• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.86.2-86.2
• /
• 2015

Cu2ZnSn(S,Se)4 thin film solar cells have been fabricated using sputtered Cu/Sn/Zn metallic precursors on Mo coated sodalime glass substrate without using a toxic H2Se and H2S atmosphere. Cu/Sn/Zn metallic precursors with various thicknesses were prepared using DC magnetron sputtering process at room temperature. As-deposited metallic precursors were sulfo-selenized inside a graphite box containing S and Se pellets using rapid thermal processing furnace at various sulfur to selenium (S/Se) compositional ratio. Thin film solar cells were fabricated after sulfo-selenization process using a 65 nm CdS buffer, a 40 nm intrinsic ZnO, a 400 nm Al doped ZnO, and Al/Ni top metal contact. Effects of sulfur to selenium (S/Se) compositional ratio on the microstructure, crystallinity, electrical properties, and cell efficiencies have been studied using X-ray diffraction, Raman spectroscopy, field emission scanning electron microscope, I-V measurement system, solar simulator, quantum efficiency measurement system, and time resolved photoluminescence spectrometer. Our fabricated Cu2ZnSn(S,Se)4 thin film solar cell shows the best conversion efficiency of 9.24 % (Voc : 454.6 mV, Jsc : 32.14 mA/cm2, FF : 63.29 %, and active area : 0.433 cm2), which is the highest efficiency among Cu2ZnSn(S,Se)4 thin film solar cells prepared using sputter deposited metallic precursors and without using a toxic H2Se gas. Details about other experimental results will be discussed during the presentation.

• Journal of Biomedical Engineering Research
• /
• v.28 no.2
• /
• pp.310-315
• /
• 2007

The axial-flow type blood pump(XVAD) which has been developed in our group consists of mechanical parts (an impeller, a diffuser and a flow straightener) and electrical parts (a motor and a magnetic bearing). The magnetic bearing system fully levitates the impeller to remove mechanical coupling with other parts of the pump with constant gap, which needs non-contact type gap sensing. Conventional gap sensors are too large to be adopted to the implantable axial -flow type blood pump. Thus, in this paper, the compact eddy current type gap sensor system proper for the implantable axial-flow type blood pump was developed and its performance was evaluated in vitro. The developed eddy current type gap sensor system is a transformer type and has a differential probe. Sensor coil(probe) has small dimensions(6 mm diameter, 2 mm thickness) and its optimal inductance was determined as 0.068 mH for the measurement range of $0\sim3mm$. It could be manufactured with 130 turns of the 0.04 mm diameter copper coil. The characteristics of the developed eddy current type gap sensor system was evaluated by in vitro experiment. At experiment, it showed satis(actory performance to apply to the magnetic bearing system of the XVAD. It could measure the gap up to 3mm, but the linearity was decreased at the range of $1.8\sim3.0mm$. Moreover, it showed no difference in different media such as the water and the blood at the temperature range of $35\sim40^{\circ}C$.

• Maxillofacial Plastic and Reconstructive Surgery
• /
• v.18 no.3
• /
• pp.358-365
• /
• 1996

Deep burns of the face & lips often lead to scarring and contraction of the circum-oral tissues with a marked reduction in the size of the oral aperture. Such burns most commonly caused by electrical contact, for example, children sucking electric plugs, or as a result of chemical burns and the exposture to flame. Once having burns, burned tissue may contract and reduce considerably the size and mobility of the mouth ; therefore bring up the resultant functional disturbance, verbal difficulty, even digestive difficulty, and poor appearance, which fall into difficulty in social acceptability, caused by burns. In our department, 2 patients who were complain of functional limitations and esthetic problem owing to scar contracture, were visited, and we treated this microstomia with scar excision, graft and flap technique, and postoperative intensive physical therapy. We obtained relatively favorable results, thus report this cases with literature review.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.38 no.7
• /
• pp.601-605
• /
• 2014

Porous conductors are known to demonstrate excellent electrical, mechanical, and chemical resistance. These porous conductors demonstrated potential applications in various fields such as electrodes for supercapacitors, flexible heaters, catalytic electrodes, and sorbents. In this study, we described a pressure sensitive device using conductive and porous sponges. With an extremely simple "dipping and drying" process using a single-walled carbon nanotube (SWCNT) solution, we produced conductive sponges with sheet resistance of < $30k{\Omega}/sq$. These carbon nanotube sponges can be deformed into any shape elastically and repeatedly compressed to large strains without collapse. The pressure sensors developed from these sponges demonstrated high resistance change under pressure of up to a half of their initial resistance.

