• Journal of the Korean Ceramic Society
• /
• v.35 no.3
• /
• pp.219-230
• /
• 1998

Various interlayer materials have been tested for active metal(Cusil ABA) brazing of Si3N4/S. S316 joint. In general multilayer joint had higher strength(80-150 MPa) and better reliability than monolayered one. The joint with Cu(0.2)/Mo(0.3)/Cu(0.2mm) interlayer showed the highest bending strength of abou 490 MPa and the joint with Cu(0.2)/Mo(0.3mm) interlayer the best reliability (14.6 Weibull modulus). The stresses distributed in joint materials during 4-point bending test were estimated by CAE von Mises analysis; the estimated stresses were In good agreement with the measured data. In multilayer joint Cu was though to reduce the residual stresses induced by the difference in thermal expansion coefficient between the ceramic Mo and metal It apperared that a Cu/Mo was optimum interlayer material for Si3N4/S. S316 joint with high bending strength (420 MPa) and reliability. In addition the various shapes and types of compound were examined by EPMA in joining interface.

• The Journal of the Korea Contents Association
• /
• v.13 no.12
• /
• pp.893-899
• /
• 2013

This study was to determine the efficacy in the remineralization on premary teeth following the application of toothpaste with and without sodium fluoride. All tooth were checked using microhardness tester and the calcium (Ca) and phosphorous (P) concentration by electron probe microanalyzer (EPMA) analysis for the 4 weeks. The collected data was analysed using the statistical software program SPSS, 20.0. The applied enamel of premary teeth with 0.243% fluoridated toothpaste resulted in significant differences in the microhardness values (p>0.05). The Ca and P concentrations of applied premary teeth with fluoridated toothpaste were also significant difference in norm wt% (p>0.05). As a results, a increasing the surface microhardness of the premary teeth and providing a remineralizing effect by increased Ca and P concentrations.

• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.15-20
• /
• 2016

Niobium is one of the most important and rarest metals, and is used in the electronic and energy industries. However, it's extremely high melting point and oxygen affinity limits the manufacture of Nb coating materials. Here, a Nb coating material is manufactured using a kinetic spray process followed by hot isotactic pressing to improve its properties. OM (optical microscope), XRD (X-ray diffraction), SEM (scanning electron microscopy), and Vickers hardness and EPMA (electron probe micro analyzer) tests are employed to investigate the macroscopic properties of the manufactured Nb materials. The powder used to manufacture the material has angular-shaped particles with an average particle size of $23.8{\mu}m$. The porosity and hardness of the manufactured Nb material are 0.18% and 221 Hv, respectively. Additional HIP is applied to the manufactured Nb material for 4 h under an Ar atmosphere after which the porosity decreases to 0.08% and the hardness increases to 253 Hv. Phase analysis after the HIP shows the presence of only pure Nb. The study also discusses the possibility of using the manufactured Nb material as a sputtering target.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.534-538
• /
• 2002

Dissimilar friction stir welding of aluminum (AI) alloy 1050 and magnesium (Mg) alloy AZ31 was successfully done in the limited welding parameters. The dissimilar weld showed good quality and facility compared to conventional fusion weld. Transverse cross section perpendicular to the welding direction had no defects. The weld was divided into base material of Al alloy, an irregular shaped stir zone and base material of Mg alloy. The irregular shaped stir zone was roughly located around the initial weld center. The weld interface near plate surface shifted from initial weld centerline to the advancing side. Hardness profile of the weld was heterogeneous, and the hardness value of the stir zone was raised to about 150 Hv to 250 Hv. The mixed phase was identified to intermetallic compound $Mg_{17}$Al$_{12}$ using x-ray diffraction method, energy dispersive x-ray spectroscopy (EDX) and electron probe micro analysis (EPMA). The formation of intermetallic compound $Mg_{17}$Al$_{12}$ during FSW causes the remarkable increase in hardness value in the stir zone.one.

• Journal of Welding and Joining
• /
• v.33 no.3
• /
• pp.47-53
• /
• 2015

By the trends of electronic package to be more integrative, the fine Cu trace pitch of organic PCB is required to be a robust design. In this study, the short circuit failure mechanism of PCB with a Cl element under the Temperature humidity bias test ($85^{\circ}C$/85%RH/3.5V) was examined by micro-structural study. A focused ion beam (FIB) and an electron probe micro analysis (EPMA) were used to polish the cross sections to reveal details of the microstructure of the failure mode. It is found that $CuCl_x$ were formed and grown on Cu trace during the $170^{\circ}C$/3hrs and that $CuCl_x$ was decomposed into Cu dendrite and $Cl_2$ gas during the $85^{\circ}C$/85%RH/3.5V. It is suggested that Cu dendrites formed on Cu trace lead to a short circuit failure between a pair of Cu traces.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.1
• /
• pp.6-9
• /
• 2006

