• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.5
• /
• pp.7-12
• /
• 2019

The naval surface vessels, which were often exposed to harsh marine environment, tended to be corrosive due to military operations on various sea-areas and courses. Although R.O.K Navy applied various methods to protect further corrosion, the hull corrosion occurred due to cavitation were found on the naval surface vessels at regular and occasional docking. Hull corrosion was a critical factor directly to affect the lifetime of ships and their operational capabilities adversely. In this paper, EH 2350, which was the main anticorrosion paint used by R.O.K. Navy, was compared with DuraTough DL by used by the U.S Navy to collect materials related to anti-corrosion paint. In addition, the paint compatibility verification was conducted through wear abrasion test. Assuming that it was exposed to sea-environment various both abrasion cycle and weight for objective verification. by varying both the abrasion cycles and weights. In this study, the reliability of the EH 2350 conformity, which was used in Naval surface vessels, was secured.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.227-233
• /
• 1999

This study is mainly concerned with phenomenon of cavitation-erosion on the several materials and corrosive liquids which were applied with vibrator (suggested by ASTM G-32, 20KHZ, 24{$mu}m$).The main results obtained are summarized as follows ; (1) The maximum erosion rate by cavitation erosion in both of fresh-water and sea-water appeared to be proportioned to their hardness and tensile strength. (2) Cavitation weight loss and rate of cast iron in sea-water condition were greater (approximately 3 times) than that in distilled-water condition, however in case of stainless and brass the cavitation weight loss and their rates were not so different in both of their conditions. (3) Cavitation weight loss of composite materials were shown as below on this test, DuraTough DL : Weight loss in sea-water condition were greater (approximately 2.3 times) than it's fresh-water condition. (4) As the result of observation with digital camea of specimens, the main tendency of cavitation erosion for metals, was that small damaged holes causing by cavitation e개sion was appeared with radial pattern, and composites materials was that small damaged holes were appeared randomly.