• Journal of Sensor Science and Technology
• /
• v.23 no.4
• /
• pp.266-271
• /
• 2014

Chemical sensors are used in various industrial facilities such high-risk and prevent the leakage of substances, important in life and environmental protection and the safe use of industry, used for management. In particular, high-temperature environments such as power generation equipment of the rotating part due to leakage generated by the various oil, power plants Shut Down, fire, work environment (exposure to various chemical solution and gas leak) and various water, air and soil pollution causes. Thus, over the long term through various channels such as crops and groundwater contamination caused by the slow, serious adverse effect on the ecosystem. In this paper, synthetic lube oil and high pressure hydraulic fluid leakage and immediately detect a new Printed Electronic implementation of technology-based film-type sensors, and its performance test. Thus, industrial accidents and environmental pollution and for early detection of problems, large accidents can be prevented. Experimental results of the synthetic lube oil and high pressure hydraulic fluid solution after the contact time depending on the experiment and the oil solution of the sensor material of the conductive porous PE resistance value by a chemical reaction could be confirmed that rapid increase. Also implemented in the film-type oil sensor electrical resistance change over time of the reaction rate and the synthetic lube oil is about 2 minutes or less, the high pressure hydraulic fluid is less than about 1 minute was. Therefore, more high-pressure hydraulic fluid such as a low volatility synthetic lube oils are the resistance change and the reaction rate was confirmed to be the slowest.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.12C no.4
• /
• pp.220-224
• /
• 2002

The electromagnetic properties and thermal behavior of Mn-Zn ferrite cores for the blocking filter of PLC application were investigated as the function of additives. The highest density and permeability were 4.98 g/㎤ and 8,221, respectively and were obtained to the specimen with composition of MnO 24 mol%, ZnO 25 mol% and Fe$_2$O$_3$51 mol%, added MoO$_3$ of 400 ppm, SiO$_2$ of 100 ppm, and CaO of 200 ppm. The uniform grains were organized, and the microstructures were compacted due to reduction of pores in the specimen. The permeability was increased up to 13,904 as the temperature of specimen increased to 110。C. However, it was decreased precipitously under 100 over 110。C. The exothermic behavior was observed in the frequency range from 1 kHz to 1 MHz, and the maximum temperature of specimen was 102。C at 1 MHz. In the consequence, the Mn-Zn ferrite core developed in this research will maintain the stable electromagnetic properties since the temperature of ferrite core rose to 93 。C in the range of 100 kHz to 450 kHz bandwidth qualified for PLC. The blocking filters were designed for single phase and three phases using the in-line and non-contact core. The best attenuation ratios of -46.46 dB and -73.9 dB were measured in the range of 100 kHz to 450 kHz bandwidth, respectively.

