $60{\sim}100{\mu}m$ in diameter and 4~5 cm in length.

• Korean Chemical Engineering Research
• /
• v.57 no.4
• /
• pp.559-564
• /
• 2019

Hierarchical $ZnCo_2O_4$ hollow nanofibers were prepared by electrospinning and subsequent heat-treatment process. The spinning solution containing polystyrene (PS) nanobeads was electrospun to nanofibers. During heat-treatment process, PS nanobeads in the composite were decomposed and therefore generated numerous pores uniformly in the structure, which facilitated the heat transfer and gas penetration into the structure. The resulting hierarchical $ZnCo_2O_4$ hollow nanofibers were applied as an anode material for lithium-ion batteries. The discharge capacity of the nanofibers was $815mA\;h\;g^{-1}$ ($646mA\;h\;cm^{-3}$) after the 300th cycle at a high current density of $1.0A\;g^{-1}$. However, $ZnCo_2O_4$ nanopowders showed the discharge capacity of $487mA\;h\;g^{-1}$ ($450mA\;h\;cm^{-3}$) after 300th cycle. The excellent lithium ion storage property of the hierarchical $ZnCo_2O_4$ hollow nanofibers was attributed to the synergetic effects of the hollow nanofiber structure and the $ZnCo_2O_4$ nanocrystals composing the shell. The hierarchical hollow nanofiber structure introduced in this study can be extended to various metal oxides for various applications, including energy storage.

• Polymer(Korea)
• /
• v.32 no.4
• /
• pp.334-339
• /
• 2008

Recently electro spinning is a widely used simple technique to prepared micro- to nanometer-sized fiber of various polymers. In general, a normal multiple-nozzle electro spinning system has been difficult to achieve high production-rate fabricating micro/nanofibers due to the interference of electric field between individual nozzles in the process. To reduce the interference effect of electric field between nozzles, we developed a multi-nozzle electrospinning system supplemented with auxiliary electrodes. Poly($\varepsilon$-carprolactone)(PCL), which has good mechanical property and biocompatibility, was electrospun by the multi-nozzle electro spinning system. Electrospinnability, product rate, and size uniformity of spun fibers for the system with and without auxiliary electrodes were characterized. As a result, the multi-nozzle electrospinning system supplemented with auxiliary electrodes provides excellently stable processability and showed high mass productivity of PCL-nanofibers relative to a normal multi-nozzle electro spinning system.

• Journal of the Korean Ceramic Society
• /
• v.55 no.3
• /
• pp.267-274
• /
• 2018

$TiO_2/CuS$ nanocomposites were fabricated by precipitation of nanosized CuS via sonochemical method on electrospun $TiO_2$ nanofibers, and their structure, chemical bonding states, optical properties, and photocatalytic activity were investigated. In the $TiO_2/CuS$ nanocomposite, the position of the conduction band for CuS was at a more negative than that of TiO; meanwhile, the position of the valence band for CuS was more positive than those for TiO, indicating a heterojunction structure belonging to type-II band alignment. Photocatalytic activity, measured by decomposition of methylene blue under visible-light irradiation (${\lambda}$ > 400 nm) for the $TiO_2/CuS$ nanocomposite, showed a value of 85.94% at 653 nm, which represented an improvement of 52% compared to that for single $TiO_2$ nanofiber (44.97% at 653 nm). Consequently, the photocatalyst with $TiO_2/CuS$ nanocomposite had excellent photocatalytic activity for methylene blue under visible-light irradiation, which could be explained by the formation of a heterojunction structure and improvement of the surface reaction by increase in surface area.

• Textile Coloration and Finishing
• /
• v.29 no.4
• /
• pp.256-267
• /
• 2017

The purpose of this study was to analyze the functional ingredients of Perilla Frutescens L. Britt extracts and to confirm the possibility of producing PVA nanofibers using extracts. Distilled water, 3% aqueous sodium hydroxide solution and ethanol were used as extraction solvents. The electrospinning was carried out at a PVA concentration of 12%, an applied voltage of 10 kV and a tip to collector distance of 15cm. The contents of volatile substances, essential oils, total polyphenols and flavonoids of the extracts were measured to examine the constituents of functional materials. Flavor components and esters were identified in 3% sodium hydroxide and ethanol extracts. The content of polyphenols and flavonoids in ethanol extracts was higher than that of medicinal plants. 1wt.% of Tween 20 was added to disperse the essential oil components of the ethanol extract. Addition of a dispersant made it possible to produce a homogeneous mixture by having some compatibility with the ethanol extracts and the PVA molecule. When the concentration of the ethanol extract was 0.25 and 0.5wt%, relatively uniform PVA nanofiber having an average diameter of 350 to 365nm could be produced. The results of FT-IR, XRD and DSC analysis confirmed that Perilla Frutescens L. Britt ethanol extract was well mixed with PVA molecules and was electrospun.

• Science of Emotion and Sensibility
• /
• v.19 no.3
• /
• pp.43-50
• /
• 2016

The uniform nanofibers of polyurethane with different contents of Juniperus Chinensis extracts were successfully prepared by electrospinning method. Polyurethane is widely used as functional polymers in the industrials, medical field as their properties can be tailor-made by adjusting their compositions. Juniperus Chinensis has been reported for anti-tumor, anti-bacterial, anti-fungal, and anti-viral activities. PU/Juniperus Chinensis extracts composite nanofibers were produced at different Juniperus Chinensis extracts concentrations (0.25, 0.5, 1, 1.5wt.%). The effects of the major parameters in electrospinning process such as tip to collector distance (TCD), voltage, polymer concentration on the average diameter of electrospun nanoweb were investigated. As results, 12wt% PU solution concentration, 8kV applied voltage and 15cm tip to collector distance were identified as optimum conditions for electrospinning the composite nanofibers. The diameter and morphology of the nanocomposite nanofibers were confirmed by a scanning electron microscopy (SEM). The resulting fibers exhibited a uniform diameter ranging from 435nm~547nm. It has been found that the average diameters of fibers decreased by the adding of Juniperus Chinensis extracts. These nanowebs can be used for medical materials, protective clothing, and antimicrobial filters.