• Journal of the Korean Vacuum Society
• /
• v.7 no.s1
• /
• pp.57-77
• /
• 1998

Heteroepitaxial $Y_2O_3$ films were grown on a Si(111) substrate by ionized cluster beam deposition(ICBD) in ultra high vacuum, and its qualities such as crystllitnity, film stress, and morphological characteristics were investigated using the various measurement methods. The crystallinity was investigated by x-ray diffraction (XRD) and reflection high energy electron diffraction (RHEED). Interface crystallinity was also examined by Rutherford backscattering spectroscopy(RBS) channeling, transmission electron microscopy(TEM). The stress of the films was measured by RBS channeling and XRD. Surface and interface morphological characteristics were investigated by atomic force microscopy (AFM) and x-ray scattering method. Comparing the interface with the surface characteristics, we can conclude that many defects at the interface region were generated by interface reaction between the yttrium metal and SiO2 layer and by ion beam characteristic such as shallow implantation, so that they influenced the film qualities. The film quality was dominantly depended on the characteristic temperature range. In the temperature range from $500^{\circ}C$ to $600^{\circ}C$, the crystallinity was mainly improved and the surface roughness was drastically decreased. On the other hand, in the temperature range from $600^{\circ}C$ to $700^{\circ}C$, the compressive stress and film density were dominantly increased, and the island size was more decreased. Also the surface morphological shape was transformed from elliptical shape to triangular. The film stress existed dominantly at the interface region due to the defects generation.

• Journal of the Korean Vacuum Society
• /
• v.10 no.1
• /
• pp.119-126
• /
• 2001

Hydrogenated amorphous carbon (a-C:H) films were deposited by ECR-PECVD (electron cyclotron resonance-plasma enhanced chemical vapor deposition) method with deposition conditions such as ECR plasma source power, gas composition of methane and hydrogen, deposition time and substrate bias voltage. The hydrogen content in the films has been measured by ERDA (elastic recoil detection analysis) using 2.5 MeV $He^{++}$ ion beam. From the results of AES (Auger electron spectroscopy), RBS (Rutherford backscattering spectrometry) and ERDA, the composition elements of deposited film were confirmed the carbon atom and the hydrogen atom. It was observed by FTIR (Fourier transform infrared) that the hydrogen contents in the film varied according to the deposition conditions. In deposition condition of substrate bias voltage, the hydrogen contents were decreased remarkably because the amount of dehydrogenation in films was increased as the substrate bias voltage increased. In the rest deposition conditions, the hydrogen contents in the film were measured in the range 45~55%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05d
• /
• pp.45-48
• /
• 2003

BiSrCaCuO thin films were fabricated by atomic layer-by-layer deposition using an ion beam sputtering method. 10 wt% and 90 wt% ozone mixed with oxygen were used with ultraviolet light irradiation to assist oxidation. At early stages of the atomic layer by layer deposition, two dimensional epitaxial growth which covers the substrate surface would be suppressed by the stress and strain caused by the lattice misfit, then three dimensional growth takes place. Since Cu element is the most difficult to oxidize, only Sr and Bi react with each other predominantly, and forms a buffer layer on the substrate in an amorphous-like structure, which is changed to $SrBi_2O_4$ by in-situ anneal.

• Journal of the Korean Vacuum Society
• /
• v.12 no.S1
• /
• pp.63-66
• /
• 2003

It is experimentally shown that a $TiO_2$ film on Si(111) substrate was prepared by using the technique of D.C. reaction sputter deposition with $Ar^{+}$ ion beam bombardment, and a layer-like structure was observed from the depth profile of the interface between $TiO_2$ film and Si substrate with Scanning Electron Microscopy and Electron Probe. It was also surprisingly discovered that Ti atoms could be detected at about 9 $\mu$m depth. The $TiO_2$-Si interface bombarded by $Ar^{+}$ ion beams revealed multi-layer structures, a mechanism might be caused by defect diffusion, impurity and matrix relocation. Multi-relocations of impurity and matrix atoms were as a result of profile broadening of the $TiO_2$-Si interface, and the spread due to matrix relocation in this system is shown to exceed much more the spread due to impurity relocation.

• Korean Journal of Materials Research
• /
• v.33 no.11
• /
• pp.497-501
• /
• 2023

ZnO/Cu/ZnO (ZCZ) thin films were deposited at room temperature on a glass substrate using direct current (DC) and radio frequency (RF, 13.56 MHz) magnetron sputtering and then the effect of post-deposition electron irradiation on the structural, optical, electrical and transparent heater properties of the films were considered. ZCZ films that were electron beam irradiated at 500 eV showed an increase in the grain sizes of their ZnO(102) and (201) planes to 15.17 nm and 11.51 nm, respectively, from grain sizes of 13.50 nm and 10.60 nm observed in the as deposited films. In addition, the film's optical and electrical properties also depended on the electron irradiation energies. The highest opto-electrical performance was observed in films electron irradiated at 500 eV. In a heat radiation test, when a bias voltage of 18 V was applied to the film that had been electron irradiated at 500 eV, its steady state temperature was about 90.5 ℃. In a repetition test, it reached the steady state temperature within 60 s at all bias voltages.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.388-388
• /
• 2011

