• Analytical Science and Technology
• /
• v.24 no.2
• /
• pp.113-118
• /
• 2011

When butyl rubber dissolved in toluene was used as a binder of carbon powder, carbon paste showed a mechanical hardness due to the fast volatility of the solvent just after the electrode fabrication. With a view of validating its quantitative electrochemical behaviors, its kinetic parameters, e.g. the symmetry factor, the exchange current density, the capacity of the double layer, the Michaelis constant, the time constant and other factors were investigated. Our experimental facts indicated that butyl rubber is available for a promising binder of carbon powder.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.353-354
• /
• 2006

This work describes the effect of binders, such as carboxymethylcellulose (CMC), CMC+Polytetrafluoroethylene (PTFE) and PTFE, on the electrochemical and mechanical properties of activated carbon-electrode for electric double layer capacitor. The cell capacitors using the electrode bound with binary binder composed of CMC and PTFE, especially m composition CMC ; PTFE = 60 : 40 wt %, has exhibited the better rate capability and the lower internal resistance than those of the cell capacitor with CMC. On the other hand, the sheet type electrode kneaded with PTFE was bonded with conductive adhesive on Al foil. This cell capacitor using the electrode with PTFE exhibited the best mechanical properties and rate capability compared to the CMC and CMC+PTFE one These behaviors could be explained by the well-developed network structure of PTFE fibrils during the kneading process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.12
• /
• pp.1167-1171
• /
• 2006

This work describes the effect of binders, such as carboxymethylcellulose (CMC), CMC+ Polytetrafluoroethylene (PTFE) and PTFE, on the electrochemical and mechanical properties of activated carbon-electrode for electric double layer capacitor. The cell capacitors using the electrode bound with binary binder composed of CMC and PTFE, especially in composition CMC PTFE = 60 : 40 wt.%, has better rate capability and the lower internal resistance than those of the cell capacitor with CMC. On the other hand, the sheet type electrode kneaded with PTFE was bonded with conductive adhesive on Al foil. This cell capacitor using the electrode with PTFE exhibited the best mechanical properties and rate capability compared to the CMC and CMC+PTFE one. These behaviors could be explained by the well-developed network structure of PTFE fibrils doting the kneading process.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.6
• /
• pp.78-88
• /
• 2000

The effect of post-weld heat treatment(PWHT) of SCM440 steel was investigated with parameters such as micro-Vickers hardness, corrosion potential, polarization behaviors, galvanic current, Al anode generating current and Al anode weight loss, etc. Each hardness of three parts(HAZ, BM, WM) by PWHT is lower than each of as-welded parts. However, hardness of WM area was the highest among those three parts in case of both PWHT and as-welded. Corrosion potential of WM part was the highest among those three parts and WM area was also acted as cathode without regard to PWHT. The magnitude of corrosion potential difference among three parts by PWHT was larger than that of three parts of as-welded, and corrosion current by galvanic cell of these three parts by PWHT was also larger compared to as-welded. Therefore, it is suggested that corrosion resistance property of SCM440 steel is decreased by PWHT than as-welded. However, both Al anode generating current and anode weight loss were also increased by PWHT compared to as-welded when SCM400 steel is cathodically protected by Al anode.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.973-978
• /
• 2004

This work describes the effect of conducting materials on the electrochemical performances of electric double layer capacitor. Three kinds of Carbon black, such as Acethylene Black, Super P Black, Ketjen black supplied by Denki Kagaku Kogyo, MMM Carbon, Ketjen Black International Co. respectively, was added in carbon-Polytetrafluoroethylene (PTFE) electrode, which composition is activated carbon : carbon black : PTFE = 80 : 15 : 5 wt.%, and were compared with their electrochemical properties. The electrode with Ketjen Black has showed the lowest resistance than other carbon black, and also exhibited the better rate capability between 0.5 mA/cm$^2$ ∼ 100 mA/cm$^2$ current density in unit cell capacitor. On the other hand, as increasing the composition of Ketjen Black, the specific resistances of electrodes were decreased and Ketjen Black content higher than 15 wt% increased. The best rate capability was obtained at the electrode with 15 wt.% of Ketjen Black in unit cell capacitor. This behaviors would be correlated with the dense structure of electrode.

