• International Journal of Railway
• /
• 제1권2호
• /
• pp.72-81
• /
• 2008

This paper introduces a new steel jacketing method for reinforced concrete columns with lap splice and evaluates its performance by a series of axial tests of concrete cylinders. At first, 45 concrete cylinders were fabricated with varying the design compressive strengths of 21, 27 and 35 MPa and, then, the part of them was jacketed with two-split-steel jackets under lateral confining pressure. The parameters in the first test were the steel jacket's thickness and the existence of adhesive between steel and concrete surface. In the second test, whole steel jackets were used to wrap cylinders with lateral pressure. Also, a double-layer jacket consisted of two steel plates was introduced; a cylinder was jacketed by two steel plates one after another. The effect of the new method was verified through comparing the results of the compressive tests for plain and jacketed cylinders. The steel jacket built following the new method showed good results of increasing the compressive strength and ductility of the jacketed cylinders with respect to the plain cylinders. The thicker steel jackets showed the more increased compressive strength, and the ductility at failure depended on the welding quality on steel jackets. The adhesive between steel and concrete surface reduced the confining effect of the steel jackets. The whole jacket showed more ductile behavior than the two-split jackets. The double-layered jackets were estimated to possess an equal performance to that of a single steel jacket having the same thickness of the double-layered jacket. Finally, the experimental results were compared with the constitutive model of steel-jacketed concrete; which showed a good agreement between the experimental results and the models.

• 한국구조물진단유지관리공학회 논문집
• /
• 제20권6호
• /
• pp.30-39
• /
• 2016

이 연구에서는 고연성과 낮은 탄성계수를 갖는 PET 섬유로 보강한 철근콘크리트 보의 부착특성과 휨거동을 각각 부착실험 및 휨실험을 통하여 규명하고자 하였다. 부착실험은 CSA S806에 따라 수행하였고, 실험변수는 섬유 종류와 보강량(CF 및 GF 시트 각 1겹, PET 시트 10겹)이었다. 총 8개의 보 실험에서 주요 실험변수는 단면의 연성비(${\mu}=3.4$, 7.0), 보강섬유 종류(CF, GF, PET) 및 보강량이었다. 보 단면의 모멘트-곡율 해석을 병행하였다. 부착실험의 결과, CF, GF 시트 1겹 보강에서 유효 부착길이는 각각 120, 60 mm 이었고 최대부착응력은 각각 3.25, 2.99 MPa 이었다. PET 10겹 보강에서 유효 부착길이는 60 mm, 최대 및 평균 부착응력은 각각 2.30, 2.10 MPa 이었다. 또한 최대 강도 시 CF, GF, PET의 변형율은 각각 0.36%, 0.49%, 6.29% 였으며 CF, GF 부착실험체는 계면에서 시트가 최종적으로 탈락하였지만 PET 부착 실험체에서 박리현상은 나타나지 않았다. 휨실험의 결과, PET 10, 20, 30겹으로 보강한 RC 보의 휨강도, 휨강성이 모두 무보강 보에 비해 증가하였고, 연성적인 휨파괴 양상을 보였으나 PET 30겹의 경우 20겹에 비하여 연성이 감소하였다. 모멘트-곡율 해석의 결과, PET 보강 보에서 접착제의 물성을 해석에 포함시키면 해석의 정확도가 향상하였다. 한편 PET 의 내구성에 대해서는 보고된 문헌이 없어서 현재 연구 진행 중이다.

