• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.95-104
• /
• 2005

The research conducted to study the potential practicability of recycled aggregate concrete by analyzing the characteristics of concretes made of recycled quality aggregates produced by wet and dry process has found the following results. The air content of recycled aggregate concrete increased with increase of the substitut on rate due to mortar included while producing recycled aggregates. However, the concretes with aggregate produced by dry process had relatively low rate of increase in air content. The slump showed generally decreasing trend as the substitution rate of recycled aggregate increased regardless of the wet or dry process. It was assumed that the mortar particles remained in recycled aggregate absorbed the surplus hydration in concrete and decreased fluidity The compressive strength generally decreased as the substitution rate of recycled aggregate increased, however there was an increasing trend as well due to decreasing effect of water-cement ratio when the substitution rate of recycled aggregate reached 25, 50% after mix. This phenomena also appeared in early age, which meant that recycled aggregate concrete should not be retarded in setting when applied in the field. The tensile strength also reached the maximum when wet or dry recycled aggregate replaced with 25%. To conclude, recycled aggregates for concrete produced by wet or dry process are expected to demonstrate essential characteristics of concrete without significant decline in physical or dynamic quality when the substitution rate is below 25% although there are variations subject to water-cement ratio. However, slight differences are expected due to types of recycled aggregate and physical quality.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.368-371
• /
• 2004

It analyzes the quality of the fine aggregate which is reproduced through a dry production process with cyclone and a wet production process. The conclusions of the study are as follows. 1. The recycled fine aggregate through the dry production process with cyclone shows the low rate of absorption and impurity content after the cyclone process. It shows that its density is 2.37, absorption rate is 4.8 and stability is $5.1\%$ and less. Therefore, it satisfies the standards of KS F 2573(recycled aggregate for concrete) as the first grade. 2. The recycled fine aggregate through the wet production process shows the low rate of absorption and foreign substance content after the process of wash and dehydration. It shows that its density is 2.40, absorption rate is 3.12 and stability is $3.2\%$ and less. Therefore, it satisfies the standards of KS F 2573(recycled aggregate for concrete) as the first grade.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.2
• /
• pp.92-97
• /
• 2009

In order to export aircraft components or substructures, it is necessary to get a certification from the main company for the components or an airworthiness certification from the FAA. In Korea, those processes are performed by a small number of private companies for aircraft components. However, airworthiness certification has never been done in the company. To export an assembled aircraft, whether small or large, it is obligatory to get a certification for the aircraft being exported. Currently, the Korean government is trying to get BASA agreement in a few years. For a mid-size company, it is easier to get the NADCAP audit process for the supply of aircraft components to the main company. In this paper, the overall process of aircraft certification is discussed and airworthiness certification is treated for export aircraft. Moreover, the NADCAP audit process is described in detail by introducing example parts made of composite material. This detailed process would be very helpful to a small or mid-size company that wants to develop and deliver aircraft components to foreign companies.

• Korean Journal of Medicinal Crop Science
• /
• v.22 no.4
• /
• pp.255-261
• /
• 2014

Cosmetic activities of the leaves of Curcuma longa L. were compared according to different drying methods, to expand the use of the by-products of Curcuma longa L. The highest extraction yield of 29.4% was obtained from vacuum drying process (VD), whose value was very close to 29.2% from freeze drying process (FD). Relatively lower extraction yield were observed as 24.5% and 25.3% from the raw leaf (RL) as control and hot air drying process (HD). The cytotoxicity was observed lower FD and VD than RL and HD. It shows that cytotoxicity was closely related to cosmetic activities such as tyrosinase and melanin inhibition activities by showing much better cosmetic activities of the extracts from both FD and VD than those from the RL and HD. It was interesting that was differences of the cosmetic activities and cytotoxicity between FD and VD, which implies that VD method should be a more efficient process than FD method in terms of drying time and operation costs: 6 hours vs 24 hours and 3-5 times higher extraction costs in drying. It was observed that VD is more excellent dry method than others. This result could be utilized to effectively dry other soft plant biomass.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1466-1468
• /
• 2009

The preparation method of copper nanopowder by dry process for conductive ink was investigated. Inert gas condensation method was used to synthesize copper nanopowder. The produced powders was spherical and sized 10~100nm flowing the conditions. The results showed that input voltage and evaporation rate is critical variables for nano-sized copper powder.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.491-492
• /
• 2006