• Journal of the Korean Electrochemical Society
• /
• v.13 no.3
• /
• pp.163-168
• /
• 2010

Effects of Cetyl Trimethyl Ammonium Bromide (CTAB), which is a kind of cationic surfactants, and Sodium Dodecyl Sulfate (SDS), which is a kind of anionic surfactants on the anodic formation of nanoporous niobium oxide were compared. The addition of SDS could protect the surface from dissolution for long time, leading to the formation of niobium oxide with a double thickness (~400 nm) compared to that prepared without surfactant, whereas dissolution seriously occurred in the solution containing CTAB. The different behaviors were attributed to the interaction between the surfactants with positive (or negative) charge and positively charged niobium oxide.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.343-352
• /
• 2013

Purpose: The purpose of this study was to investigate to effect of the ZrN coated on corrosion resistance and physical property of dental Co-Cr alloys using various instruments. Methods: The specimens were used, respectively, for experiment, Arc Ion plating was carried out for dental casting alloys using ZrN coated materials with nitrogen gas. ZrN coated surface of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), vickers hardness tester, and electrochemical tester. Results: The current density of ZrN coated specimen was smaller than that of non-coated specimen in 0.9% NaCl solution. Pit nucleated at scratch of specimen. The pitting corrosion resistant |$E_{max}-E_{rep}$| increased in order of ZrN coated (110 mV), and non-coated wire (100 mV). Conclusion: The corrosion potential of the ZrN coated specimen was comparatively high. the surface of ZrN coated specimen was more smooth than that of other kinds of non-coated specimen. ZrN coated surface showed higher hardness than that of non-coated surface.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.533-539
• /
• 2002

Porous anodic aluminum oxide layer for nano templates was prepared in acidic solutions. In order to investigate effects of 2nd anodization on ordered formation behaviors of the porous oxide layers, electrochemical and microstructural studies were performed, primarily using TEM, FE- SEM, AFM, and Ultramicrotomy. The pore diameter of the anodic oxide layer increased approximately linearly with increasing voltages, and to the contrary, the pore density decreased. It was shown that 2nd anodizing on the cell base after dissolving 1st anodic oxide layer was remarkably effective for forming ordered array of the pores, comparing with the case for 1st anodization only. And for controlling the diameter of pores, widening method by chemical dissolution seemed more practical than by electrochemical methods.

• Journal of Integrative Natural Science
• /
• v.2 no.4
• /
• pp.233-236
• /
• 2009

This study was undertaken to measure the electrochemical corrosion of amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ (at.%) alloy ribbon under various conditions, including 0.4 mM HCl solution, and for various values of the pH and the immersion time. The corrosion potentials($E_{corr}$) for the amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ alloy in 0.4 mM HCl decreased with increasing temperature; the corrosion current density($I_{corr}$) increased with increasing temperature in general. The polarization resistance($R_p$) was inversely proportional to the corrosion rate. While pH=7, 9, 11 was not as sensitive as pH=3, 5, pH=3 was more sensitive for amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ alloy than other pHs specially. The change of mass in the 70 mM $H_2SO_4$ solution with immersion time was the greatest in the first 100 h.

• The Journal of Natural Sciences
• /
• v.11 no.1
• /
• pp.33-39
• /
• 1999

Electrochemical behaviors of $Sm^3+$-ARS complexes has been investigated by d.c.polarography, differential pulse polarography and cyclic voltammetry. $Sm^3+$forms 1 : 3 adsorptive complexes with ARS.The reduction potential of complex wave $(P_2)$ shifted more negatively than the ligand wave $(P_1)$. The linear calibration curves of decreasing $P_1$ and increasing $P_2$ is obtained when $Sm^3+$ concentration varies from TEX>$2{\times}10^{-6}$ M to $3.2{\times}10^{-5}$ M.