• 대한기계학회논문집
• /
• 제17권10호
• /
• pp.2498-2508
• /
• 1993

$Al/SiC/Al_{2}O_{3}$ hybrid composites are fabricated by squeeze infiltration method. From the misconstructive of $Al/SiC/Al_{2}O_{3}$ hybrid composites fabricated by squeeze infiltration method, uniform distribution of reinforcements and good bondings are found. Hardness value of $Al/SiC/Al_{2}O_{3}$ hybrid composites increases linearly with the volume fraction of reinforcement because SiC whisker and $Al_{2}$O$_{3}$ fiber have an outstanding hardness. Optimal aging conditions are obtained by examining the hardness of $Al/SiC/Al_{2}O_{3}$ hybrid composites with different aging time. Tensile properties such as Young's modulus and ultimate tensile strength are improved up to 30% and 40% by the addition of reinforcements, respectively. Failure mode of $Al/SiC/Al_{2}O_{3}$ hybrid composites is ductile on microstructural level. Through the abrasive wear test and wear surface analysis, wear behaviour and mechanism of 6061 aluminum and $Al/SiC/Al_{2}O_{3}$ hybrid composites are characterized under various testing conditions. The addition of SiC whisker to $Al/SiC/Al_{2}O_{3}$ composites gives rise to improvement of the wear resistance. The wear resistance of $Al/SiC/Al_{2}O_{3}$ hybrid composites is superior to that of Al/SiC composites. The wear mechanism of aluminum alloy is mainly abrasive wear at low speed range and adhesive and melt wear at high speed range. In contrast, that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is abrasive wear at all speed range, but severe wear when counter material is stainless steel. As the testing temperature increases, wear loss of aluminum alloy decreases because the matrix is getting more ductile, but that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is hardly varied. Oil lubricant is more effective to reduce the wear loss of aluminum alloy and $Al/SiC/Al_{2}O_{3}$ hybrid composites at high speed range.

• 대한치과보철학회지
• /
• 제43권2호
• /
• pp.149-157
• /
• 2005

Statement of problem. Dental ceramics exhibit excellent esthetic property, compressive strength, chemical durability biocompatibility and translucency. However, it suffers from inherent brittle fractures. Various techniques and materials for intraoral porcelain repair has been suggested. Purpose. This study is to compare the tensile bond strength of four commonly used porcelain repair systems (Vivadent, Bisco, Ulttadent, Voco) and to insure the best system for the clinical application to the fractured porcelain. Materials and methods. A total of fifty specimens were fabricated. Specimens were stored in $37^{\circ}C$ distilled water for 7 days and thermocycling was performed(1000 cycles), and subjected to a tensile force parallel to the repair resin and porcelain interface by use of an Universal Testing Machine. Result. 1. Voco showed the highest tensile bond strength. In decreasing order, the tensile bond strength of the other materials was as follows : Ultradent, Bisco, Vivadent. 2. There was a statistically significant difference between the porcelain repair systems(Voco, Ultradent > Bisco, Yivadent) (p<0.05). 3. SEM examination of prepared porcelain surfaces revealed that the surface treated with Voco showed brittle fracture. However, Ultradent, Bisco and Vivadent showed ductile fracture. 4. All specimens treated with four porcelain repair systems showed adhesive failure between porcelain and composite resin.

• 한국구조물진단유지관리공학회 논문집
• /
• 제13권2호통권54호
• /
• pp.215-222
• /
• 2009

콘크리트 공시편의 외부보강을 위해서 강판과 FRP 자켓을 이용하였다. 기존의 강판 또는 FRP 자켓 보강기법은 보강재와 콘크리트 사이에 접착제를 이용하여 시공하므로 콘크리트와 보강재가 합성거동 하게 된다. 그러나 본 연구에서 사용한 강판 보강기법은 외부압착에 의한 기법으로 강판과 콘크리트가 합성거동을 하지 않는다. 본 연구에서는 비합성거동과 합성거동을 하는 보강된 콘크리트 시편의 압축 변형률의 측정과 이를 보정하는 기법을 제시하였다. 비합성거동의 강판보강 콘크리트 시편의 압축변형률 측정은 강판의 표면에서 변형률을 측정하여 표시할 수 없으며, 시편에 설치하여 측정하는 compressometer를 사용할 수도 없었다. 따라서 시편의 상하단에 두꺼운 판을 설치하여 두 판사이의 변형을 측정한 후. 이를 압축변형률로 변환하였다. 합성 거동을 하는 FRP 보강의 경우는 FRP 튜브 표면에서 측정되는 수직방향의 변형률을 콘크리트의 압축변형률로 사용이 가능하다. 그러나 튜브 표면의 수직변형률은 시편의 부풀음에 의한 인장변형률이 포함되어 있기 때문에 콘크리트의 압축변형률을 추정하기 위해서는 이를 보정하여야 한다. 보정된 압축변형률은 콘크리트 내부에서 측정한 변형률과 기존의 콘크리트 연속체 모델과 비교하였을 때, 만족한 결과를 보였다. 보정 전의 응력-변형률 곡선은 콘크리트의 연성거동 및 에너지 소산능력을 보정 전에 비해 낮게 평가할 위험성이 있다.