The effect of $ZrO_2$-coating on the electrochemical properties of the cathode material $LiNi_{0.8}Co_{0.2}O_2$ was investigated using EPMA, TEM, and EIS. In particular, we facused on the distribution of the $ZrO_2$ on the particle surface to study the relation between electrochemical properties of the coated cathode and the distribution of the coating materials in the particle. Based on the results from the composition analysis and electrochemical tests, it was found that the coating layer consisted of nano-sized $ZrO_2$ particles attached non-uniformly on the particle surface and the $ZrO_2$ layer significantly improved the electrochemical properties of the cathode by suppressing the impedance growth at the interface between the electrodes and the electrolyte.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.375-378
• /
• 2002

We investigated the reduction of etching damage by additive O$_2$ in etching gas and recovery of etching damage by O$_2$ annealing. The PZT thin films were etched using additive Ar or O$_2$ into Cl$_2$/CF$_4$ gas mixing ratio of 8/2. In order to recover ferroelectric properties of PZT thin films after etching, the etched PZT thin films were annealed at 600 C in O$_2$ atmosphere for 10 min. The remanent polarization is decreased seriously and fatigue is accelerated in the PZT sample etched in Ar/(C1$_2$+CF$_4$) plasma, whereas these characteristics are improved in O$_2$/(Cl$_2$/CF$_4$). From x-ray photoelectron spectroscopy (XPS) analysis, the intensities of Pb-O, Zr-O and Ti-O peaks are changed and the etch byproducts such as metal chloride and metal fluoride are reduced by O$_2$ annealing. From electron probe micro analyzer (EPMA) and auger electron spectroscopy(AES), O$_2$ vacancy is observed after etching. In x-ray diffraction (XRD), the structure damage in the additive O$_2$ into C1$_2$/CF$_4$ is reduced and the improvement of ferroelectric behavioral annealed sample is consistent with the increase of the (100) and (200) PZT peaks.

• Carbon letters
• /
• v.3 no.4
• /
• pp.198-204
• /
• 2002

In this paper, impregnated activated carbon fiber (IACF) was manufactured to pitch-based activated carbon fibers (ACF) with potassium hydroxide (KOH) by using wet impregnation method to raise nitrogen oxides ($NO_x$) adsorptivity. The properties of IACF were observed using EPMA, TGA and DSC and $NO_x$ adsorptivity was observed at high and low temperature. Before and after adsorption was analyzed using ToF-SIMS for examine surface characterization of adsorbed $NO_x$. The results showed that the better adsorptivity appeared for increasing KOH ratio. So, $NO_x$ adsorptivity showed result that is proportional between KOH and the adsorbed amount. On the other hand, adsorbent that manufactured without washing was better $NO_x$ adsorptivity than adsorbent that manufactured with washing. The behavior of adsorption show that crossing time of NO and $NO_2$ delayed for a rising adsorptivity. And NO ratio increased but $NO_2$ ratio decreased according as KOH ratio increases. $NO_x$ was confirmed through surface analysis that remain in $NO_2^-$ and $NO_3^-$ form on IACF surface.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.127-130
• /
• 2002

The 2.5 vol% TiNi/6061Al composites were fabricated by permanent mold casting, and its microstructures and tensile test for the cold rolled composites with maximum 50% reduction ratio were investigated. In the case of TiNi fiber with 2mm interval in preform, the interface bonding of fabricated composites were good. EPMA analysis results were found the small amount of Mg, Si segregated interface of diffusion layer. Transverse section of TiNi fiber was decreased with increasing reduction ratio and 40% reduction ratio was observed microcrack from TiNi fiber. And the tensile strength of composites at 38% reduction ratio was 194MPa. In the case of over 38% reduction ratio, the decrease of the tensile strength was due to TiNi fiber rupture by excess working. The fracture mode was appeared brittle fracture with increasing reduction ratio

• Journal of Technologic Dentistry
• /
• v.33 no.4
• /
• pp.339-347
• /
• 2011

Purpose: This study was investigated the bonding strength of two kinds of Ni-Cr alloy with respect to the condition of surface treatment. Methods: The surface treatment was performed on the two kinds of Ni-Cr alloy (B alloy and R alloy) specimens, which were sandblasted with $50{\mu}m$, $110{\mu}m$, and $250{\mu}m$ aluminium oxide and were treated with opaque application (paste and wash opaque). The roughness on the surfaces of the specimens was observed. The metal-ceramic interfaces were analyzed with EPMA in order to ionic diffusion, and the shear test was performed. Results: The BA250 specimen, which has higher surface roughness, showed the highest bonding strength in B specimens. In R specimens, the bonding strength of RA110 specimen was the highest. Conclusion: B specimen formed a mechanical bond between metal-ceramic interfaces; however, in the case of R specimen, a chemical bond was formed between that interfaces. There was no significant statistical difference between the bonding strengths of two types of specimens (p>0.05).