• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.243-249
• /
• 2006

Porous polymer gel electrolytes (PGEs) based on poly(vinylidenefluoride-co-hexafluoropropylene) (P(VdF-co-HFP)) as a polymer matrix and polyvinylpyrolidone (PVP) as a pore-forming agent were prepared and electrochemical properties were investigated for an electric double layer capacitor (EDLC) in order to increase a permeability of an electrolyte into the PGE. Propylene carbonate (PC) and ethylene carbonate (EC) as plasticizers, and tetraethylammonium tetrafluoroborate ($TEABF_4$) as a supporting salt for the PGE were used. EDLC unit cells were assembled with the PGE and electrode comprising BP-20 and MSP-20 as activated carbon powders, Super P as a conducting agent, and P(VdF-co-HFP)/PVP as a mixed binder. Ion conductivity of PGEs increased with an increased PVP content and was the best at 7 wt% PVP, whereas electrochemical characteristics such as AC-ESR of unit cell were better in 3 wt%. And electrochemical characteristics of the unit cell with PGE were the best at a 33 : 33 weight ratio of PC to EC. Specific capacitance of a mixed plasticizer system of PE and EC was higher than that of pure PC. Ion conductivity of PGEs with a film thickness of $20{\mu}m$ was higher, but electrochemical characteristics of unit cells were higher for a $50{\mu}m$ membrane thickness. Also, the unit cell has shown the highest capacitance of 31.41 F/g and more stable electrochemical performance when PGE and electrode were hot pressed. Consequently, the optimum composition ratio of PGE for EDLCs was 23 : 66 : 11 wt% such as P(VdF-co-HFP) : PVP = 20 : 3 wt% and PC : EC = 44 : 22 wt%. In this case, $3.17{\times}10^{-3}S/cm$ of ion conductivity was achieved at the $50{\mu}m$ thickness of PGE for EDLCs. And the electrochemical characteristics of unit cells were $2.69{\Omega}$ of DC-ESR, 28 F/g of specific capacitance, and 100% of coulombic efficiency.

• Journal of Sericultural and Entomological Science
• /
• v.16 no.1
• /
• pp.21-48
• /
• 1974

The studies were carried out to disclose the physical and chemical properties of sericin fraction obtained from silk cocoon shells and its characteristics of swelling and solubility. The following results were obtained. 1. The physical and chemical properties of sericin fraction. 1) In contrast to the easy water soluble sericin, the hard soluble sericin contains fewer amino acids include of polar side radical while the hard soluble amino acid sach as alanine and leucine were detected. 2) The easy soluble amino acids were found mainly on the outer part of the fibroin, but the hard soluble amino acids were located in the near parts to the fibroin. 3) The swelling and solubility of the sericin could be hardly assayed by the analysis of the amino acid composition, and could be considered to tee closely related to the compound of the sericin crystal and secondary structure. 4) The X-ray patterns of the cocoon filament were ring shape, but they disappeared by the degumming treatment. 5) The sericin of tussah silkworm (A. pernyi), showed stronger circular patterns in the meridian than the regular silkworm (Bombyx mori). 6) There was no pattern difference between Fraction A and B. 7) X-ray diffraction patterns of the Sericin 1, ll and 111 were similar except interference of 8.85A (side chain spacing). 8) The amino acids above 150 in molecular weight such as Cys. Tyr. Phe. His. and Arg. were not found quantitatively by the 60 minutes-hydrolysis (6N-HCI). 9) The X-ray Pattern of 4.6A had a tendency to disappear with hot-water, ether, and alcohol treatment. 10) The partial hydrolysis of sericin showed a cirucular interference (2A) on the meridian. 11) The sericin pellet after hydrolysis was considered to be peptides composed with specific amino acids. 12) The decomposing temperature of Sericin 111 was higher than that of Sericin I and II. 13) Thermogram of the inner portioned sericin of the cocoon shell had double endothermic peaks at 165$^{\circ}C$, and 245$^{\circ}C$, and its decomposing temperature was higher than that of other portioned sericin. 14) The infrared spectroscopic properties among sericin I, II, III and sericin extracted from each layer portion of the cocoon shell were similar. II. The characteristics of seriein swelling and solubility related with silk processing. 1) Fifteen minutes was required to dehydrate the free moisture of cocoon shells with centrifugal force controlled at 13${\times}$10$^4$ dyne/g at 3,000 R.P.M. B) It took 30 minutes for the sericin to show positive reaction with the Folin-Ciocaltue reagent at room temperature. 3) The measurable wave length of the visible radiation was 500-750m${\mu}$, and the highest absorbance was observed at the wave length of 650m${\mu}$. 4) The colorimetric analysis should be conducted at 650mu for low concentration (10$\mu\textrm{g}$/$m\ell$), and at 500m${\mu}$ for the higher concentration to obtain an exact analysis. 5) The absorbing curves of sericin and egg albumin at different wave lengths were similar, but the absorbance of the former was slightly higher than that of the latter. 6) The quantity of the sericin measured by the colorimetric analysis, turned out to be less than by the Kjeldahl method. 7) Both temperature and duration in the cocoon cooking process has much effect on the swelling and solubility of the cocoon shells, but the temperature was more influential than the duration of the treatment. 8) The factorial relation between the temperature and the duration of treatment of the cocoon cooking to check for siricin swelling and solubility showed that the treatment duration should be gradually increased to reach optimum swelling and solubility of sericin with low temperature(70$^{\circ}C$) . High temperature, however, showed more sharp increase. 9) The more increased temperature in the drying of fresh cocoons, the less the sericin swelling and solubility were obtained. 10) In a specific cooking duration, the heavier the cocoon shell is, the less the swelling and solubility were obtained. 11) It was considered that there are differences in swelling or solubility between the filaments of each cocoon layer. 12) Sericin swelling or solubility in the cocoon filament was decreased by the wax extraction.. 13) The ionic surface active agent accelerated the swelling and solubility of the sericin at the range of pH 6-7. 14) In the same conditions as above, the cation agent was absorbed into the sericin. 15) In case of the increase of Ca ang Mg in the reeling water, its pH value drifted toward the acidity. 16) A buffering action was observed between the sericin and the water hardness constituents in the reeling water. 17) The effect of calcium on the swelling and solubility of the sericin was more moderate than that of magnecium. 18) The solute of the water hardness constituents increased the electric conductivity in the reeling water.