Graphene, with its unique physical and structural properties, has recently become a proving ground for various physical phenomena, and is a promising candidate for a variety of electronic device and flexible display applications. The physical properties of graphene depend directly on the thickness. These properties lead to the possibility of its application in high-performance transparent conducting films (TCFs). Compared to indium tin oxide (ITO) electrodes, which have a typical sheet resistance of ~60 ${\Omega}/sq$ and ~85% transmittance in the visible range, the chemical vapor deposition (CVD) synthesized graphene electrodes have a higher transmittance in the visible to IR region and are more robust under bending. Nevertheless, the lowest sheet resistance of the currently available CVD graphene electrodes is higher than that of ITO. Here, we report an ingenious strategy, irradiation of MeV electron beam (e-beam) at room temperature under ambient condition,for obtaining size-homogeneous gold nanoparticle decorated on graphene. The nano-particlization promoted by MeV e-beam irradiation was investigated by transmission electron microscopy, electron energy loss spectroscopy elemental mapping, and energy dispersive X-ray spectroscopy. These results clearly revealed that gold nanoparticle with 10~15 nm in mean size were decorated along the surface of the graphene after 1.0 MeV-e-beam irradiation. The fabrication high-performance TCF with optimized doping condition showed a sheet resistance of ~150 ${\Omega}/sq$ at 94% transmittance. A chemical transformation and charge transfer for the metal gold nanoparticle were systematically explored by X-ray photoelectron spectroscopy and Raman spectroscopy. This approach advances the numerous applications of graphene films as transparent conducting electrodes.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.154-154
• /
• 1999

금속산화막은 전자부품 및 광학적 응용에 널리 사용되고 있다. 특히 알루미늄의 산화막은 유전체의 재료로 커패시터에 많이 사용되고 있다. 이러한 알루미늄 산화막을 plasma를 이용한 ion plating에 의해 형성하였다.Activated Reactive Evaporation은 화합물의 증착율을 높이는데 좋은 증착법이다. 이러한 증착법에는 reactive ion plating와 ion-assisted deposition 그리고 ion beam sputtering 등이 있다. 본 연구에서는 알루미늄 산화막을 증착시키기 위해 plasma를 이용한 electron-beam법을 사용하였다. Turbo molecular pump로 챔버 내의 진공을 약 10-7torr까지 낸린 후 5$\times$10-5torr까지 O2와 Ar을 주입시켰다. 각 기체의 분압은 RGA(residual gas analyzer)로 조사하여 일정하게 유지시켰다. plasma를 발생시키기 위해 filament에서 열전자를 방출시키고 1kV 정도의 electrode에 의해 가속시켜 이들 기체들과 반응시켜 plasma를 발생시켰다. 금속 알루미늄을 5kV정도의 고전압과 90mA의 전류로 electron beam에 의해 증발시켰다. 기판의 흡착율을 높ㅇ기 위해 기판에 500V로 bias 전압을 걸어 주었다. 증발된 금속 알루미늄 증기들이 plasmaso의 산소 이온들과 활성 반응을 이루어 알루미늄 기판 위에 Al2O3막을 형성하였다. 알루미늄 산화막을 분석하기 위해 XPS(X-ray Photoelectron Spectroscopy)로 화학적 조성을 조사하였는데, 알루미늄의 2p전자의 binding energy가 76.5eV로 측정되었다. 이는 대부분 증착된 알루미늄이 산소 이온과 반응하여 Al2O3로 형성된 것이다. SEM(Scanning electron Microscopy)과 AFM(Atomim Force microscopy)으로 증착박 표면의 topology와 roughness를 관찰하였다. grain의 크기는 10nm에서 150nm이었고 증착막의 roughness는 4.2nm이었다. 그리고 이 산화막에 전극을 형성하여 유전 상수와 손실률 등을 측정하였다. 이와 같이 plasma를 이용한 3-beam에 의한 증착은 금속의 산화막을 얻는데 유용한 기술로 광학 재료 및 유전 재료의 개발 및 연구에 많이 사용될 것으로 기대된다.

• Journal of the Korean Magnetics Society
• /
• v.4 no.4
• /
• pp.313-318
• /
• 1994

We have investigated the effects of deposition angle on magnetic and magneto-optic properties in Co/Pt multilayer thin films. which were prepared bye-beam evaporation on tilted substrates. with varying tilt angle from $0^{\circ}$ to $60^{\circ}$. The structure of the specimens was examined by x-ray diffractometer and scanning electron microscope. and the magnetic and magneto-optical properties were measured by VSM, torque magnetometer, and Kerr loop tracer. X-ray diffractometry revealed that all of the specimens had multilayer structure and growth orientation of column followed the tangent rule but the crystallograpic orientation, <111>, was slightly deviated from the substrate normal even though the deposition angle was increased up to $60^{\circ}$. A decrement of the magnetization and Kerr angle with the deposition angle was related with that of the film density due to increasing porosity. The perpendicular mag¬netic anisotropy was also decreased with increasing the deposition angle.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.92-97
• /
• 2002

We establish a visible light emission from porous polycrystalline silicon nano structure(PPNS). The PPNS layer are formed on heavily doped n-type Si substrate. 2um thickness of undoped polycrystalline silicon deposited using LPCVD (Low Pressure Chemical Vapor Deposition) anodized in a HF: ethanol(=1:1) as functions of anodizing conditions. And then a PPNS layer thermally oxidized for 1 hr at $900 ^{\circ}C$. Subsequently, thin metal Au as a top electrode deposited onto the PPNS surface by E-beam evaporator and, in order to establish ohmic contact, an thermally evaporated Al was deposited on the back side of a Si-substrate. When the top electrode biased at +6V, the electron emission observed in a PPNS which caused by field-induces electron emission through the top metal. Among the PPNSs as functions of anodization conditions, the PPNS anodized at a current density of $10mA/cm^2$ for 20 sec has a lower turn-on voltage and a higher emission current. Furthermore, the behavior of electron emission is uniformly maintained.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.210.2-210
• /
• 2003