The horizontal high energy rotor ball mill ($Simoloyer^{(R)}$) is used to break and activate dry solids. It is used for dry-milling and in the vertical mount for wet-milling in leaching processes. Technical electric arc furnace (EAF) dust with high contents of zinc oxide, zinc ferrite and magnetite is efficiently separated by ambient temperature leaching. The process shows promise for industrial application

• Transactions on Electrical and Electronic Materials
• /
• v.3 no.1
• /
• pp.42-45
• /
• 2002

Properties of lead zirconate titanate ferroelectric thin films prepared by rapid thermal annealing/direct insertion thermal annealing were investigated. The remnant polarization (Pr), saturation polarization (Ps), and coercive force (Ec) of typical samples annealed by rapid thermal annealing (RTA) are about 13.7 $\mu$ C/cm$^2$, 27.1 $\mu$C/cm$^2$, and 55.6 kV/cm, respectively. The dielectric constant of the sample is about 786, the dielectric loss tangent is about 2.4% at 1 kHz. Furthermore, ferroelectric, conduction, and piezoelectric properties of the thin films annealed by RTA process and the direct insertion thermal annealing (DITA) process were compared. The influence of temperature in the dry process on the above properties was also investigated.

• Journal of computational fluids engineering
• /
• v.21 no.2
• /
• pp.54-61
• /
• 2016

When spent fuel assemblies from the reactor of nuclear power plants(NPPs) are transported, the assemblies are exposed to short-term operations that can affect the peak cladding temperature of spent fuel assemblies. Therefore, it needs to perform the analysis of heat transfer on spent fuel dry cask during the operation. For 3 dimensional computational fluid dynamnics(CFD) simulation, it is proposed that the short-term operation is divided into three processes: Wet, dry, and vacuum drying condition. The three processes have different heat transfer mode and medium. Metal transportation cask, which is Korea Radioactive Waste Agency(KORAD)'s developing cask, is evaluated by the methods proposed in this work. During working hours, the boiling at wet process does not occur in the cask and the peak cladding temperatures of all processes remain below $400^{\circ}C$. The maximum peak cladding temperature is $173.8^{\circ}C$ at vacuum drying process and the temperature rise of dry, and vacuum drying process occurs steeply.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.36 no.2
• /
• pp.99-108
• /
• 2023

Currently, semiconductor manufacturing industry heavily relies on a wide range of high global warming potential (GWP) gases, particularly during etching and cleaning processes, and their use and relevant carbon emissions are subject to global rules and regulations for achieving carbon neutrality by 2050. To replace high GWP gases in near future, dry etching using alternative low GWP gases is thus being under intense investigations. In this review, we report a current status and recent progress of the relevant research activities on dry etching processes using a low GWP gas. First, we review the concept of GWP itself and then introduce the difference between high and low GWP gases. Although most of the studies have concentrated on potentially replaceable additive gases such as C₄F₈, an ultimate solution with a lower GWP for main etching gases including CF₄ should be developed; therefore, we provide our own perspective in this regard. Finally, we summarize the advanced dry etch process research with low GWP gases and list up several issues to be considered in future research.

• Tribology and Lubricants
• /
• v.36 no.1
• /
• pp.1-10
• /
• 2020

Large-area two-dimensional (2D) materials synthesized by chemical vapor deposition on donor substrates are promising functional materials for conductors, semiconductors, and insulators in flexible and transparent devices. In most cases, 2D materials should be transferred from a donor substrate to a target substrate; however, 2D materials are prone to damage during the transfer process. The damages to 2D materials during transfer are caused by contamination, tearing, and chemical doping. For the commercialization of 2D materials, a damage-free, large-area, and productive transfer process is needed. However, a transfer process that meets all three requirements has yet to be developed. In this paper, we review the recent progress in the development of transfer processes for 2D materials, and discuss the principles, advantages, and limitations of each process. The future prospects of transfer processes are also discussed. To simplify the discussion, the transfer processes are classified into four categories: wet transfer, dry transfer, mechanical transfer, and electro-chemical transfer. Finally, the "roll-to-roll" and "roll-to-plate" dry transfer process is proposed as the most promising method for the commercialization of 2D materials. Moreover, for successful dry transfer of 2D materials, it is necessary to clearly understand the adhesion properties, viscoelastic behaviors, and mechanical deformation of the transfer film used as a medium in the transfer process.