• Journal of Biosystems Engineering
• /
• v.41 no.2
• /
• pp.138-144
• /
• 2016

Purpose: Phosphorus is an essential element for water quality control. Excessive amounts of phosphorus causes algal bloom in water, which leads to eutrophication and a decline in water quality. It is necessary to maintain the optimum amount of phosphorus present. During the last decades, various studies have been conducted to determine phosphorus content in water. In this study, we present a comprehensive overview of colorimetric, electrochemical, fluorescence, microfluidic, and remote sensing technologies for the measurement of phosphorus in water, along with their working principles and limitations. Results: The colorimetric techniques determine the concentration of phosphorus through the use of color-generating reagents. This is specific to a single chemical species and inexpensive to use. The electrochemical techniques operate by using a reaction of the analyte of interest to generate an electrical signal that is proportional to the sample analyte concentration. They show a good linear output, good repeatability, and a high detection capacity. The fluorescence technique is a kind of spectroscopic analysis method. The particles in the sample are excited by irradiation at a specific wavelength, emitting radiation of a different wavelength. It is possible to use this for quantitative and qualitative analysis of the target analyte. The microfluidic techniques incorporate several features to control chemical reactions in a micro device of low sample volume and reagent consumption. They are cheap and rapid methods for the detection of phosphorus in water. The remote sensing technique analyzes the sample for the target analyte using an optical technique, but without direct contact. It can cover a wider area than the other techniques mentioned in this review. Conclusion: It is concluded that the sensing technologies reviewed in this study are promising for rapid detection of phosphorus in water. The measurement range and sensitivity of the sensors have been greatly improved recently.

• Journal of Biomedical Engineering Research
• /
• v.30 no.2
• /
• pp.179-184
• /
• 2009

Magnetic Resonance Electrical Impedance Tomography (MREIT) is a new bio-imaging modality providing cross-sectional conductivity images from measurements of internal magnetic flux densities produced by externally injected currents. Recent MREIT studies demonstrated successful conductivity image reconstructions of postmortem and in vivo canine brain. However, the whole head imaging was not achieved due to technical issues related with electrodes and noise in measured magnetic flux density data. In this study, we used a new carbon-hydrogel electrode with a large contact area and injected 30 mA imaging current through a canine head. Using a 3T MREIT system, we performed a postmortem canine experiment and produced high-resolution conductivity images of the entire canine head. Collecting magnetic flux density data inside the head subject to multiple injection currents, we reconstructed cross-sectional conductivity images using the harmonic $B_z$ algorithm. The conductivity images of the canine head show a good contrast not only inside the brain region including white and gray matter but also outside the brain region including the skull, temporalis muscle, mandible, lingualis proprius muscle, and masseter muscle.

• Journal of Satellite, Information and Communications
• /
• v.10 no.3
• /
• pp.6-10
• /
• 2015

RF energy harvesting technology is a promising technology for generating the electrical power from ambient RF signal to operate low-power consumption devices(eg. sensor) in wireless communication networks. This paper, motivated by this and building upon existing CR(Cognitive Radio) network model, proposes a optimal control policy for RF energy harvesting CR networks model where secondary users that have low power consumption harvest ambient RF energy from transmission by nearby active primary users, while periodically sensing and opportunistically accessing the licensed spectrum to the primary user's network. We consider that primary users and secondary users are distributed as Poisson point processes and contact with their intended receivers at fixed distances. Finally we can derive the optimal frame duration, transmission power and density of secondary user from the proposed model that can maximize the secondary users's throughput under the given several conditions and suggest future directions of research.

• Environmental Engineering Research
• /
• v.15 no.2
• /
• pp.71-78
• /
• 2010

To understand the effects of acclimation schemes on the formation of anode biofilms, different electrical performances are characterized in this study, with the roles of suspended and attached bacteria in single-chamber microbial fuel cells (MFCs). The results show that the generation of current in single-chamber MFCs is significantly affected by the development of a biofilm matrix on the anode surface containing abundant immobilized microorganisms. The long-term operation with suspended microorganisms was demonstrated to form a dense biofilm matrix that was able to reduce the activation loss in MFCs. Also, a Pt-coated anode was not favorable for the initial or long-term bacterial attachment due to its high hydrophobicity (contact angle = $124^{\circ}$), which promotes easy detachment of the biofilm from the anode surface. Maximum power ($655.0\;mW/m^2$) was obtained at a current density of $3,358.8\;mA/m^2$ in the MFCs with longer acclimation periods. It was found that a dense biofilm was able to enhance the charge transfer rates due to the complex development of a biofilm matrix anchoring the electrochemically active microorganisms together on the anode surface. Among the major components of the extracellular polymeric substance, carbohydrates ($85.7\;mg/m^2_{anode}$) and proteins ($81.0\;mg/m^2_{anode}$) in the dense anode biofilm accounted for 17 and 19%, respectively, which are greater than those in the sparse anode biofilm.