• Journal of Welding and Joining
• /
• 제31권6호
• /
• pp.58-64
• /
• 2013

Several joining methods involving resistance welding, laser welding, ultrasonic welding and mechanical joining are currently applied in manufacturing lithium-ion batteries. Cu and Al alloys are used for tab and bus bar materials, and laser welding characteristics for these alloys were investigated with similar and dissimilar material combinations in this study. The base materials used were Al 1050 and oxygen-free Cu 1020P alloys, and a disk laser was used with a continuous wave mode. In bead-on-plate welding of both alloys, the joint strength was higher than the strength of O tempered base material. In overlap welding, the effect of welding parameters on the tensile shear strength and bead shape was evaluated. Tensile shear strength of overlap welded joint was affected by interfacial bead width and weld defect formation. The tensile-shear specimen was fractured at the heat affected zone by selecting proper laser welding parameters.

• Journal of Welding and Joining
• /
• 제33권2호
• /
• pp.85-90
• /
• 2015

Recently many studies for improvement of productivity and automation of process are in progress, and among others, laser-arc hybrid welding that combined laser and arc has attracted much attention. Since parameters by interactions as well as the parameters of each heat source should be considered, There are a lot of hardship in actual application, even though many researches have been done so far. Therefore in this study, bead welding was done to examine the effects of the flow rate of shield gas and the distance between laser and arc during laser-arc hybrid welding. As for hybrid heat source, disk laser and MIG were used. As experiment result, sound bead and weld with no defect were formed when the flow rate of front and rear shield gas were respectively 20 l/min and 15 l/min, and deep penetration was done at DLA=3 mm.

• Journal of Welding and Joining
• /
• 제27권4호
• /
• pp.18-25
• /
• 2009

See Full Text

• 한국레이저가공학회지
• /
• 제17권2호
• /
• pp.11-18
• /
• 2014

This research was conducted as a fundamental study to apply tailored blank welding technique into automotive production process. Specially we tried to apply the TWB technique to exhaust system. The materials used in this work were ferritic 439 stainless steel sheet with a thickness of 1.2mm and 0.8mm. Welding tests were conducted for BOP test and dissimilar thickness (0.8 to 1.2t) cases. Major process parameters were position of focus, travel speed, shielding gas and joint (gap) condition. As a result, there are nothing significant welding characteristic compare with TWB of carbon steel. Stainless steel shows the good weldability and mechanical properties (tensile, hardness and forming strength) also shows high level. Just problem is gap condition. However, also in this case, it shows not only good forming strength but also base metal fracture after tensile test. And to conclude, it is good opportunity to make lightweight design muffler using TB welding technique.

• 한국생산제조학회지
• /
• 제24권1호
• /
• pp.31-37
• /
• 2015

A laser line welder using a solid-state laser (Yb:YAG) has been manufactured for joining ultra-thin cold-rolled steel coils in steelworks. The coils to be welded primarily range from 0.15 to 0.3 mm in thickness and 800 to 1,100 mm in width. Because the steel plate is extremely thin, it is very important to control the stop positions of the clamp at cutting and welding points. In this study, both hydraulic proportional control valves and LVDT sensor embedded cylinders were used to precisely control and monitor the positions of clamps with complementary stoppers. As a result, the positions could be controlled within an error of ${\pm}30{\mu}m$. Erichsen cupping tests on the welded joints show that the Erichsen index ranges from 4.4 to 4.6 mm. Furthermore, the tensile strength of welding points is comparable to that of the base metal.

• Journal of Welding and Joining
• /
• 제31권3호
• /
• pp.66-75
• /
• 2013

In this study, the effect of coating thickness($20{\mu}m$ and $30{\mu}m$) on microstructure and tensile properties in Yb:YAG disk laser welds of Al-Si-coated boron steel (1.2mmt) was investigated. In the case of as welds, the quantity of ferrite was found to be higher in base metal than that in HAZ (Heat Affected Zone) and fusion zone, indicating, fracture occurrs in base metal, and the fracture position is unrelated to the coating thickness. Furthermore, yield strength, tensile strength of base metal and welded specimens showed similar behavior whereas elongation was decreased. On the other hand, base metal and HAZ showed existence of martensite after heat treatment, the fusion zone indicated the presence of full ferrite or austenite and ferrite during heat treatment ($900^{\circ}C$, 5min), After water cooling, austenite was transformed to martensite, and the quantity of ferrite in fusion zone was higher as compared with in base metal, resulting in sharply decrease of yield strength, tensile strength and elongation, which leads to fracture occured at fusion zone. In particular, results showed that because the concentration of Al was higher in 30um coating layer specimen than that of 20um coating specimen, after heat treatment, producing a higher quantity of ferrite was higher after heat treatment in the fusion zone; howevers, it leads to a lower tensile property.

