The corrosion inhibition properties of conifer cone (Pinus resinosa) extract were studied in synthetic concrete pore solutions (SCPS) with and without chloride environments by electrochemical methods. The electrochemical impedance spectroscopy (EIS) revealed that the conifer cone (CC) extract showed promising inhibition behavior by diminishing the corrosion rate of steel rebar both solutions i.e. with and without chloride. The extract of conifer cone hinders the corrosion reaction between steel rebar and aggressive ions. Further, it can be verified that the up to 1000mg.L-1 of CC extract can able to reduce the corrosion rate of steel rebar in chloride contaminated concrete.

• Corrosion Science and Technology
• /
• v.16 no.3
• /
• pp.100-108
• /
• 2017

In this investigation corrosion behavior of newly developed high-pressure die cast Al-Ni (N15) and Al-Ni-Ca (NX1503) alloys was studied in 3.5% NaCl solution. The electrochemical corrosion behavior was evaluated using open circuit potential (OCP) measurement, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques. Potentiodynamic polarization results validated that NX1503 alloy exhibited lower corrosion current density ($i_{corr}$) value ($5.969{\mu}A/cm^2$) compared to N15 ($7.387{\mu}A/cm^2$). EIS-Bode plots revealed a higher impedance (${\mid}Z{\mid}$) value and maximum phase angle value for NX1503 than N15 alloy. Equivalent circuit curve fitting analysis revealed that surface layer ($R_1$) and charge transfer resistance ($R_{ct}$) values of NX1503 alloy was higher compared to N15 alloy. Immersion corrosion studies were also conducted for alloys using fishing line specimen arrangement to simultaneously measure corrosion rates from weight loss ($P_W$) and hydrogen volume ($P_H$) after 72 hours and NX1503 alloy had lower corrosion rate compared to N15 alloy. The addition of Ca to N15 alloy significantly reduced the Al3Ni intermetallic phase and further grain refinement may be attributed for reduction in the corrosion rate.

• Journal of the Korean Chemical Society
• /
• v.56 no.4
• /
• pp.448-458
• /
• 2012

In order to develop alloy resistance in aggressive sulphat ion, the corrosion behavior of metallic glasses $Ni_{92{\cdot}3}Si_{4.5}B_{32}$, $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ (at %) at different concentrations of $H_2SO_4$ solutions was examined by electrochemical methods and Scanning Electron Microscope (SEM) and X-ray Photoelectron Microscopy (XPS) analyses. The corrosion kinetics and passivation behavior was studied. A direct proportion was observed between the corrosion rate and acid concentration in the case of $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloys. Critical concentration was observed in the case of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ alloy. The influence of the alloying element is reflected in the increasing resistance of the protective film. XPS analysis confirms that the protection film on the $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ alloy was NiS which is less protective than that formed on Cr containing alloys. The corrosion rate of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$. alloys containing 7% and 13% Cr are $7.90-26.1{\times}10^{-3}$ mm/y which is lower about 43-54 times of the alloy $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ (free of Cr). The high resistance of $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloy at the very aggressive media may due to thicker passive film of $Cr_2O_3$ which hydrated to hydrated chromium oxyhydroxide.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.83-90
• /
• 2017

The corrosion behavior of a rebar in concrete according to the amount of NaCl and $LiNO_2$ was observed by using Electrochemical Impedance Spectroscopy. The corrosion was accelerated in a short time by using dry/wet cycles method, which is one of the corrosion acceleration methods, and though the value of measured impedance, equivalent circuit can be introduced. It was confirmed that the passive film of a embedded rebar in concrete with NaCl was broken quickly, and when $0.6M\;LiNO_2$ was added, the velocity of ongoing corrosion was declined considerably compared to the amount of NaCl. However, when $1.2M\;LiNO_2$ was added, it was confirmed that the passive film was not broken and its performance remained, compared to the amount of NaCl.

