• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.7
• /
• pp.664-672
• /
• 2009

Nozzle in nuclear power plant is connected to pipe using safe end. Dissimilar metal weld between nozzle and safe end is followed by similar metal weld between safe end and pipe. And thus residual stress in dissimilar metal weld can be affected by similar metal weld. Similar metal weld impose bending stress on dissimilar metal weld, which is according to the length of safe end. In this study, simple nozzle model which covers various radius to thickness ratios was proposed to quantify residual stress in dissimilar metal weld based on finite element analyses. As a result, short length of safe end was proved to be more effective to mitigate residual stress in dissimilar metal weld and critical effective length of safe end is provided according to the radius to thickness ratio.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.110-114
• /
• 2008

Determination of weld-induced residual stress has been an important issue in nuclear power industry because several failures were reported in dissimilar metal weld parts due to primary water stress corrosion cracking. In this context, a couple of remarkable round robin analyses were conducted to quantify the welding simulation variables and to establish optimized numerical analysis process. The purpose of the present research is to introduce welding simulation results for a safety and relief nozzle, which has a dissimilar metal weld part as well as a similar metal weld part. First, finite element analyses are carried out to calculate residual stresses at the inside of nozzle considering only dissimilar metal welding. Subsequently, residual stresses taking into account both the dissimilar and similar metal welding are computed. The similar metal weld effect is evaluated by compa

• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.44-52
• /
• 1999

This study deals with spot weld ability of dissimilar aluminum alloy sheets in order to take advantage of its lightweight and strength. The paper also shows the relationship between weld elements(i.e. current, welding time and tip force) and weld quality on the resistance spot weld part of the same and dissimilar Al alloy. The conclusions are: (1) Because of excessive tip force, deep indentation remained at the Al 5182 side which is lower stiffness at the dissimilar Al alloy. (2) Weld quality (i.e. tensile shear strength) of dissimilar Al alloy is superior to that of the same Al 6061 alloy. (3) As long cycles, fatigue life of spot weld specimen on dissimilar Al alloy sheets was better than that of the same Al alloy.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.189-194
• /
• 2003

It is important to evaluate strength of dissimilar weld zone to use dissimilar materials safely. This study examines mechanical characteristics of dissimilar weld zone between low alloy steel and austenitic stainless steel that satisfies welding related requirements of ASME Code, experimentally reviews metallurgical and mechanical properties at and adjacent to weld interface. It is confirmed that hardness singularity occurs at the weld interface, and that optimum buttering thickness is more than 5㎜ from view points of tensile & yield strength. From a macroscopic view, brittle fracture characteristics is observed in buttering weld zone by tensile test.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.83-84
• /
• 2008

The primary water stress corrosion cracking (PWSCC) of dissimilar metal weld based on Alloy 82/182 is one of major issues in material degradation of nuclear components. It is well known that the crack initiation and growth due to PWSCC is influenced by material's susceptibility to PWSCC and distribution of welding residual stress. Therefore, modeling the welding residual stress is of interest in understanding crack formation and growth in dissimilar metal weld. Currently in Korea, a numerical round robin study is undertaken to provide guidance on the welding residual stress analysis of dissimilar metal weld. As a part of this effort, the present paper investigates distribution of welding resisual stress of a ferritic low alloy steel nozzle with dissimilar metal weld using Alloy 82/182. Two-dimensional thermo-mechanical finite element analyses are carried out to simulate multi-pass welding process on the basis of the detailed design and fabrication data. The present results are compared with those from other participants, and more works incorporating physical measurements are going to be performed to quantify the uncertainties relating to modelling assumptions.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.1025-1028
• /
• 2004

In this paper, we studied low cycle fatigue behavior of laser welded sheet metal that used automobile body panel. Specimens were manufactured as weld condition and sheet metal using automobile manufacturing company at present. For to know mechanical properties, micro Vicker's hardness test was performed of specimens. But, we can't confirm mechanical properties of weld bead and heat affected zone because laser weld makes very narrow weld bead and heat affected zone than other welding method. Therefore, we performed low cycle fatigue test with similar weldment, dissimilar weldment, similar thickness and dissimilar weldment, and dissimilar thickness and dissimilar weldment for fatigue properties of thickness and welding direction. As well, we analysis stress distribution of base metal, weld bead, and heat affected zone according to strain load using finite element method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.10
• /
• pp.873-881
• /
• 2008

Weld overlay is one of the residual stress mitigation methods which arrest crack initiation and crack growth. Therefore weld overlay can be applied to the region where cracking is likely to be. An overlay weld used in this manner is termed a preemptive weld overlay(PWOL). In pressurized water reactor(PWR) dissimilar metal weld is susceptible region for primary water stress corrosion cracking(PWSCC). In order to examine the effect of PWOL on residual stress mitigation, PWOL was applied to a specific dissimilar metal weld of Kori nuclear power plant by finite element analysis method. As a result, strong compressive residual stress was made in PWSCC susceptible region and PWOL was proved effective preemptive repair method for weldment.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.8 no.1
• /
• pp.19-24
• /
• 2012

This paper presents the results of finite element analysis for the effects of hydrostatic test and operating condition on the weld residual stress at dissimilar metal weld of a pressurizer safety nozzle in a nuclear power plant. For the study, the weld residual stress at ambient condition was analyzed using ABAQUS in the first place. After the weld residual stress analysis, the hydrostatic test condition and operating condition was applied to the same model one after another. The weld residual stress was observed to change due to the successive hydrostatic test and operating condition. The axial residual stresses on inner surface of the dissimilar metal weld and HAZ region were decreased by hydrostatic test and operating condition, which gives beneficial effect on preventing primary water stress corrosion cracking.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.88-93
• /
• 2008

Weld overlay is one of the residual stress mitigation method which arrest crack. An overlay weld sued in this manner is termed a preemptive weld overlay(PWOL). PWOL was good for distribution of residual stress of dissimilar metal weld(DMW) by previous research. Because range of overlay welding is wide relatively, residual stress distribution on PWR is affected by welding sequence. In order to examine the effect of welding sequence, PWOL was applied to a specific DMW of KORI nuclear power plant by finite element analysis method. As a result, the welding direction that from nozzle to pipe is better good for residual stress distribution on PWR.

• Journal of Welding and Joining
• /
• v.32 no.4
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.