• Journal of The Korean Society of Agricultural Engineers
• /
• v.49 no.1
• /
• pp.45-54
• /
• 2007

This study was performed to evaluate strength and watertightness properties of EVA modified high strength concrete in order to improve durability of concrete used in agricultural water utilization facilities that are in constant contact with water. Materials used were cement, coarse and fine aggregates, silica fume, EVA and AE water reducing agent. Tests for the slump, compressive and flexural strengths, absorption ratio and permeability coefficient according to curing condition (water and water+dry curing) and content ratio of EVA were performed. The slump results of EVA modified high strength concrete similarly showed in the content ratio of EVA powder less than 4% and decreased in the content ratio of EVA powder more than 6% compared to that of concrete without EVA powder. The compressive strength of EVA modified high strength concrete decreased with increasing the content ratio of EVA powder. The flexural strength of EVA modified high strength concrete increased with increasing the content ratio of EVA powder in the content ratio of EVA powder ratio less than 4% and had similar or slightly decreased in the content ratio of EVA powder more than 6% compared to that of concrete without EVA powder. The absorption ratio and permeability coefficient of EVA modified high strength concrete decreased with increasing the content ratio of EVA powder in the content ratio of EVA powder less than 4% and slightly increased in the content ratio of EVA powder more than 6%.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2005.10a
• /
• pp.123-127
• /
• 2005

EVA Powder modified high strength concretes were prepared by varying polymer/binder mass ratio with a constant water/binder mass ratio of 0.3. The effect of EVA powder on the slump, hydration heat, compressive and flexural strength, toughness and water absorption ratio was studied. In hydration heat test, temperature of hydration reaction displayed almost fixed level regardless of containing rate of EVA powder, but peak time of hydration reaction displayed late inclination as containing rate of powder increases. With the same water/binder mass ratio, the compressive strength and water absorption of EVA powder modified concretes decreased slightly when EVA powder was added and the flexural strength of EVA powder modified concretes rised slightly when EVA powder was added. Also, the toughness of the modified concretes can be improved markedly. The interpenetrating structure between the polymeric phase and cement hydrates formed at a $2{\sim}6%$(containing rate of EVA powder). The properties of the polymer modified concretes were influenced by the polymer film, cement hydrates and the combined structure between the organic and inorganic phases.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2005.10a
• /
• pp.97-101
• /
• 2005

High strength concretes utilizing EVA with micro particles were prepared by varying polymer/binder mass ratio and curing conditions with a constant water/binder mass ratio of 0.3. The EVA modified concretes on the compressive and flexural strength, microstructure, ultrapulse modulus in curing condition(dry and water curing) were studied. Also, scanning electron microscope analysis(SEM) was performed to reveal the presence of polymer film and cement hydrates in the concrete. The compressive strength of the EVA modified concretes cured at water conditions ere higher than that of the EVA modified concretes cured at dry conditions. But, the flexural strength of the specimens cured at dry conditions were higher than that of the specimens cured at water conditions. Due to the interaction of the cement hydrates and polymer film, an interpenetrating network originated in which the aggregates were embedded. The curing of the polymer modified concrete involves two step of cement hydrates and polymer modification, and cement hydrates was promoted in water conditions and polymer film formation take place when water evaporates and was thereby was favored in dry conditions. By SEM analysis, influences of polymer modification was strengthening of the transition zone between the aggregate and the paste, and the porosity of transition zone decreases. By spring analysis, it could known that polymer film affects in porosity decrease and strengthening of transition zone.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.5
• /
• pp.85-91
• /
• 2008

Prepacked concrete has recently been used in the special constructions fields such as underwater concrete work, heavy-weight concrete work, underground structure work, partial repair works for damaged reinforced concrete structures. and polymer-modified mortars have been employed as grouting mortars for the prepacked concrete. The purpose of this study is to recommend the optimum mix design of polymer-modified grouting mortars for prepacked concrete. Polymer-modified mortars using SBR and EVA emulsions as admixture of grouting mortars for prepacked concrete are prepared with various mix proportions such as sand-binder ratio, fly ash replacement ratio, polymer-binder ratio. and tested for flowability, viscosity of grouting mortars, bleeding ratio, expansion ratio, flexural and compressive strengths of grouting mortars and compressive and tensile strengths of prepacked concretes. From the test results, it is apparent that polymer-modified mortars can be produced as grouting mortars when proper mix design is chosen. We can design the mix proportions of high strength mortars for prepacked concrete according to the control of mix design factors such as type of polymer, polymer-binder ratio, sand-binder ratio and fly ash replacement ratio. Water-binder ratio of plain mortars for a constant flowability value are in the ranges of 43% to 50%. SBR-modified mortar has a little water-binder ratios compared to those of plain mortar, however, EVA-modified mortar needs a high water-binder ratio due to a high viscosity of polymer dispersion. The expansion and bleeding ratios of grouting mortars are also controlled in the proper value ranges. Polymer-modified grouting mortars have good flexural. compressive and tensile strengths, are not affected with various properties with increasing fly ash replacement to cement and binder-sand ratio. In this study, SBR-modified grouting mortar with a polymer-binder ratio of 10% or less, a fly ash replacement of 10% to cement and a sand-binder ratio of 1.5 is recommended as a grouting mortar for prepacked concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.5
• /
• pp.71-77
• /
• 2009

In a range of forms, such as latex, water-soluble polymer, liquid resin, and monomer, polymer dispersions have been widely used in the construction industry as cement modifiers because of their excellent properties, such as acid-resistance, water-proofness, and good ductility in mortar and concrete. Polymer cement slurry (polymer-modified slurry) is made of cement and polymer dispersions, with a high polymer-cement ratio of 50% or more. The purpose of this study is to evaluate the water permeability and drying shrinkage of polymer cement mortar (polymer-modified mortar) and cement concrete coated by polymer cement slurry. The polymer cement mortar and cement concrete are prepared with various polymer types, polymer-cement ratios and curing methods, and are tested for water permeability, drying shrinkage and strength. The test results showed thatthe weight of permeable water of polymer cement mortar decreases with an increase in the polymer-cement ratio, reaching a minimum at the polymer-cement ratio of 20%. In particular, the weight of permeable water of St/BA-modified mortar with a polymer-cement ratio of 20% coated with St/BA-modified slurry is about 1/55 that of unmodified mortar. The EVA- and St/BA-modified slurries coated on cement concrete have about 4 or 5 times higher drying shrinkage compared to cement concrete. The strength of polymer cement mortars tends to increase with a higher polymer-cement ratio, and is considerably higher than that of unmodified mortar. It is thus concluded that polymer cement mortars coated by polymer cement slurry are effective for industrial application, and have superior properties such as waterproofness and strengths, compared with conventional cement mortar.