• Proceedings of the KIPE Conference
• /
• 2017.11a
• /
• pp.167-168
• /
• 2017

This paper investigates to identify an optimal for analysis of battery behavior in system-level applications such as Battery Energy Storage Systems in Smart Grid infrastructures and Electrical vehicles. At system level applications, it is mandatory to check model for meaningful equivalency and practical ability for extension from unit cell to Battery stack. The investigation of current battery models in relation to their suitability for study and analysis of system level applications of battery helpful for identification of optimal model and it also provides an intuition and direction to develop the most suitable model, if such models are not available already.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.105-106
• /
• 2017

The metal spray method, one of the surface anti-corrosion methods to prevent the corrosion of the steel material, does little effects on the material, while it can be used on a wider surface. However, metal spraying is used only in a limited environment, and research on the case of using with concrete is lacking. The purpose of this study was to observe the corrosion behavior of steels with metal spray coatings in concrete using electrochemical methods And to evaluate the performance of the method according to the type of metal used in the metal spray. As a result, the Al metal spray coating showed the best performance, because Aluminum is oxidized in the cement mortar and forms alumina oxide film.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.6
• /
• pp.283-285
• /
• 2007

The molten carbonate fuel cell has conspicuous feature and high potential in being used as an energy converter of various fuel to electricity and heat. However, the molten carbonate fuel cell which use strongly corrosive molten carbonate at $650^{\circ}C$ have many problem. Systematic investigation on corrosion behavior of stainless steels has been done 62 mole% $Li_2CO_3$ and 38 mole% $K_2CO_3$ melt at 923 K by using steady-state polarization method and electrochemical impedance spectroscopy method. It was found that SUS 310L and Al coating specimen may be the best choice among the alloys tested in this study for molten carbonate fuel cell component material.

• Corrosion Science and Technology
• /
• v.11 no.4
• /
• pp.108-111
• /
• 2012

The effects of volume fraction (15-30%) of SiC particulate reinforcements on the corrosion behavior of SiCp/7091 Al composites in the 3.5% NaCl solution were studied by electrochemical techniques and scanning electron microscopy. The results showed that the amount of SiC particulate reinforcements did not cause much difference in the corrosion behavior of SiCp/7091 Al composites but the corrosion rate was proportional to the amount of SiCp reinforcement. And numerous pits and severe dissolution of the matrix was observed probably due to the discontinuities and galvanic effects between Al matrix and SiC reinforcements.

• Transactions of the Korean hydrogen and new energy society
• /
• v.32 no.5
• /
• pp.410-416
• /
• 2021

The initial electrochemical performance of ceramic fuel cell with thin-film electrolyte was evaluated in terms of peak power density ratio, open circuit voltage ratio, and activation/ohmic resistance ratios at 500℃. Hydrogen and air were used as anode fuel and cathode fuel, respectively. The peak power density ratio reduced as ~17% for 40 minutes, which rapidly decreased in the early stage of the performance evaluation but gradually decreased. The open circuit voltage ratio decreased with respect time; however, its time behavior was remarkably different with the reduction behavior of the peak power density ratio. The activation resistance ratio increased as ~15% for 40 minutes, which was almost similar with the time behavior of the peak power density ratio.

• Transactions of the Korean hydrogen and new energy society
• /
• v.32 no.5
• /
• pp.340-346
• /
• 2021

The initial electrochemical performance of ceramic fuel cell with thin-film electrolyte fabricated by plasma-enhanced atomic layer deposition method was evaluated in terms of peak power density ratio, open circuit voltage ratio, and activation/ohmic resistance ratios at 500℃. Hydrogen and air were used as anode fuel and cathode fuel, respectively. The peak power density ratio reduced as ~52% for 30 min, which continually decreased as time increased but degradation rate gradually decreased. The open circuit voltage ratio decreased with respect time; however, its behavior was evidently different from the reduction behavior of the peak power density. The activation resistance ratio increased as ~127% for 30 min, which was almost similar with the reduction behavior of the peak power density ratio.