• 대한기계학회논문집A
• /
• 제38권12호
• /
• pp.1373-1377
• /
• 2014

핫스탬핑 공정은 고강도의 강을 얻을 수 있는 방법으로써, 일반적으로 보론강을 오스테나이트 온도까지 가열한 후, 성형과 냉각을 통해 제품을 생산한다. 열처리된 보론강은 1500MPa 이상의 강도를 가지기 때문에 경량화와 안전성을 동시에 향상시킬수 있는 특징이 있다. 뿐만아니라 우수한 성형성으로 인한 치수정밀도가 기존 강판대비 90 % 이상 향상되어 우수한 성형품질을 확보할 수 있는 장점도 있다. 따라서 본 연구에서는 디스크 레이저를 사용하여 핫스탬핑 강판의 맞대기 및 겹치기 용접을 실시하여 용접특성을 파악하였다. 실험결과, 맞대기 용접에서는 맞댄면의 갭에 영향으로 인해 겹치기 용접과 비교하여 더 빠른 속도에서도 완전 용입을 얻을 수 있었으며, 모든 용접부에서 열영향부에서 화이트밴드가 관찰되었다.

• 대한기계학회논문집A
• /
• 제39권1호
• /
• pp.89-94
• /
• 2015

본 연구의 목적은 열처리 전 후의 보론강 레이저 용접성을 비교하는 것이다. 일반적으로 보론강이 핫스탬핑 공정에 사용되고 있으며, 핫스탬핑 공정은 강판을 오스테나이트 온도까지 가열한 후 성형과 동시에 냉각하는 방법이다. 열처리후 보론강은 1500 MPa 이상의 고강도를 가진다. 따라서 본 연구에서는 보론강 및 핫스탬핑강의 레이저 용접성을 조사한 후 비교하였다. CW 디스크 레이저를 이용하여 레이저 출력 및 용접속도를 변화시켜가며 맞대기 및 겹치기 용접을 실시하였다. 맞대기 용접 결과, 핫스탬핑강에서 완전 용입을 얻을 수 있는 임계냉각속도가 보론강보다 낮았으며, 겹치기 용접결과 완전 관통이 일어난 용접 조건에서는 접합부 폭은 용접속도와 관계없이 거의 유사하였다.

• Journal of Welding and Joining
• /
• 제34권1호
• /
• pp.75-81
• /
• 2016

This study applied laser surface melting process using CW(Continuous wave) Yb:YAG laser and cold-work die steel SM45C and investigated microstructure and hardness. Laser beam speed, power and beam interval are fixed at 70 mm/sec, 2.8 kW and $800{\mu}m$ respectively. Depth of Hardening layer(Melting zone) was a minimum of 0.8 mm and a maximum of 1.0 mm that exceeds the limit of minimum depth 0.5 mm applying trimming die. In all weld zone, macrostructure was dendrite structure. At the dendrite boundary, Mn, Al, S and O was segregated and MnS and Al oxide existed. However, this inclusion didn't observe in the heat-affected zone (HAZ). As a result of interpreting phase transformation of binary diagram, MnS crystallizes from liquid. Also, it estimated that Al oxide forms by reacting with oxygen in the atmosphere. The hardness of the melting zone was from 650 Hv to 660 Hv regardless of the location that higher 60 Hv than the hardness of the HAZ that had maximum 600 Hv. In comparison with the size of microstructure using electron backscatter diffraction(EBSD), the size of microstructure in the melting zone was smaller than HAZ. Because it estimated that cooling rate of laser surface melting process is faster than water quenching.

• The Journal of Advanced Prosthodontics
• /
• 제6권1호
• /
• pp.39-45
• /
• 2014

PURPOSE. The aim of the present study was to evaluate the accuracy of three techniques for correction of cast implant bars. MATERIALS AND METHODS. Thirty cast implant bars were fabricated on a metal master model. All cast implant bars were sectioned at 5 mm from the left gold cylinder using a disk of 0.3 mm thickness, and then each group of ten specimens was corrected by gas-air torch soldering, laser welding, and additional casting technique. Three dimensional evaluation including horizontal, vertical, and twisting measurements was based on measurement and comparison of (1) gap distances of the right abutment replica-gold cylinder interface at buccal, distal, lingual side, (2) changes of bar length, and (3) axis angle changes of the right gold cylinders at the step of the post-correction measurements on the three groups with a contact and non-contact coordinate measuring machine. One-way analysis of variance (ANOVA) and paired t-test were performed at the significance level of 5%. RESULTS. Gap distances of the cast implant bars after correction procedure showed no statistically significant difference among groups. Changes in bar length between pre-casting and post-correction measurement were statistically significance among groups. Axis angle changes of the right gold cylinders were not statistically significance among groups. CONCLUSION. There was no statistical significance among three techniques in horizontal, vertical and axial errors. But, gas-air torch soldering technique showed the most consistent and accurate trend in the correction of implant bar error. However, Laser welding technique, showed a large mean and standard deviation in vertical and twisting measurement and might be technique-sensitive method.