• Transactions of the Korean Society of Mechanical Engineers
• /
• v.6 no.3
• /
• pp.232-238
• /
• 1982

The behavior of corner crack propagation by unidirectional plane bending fatigue was investigated in the butt welded joints of SS41 and SM50 steel plates including an edge through-thickness notch. The properties of fatigue crack propagation were inspected in the weld metal, heat-affected zone, and base metal of the welded joints. Main results obtained are as follows; (1) When a plate with an edge through-thickness notch is loaded by plane bending fatigue in indirection, the 2 variant corner cracks on the upper and lower edge of the plate are initiated and propagated respectively from the notch. (2) In case of a specimen containing a corner crack, it is more reasonable to estimate the crack propagation rate by area of fracture surface than by crack surface length. (3) The rate of fatigue crack propagation becomes faster in the following order; weld metal, heat-affected zone, and base metal. (4) The specimen including reinforcement shape is rapidly failed throughout bond due to effect of its shape when the repeated load exceeds a certain cycle.

• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.36-43
• /
• 1999

The effect of microstructure on the fracture toughness of multi pass weld metal has been investigated. The micromechanisms of fracture process are identified by in-situ scanning electron microscopy(SEM) fracture observation using single edge notched specimen. The notches of the in-situ fracture specimens were carefully located such that the ends of the notches were in the as-deposited top bead and the reheated weld metal respectively. The observation of in-situ fracture process for as-deposited top bead indicated that as strains are applied, microcracks are formed at the interfaces between soft proeutectoid ferrite and acicular ferrite under relatively low stress intensity factor. Then, the microcracks propagate easily along the proeutectoid ferrite phase, leading to final fracture. These findings suggest that proeutectoid ferrite plays an important role in reducing the toughness of the weld metal. On the other hand, reheated regions showed that the microcrack initiated at the notch tip grows along the localized shear bands under relatively high stress intensity factor, confirming that reheated area showing momogeneous and fine microstructure would be beneficial to the fracture resistance of weld metal.

• International Journal of Korean Welding Society
• /
• v.1 no.2
• /
• pp.23-29
• /
• 2001

In this study, a preview-sensing visual sensor system is constructed far weld seam tracking in GMA welding. The visual sensor system consists of a CCD camera, a diode laser system with a cylindrical lens, and a band-pass-filter to overcome the degrading of image due to spatters and/or arc light. Among the image processing methods, Hough transform method is compared with the central difference method from a viewpoint of the capability for extracting the accurate feature position. As a result, it was revealed that Hough transform method can more accurately extract the feature positions and it can be applied to real time weld seam tracking. Image processing which includes Hough transform method is carried out to extract straight lines that express laser stripe. After extracting the lines, weld joint position and edge points are determined by intersecting the lines. Even though the image includes a spatter trace on it, it is possible to recognize the position of weld joint. Weld seam tracking was precisely implemented with adopting Hough transform method, and it is possible to track the weld seam in the case of offset angle is in the region of $\pm$ $15^{\circ}$.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.10a
• /
• pp.668-671
• /
• 1995

In this study, the fatigue charateristics of weld specimen was studied experimentally by using the various specimen types. The specimen type were tensile shesr(TS) specimen, cross tension(CT) specimen, and T typr (TT) specimen. Tensile test and fatigue test were carried out and microstucture was investigated. Finite element method was used to investigate stress distribution near nugget edge. Finally fracture mechanics approach was tried to the various specimen types.

• Proceedings of the KWS Conference
• /
• 2002.05a
• /
• pp.62-64
• /
• 2002

• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.66-75
• /
• 1999

Weld bead quality in tailored blank(TB) is critically affected by edge preparation of sheets. The edge quality of prepared sheets for TB can be classified into straightness and the cross section quality of sheared plane such as a ratio of shear face, shear plane angle, etc. In order to have a good edg quality for butt-welding sheets, precision shearing will be recommended. In this paper, the feasibility of a conventional mechanical shearing as the edge preparation for tailored blanks is studyied. It reveals that fine shearing may not be the unique solution as it is generally accepted. To obtain the good shearing condition with a conventional mechanical shearing, experiments were carried out using Tahuchi method. The major parameters affecting a sheared contour are the clearance between upper blade and lower blade, and shear angle. The optimal shearing condition yields a very good straightness along the entire length of the cut, which gives a butt joint gap less than 10% of the base material thickness. The good cross section of sheared plane is also achieved in the optimal shearing condition such as a ratio of the shear face above 65%, a cross section's shear plane angle above 85%, little burr, which is providing finally good weld beads.

• Journal of the Institute of Electronics Engineers of Korea SP
• /
• v.45 no.5
• /
• pp.103-110
• /
• 2008

A reliable extraction of welded area is the precedent task before the detection of weld defects in industrial radiography. This paper describes an attempt to detect and extract the welded features of steel tubes from the computed radiography(CR) images. The statistical properties are first analyzed on over 160 sample radiographic images which represent either weld or non-weld area to identify the differences between them. The analysis is then proceeded by pattern classification to determine the clustering parameters. These parameters are the width, the functional match, and continuity. The observed weld image is processed line by line to calculate these parameters for each flexible moving window in line image pixel set. The local statistic line-clustering method is used as the classifier to recognize each window data as weld or non-weld cluster. The sequential procedure is to track the edge lines between two distinct regions by iterative calculation of threshold, and it results in extracting the weld feature. Our methodology is concluded to be effective after experiment with CR weld images.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.102-104
• /
• 2003

Laser weldability of aluminized steels of 0.8mm thick has been investigated. Test materials were cut from the commercial steels that were produced at the Coating Mill of POCOS. Test coupons for welding were prepared by using a conventional shearing machine and no additional edge treatment was peformed. Nd:YAG laser welding system was mainly applied to make weld specimens. Test results revealed that almost no spattering was observed even though the welding was peformed with no overlap joint clearance. Bead quality of aluminized steel laser weld was smooth and stable. According to x-ray inspection results, it was proved that the laser welds of aluminized steels were metallurgically defect free.

• Journal of Korean Institute of Industrial Engineers
• /
• v.18 no.2
• /
• pp.83-97
• /
• 1992

A new approach, to seam tracking for robotic are welding is proposed. In this approach, the weld model is a snapshot image and the acquired image is analyzed and compared to the welding database which contains CAD data, weld positions, weld parameters, etc. This paper presents a fast and robust algorithm for the Hough Transform. This modified Hough Transform(MHT) algorithm uses the least-squares regression analysis method in order to approximate the edge lines more precisely, and leads to a significant reduction in both computation and storage. In comparison with the conventional seam tracking methods, this new approach has the advantages of low cost, continuous welding, and various type welding.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.6 no.5
• /
• pp.20-27
• /
• 1998

According as the member of the automobile body structure have been thinned their thickness and have become high strength, each part of the body structure has been put more severe stress condition. And, because fatigue strength of the spot welded lap joint is influenced by its geometrical and mechanical factors, welding condition and etc., there needs a quantitative and systematic evaluation method for them. In this study, by considering nugget edge of the spot weld part of the IB-type spot welded lap joint under tension-shear load to the ligament crack. fatigue strength of various IB-type spot welded lap joints was estimated with the stress intensity factor(S.I.F.) KIII which is fracture mechanical parameter. We could find that fatigue strength evaluation of the IB-type spot welded lap joints by KIII is more effective than the maximum principal stress ($\sigma$1max) at edge of the spot weld obtained from FEM analysis.