• Journal of the Korean Society of Industry Convergence
• /
• v.4 no.1
• /
• pp.27-34
• /
• 2001

Refining of powder particles and their dissolution into the Al matrix during mechanical alloying(MA) were investigated by using X-ray diffraction(XRD) transmission electron microscopy (TEM) functions of alloy composition, milling time and ball to powder ratio(BPR). It is found that Ti particles less than 20nm are observed in a dark field image of mechanically alloyed Al-10wt%Ti whose XHD pattern exhibits no Ti peak. The observed change of lattice constant of AI indicates that about 1 wt%Ti can he solved in Al after MA for a long time, independent of alloy composition, milling time and BPR, suggesting that most of Ti particles arc retained in the Al matrix. It is concluded that the disappearance of XRD peaks in mechanically alloyed Al-10wt%Ti is not simply attributable to the dissolution of Ti into Al, but associated mainly with extreme refining and/or heavy straining of Ti Particles.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1035-1041
• /
• 2001

The refining process and solubility of Ti in Al matrix during mechanical alloying (MA) were investigated by using X-ray diffraction (XRD), transmission electron microscopy (TEM) as functions of alloy composition, milling time and ball to powder ratio (BPR). Mechanical alloyed samples were annealed for investigating their stability and the formation behavior of$Al_3Ti$in the temperature range from$200{\circ}C$to$600{\circ}C$. It is observed from present experimental that disappearance of Ti peaks in mechanically alloyed Al-10wt%Ti is not simply attributable to the dissolution of Ti into Al, but associated mainly with extreme refining and/or heavy straining of Ti particles The annealing of the mechanically alloyed Al-Ti powders show differences in aluminide formation behavior when Ti content in Al is equal to or less than l0wt% and higher than l5wt%Ti. When Ti-content in Al is equal to or less than l0wt%, the MA powders transform directly to a global equilibrium state forming $DO_{22}- type\;Al_3$Ti above$400{\circ}C$. In the Al-Ti samples with equal to or higher than l5wt%Ti, transitional phases of cubic$Al_3Ti$and tetragonal $Al_{24}Ti_8$ are formed above$400{\circ}C$. They are stable only below$500{\circ}C$, and, $DO_{22}-type\;Al_3Ti$ becomes dominant aluminide at temperature higher than$ 600{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.347-356
• /
• 1992

Various kaolin samples with different alumina content were prepared from calcined admixture of kaolin and ammonium sulfate by varying the treatment time in sulfuric acid. Samples were nitridated under N2 or N2-H2 atmosphere with changing the amount of added carbon, the reaction time and temperature. As the alumina content lowered, the size of kaolin particles decreased and the specific surface area increased. XRD analysis indicated that ${\alpha}$-quartz remained by decomposition of halloysite and meta-halloysite. Experimental results of nitridation behavior are summerized as follows; 1) Nitridation under N2 atmosphere. With the increase of C/SiO2 ratio and with the decrease of Al2O3 content, disappearance of XRD pattern peaks of mullite, ${\alpha}$-quartz and ${\alpha}$-Al2O3 were accelerated at 1300$^{\circ}C$. SiC was the main phase in the reaction product of acid-treated kaolin samples nitridated at 1300$^{\circ}C$ for 10 hours regardless of C/SiO2 ratio. But the XRD peak intensities of ${\beta}$-Si3N4, ${\beta}$-sialon and SiC did not show much difference when untreated raw kaolin was fired at the same condition. When the ratio of C/SiO2 was 3.5, ${\beta}$-sialon and ${\beta}$-Si3N4 existed in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 7 hours. Only ${\beta}$-sialon existed in the same sample fired at 1400$^{\circ}C$ for 10 hours. ${\beta}$-sialon was obtained from all of the acid-treated kaolin samples fired at 1400$^{\circ}C$ for 40 hours, but AlN and SiC remained in the untreated kaolin sample. Z value of the ${\beta}$-sialon obtained from the 22% alumina containing kaolin sample fired at 1400$^{\circ}C$ for 40 hours was about 1.3(XRD) and 1.5(EDS). 2) Nitridation under 80N2+2OH2 mixed gas atmosphere with the C/SiO2 ratio of 1 Mullite was not found, but ${\alpha}$-Si3N4, and ${\beta}$-sialon were present in the reaction product of about 22% alumina containing kaolin sample fired at 1300$^{\circ}C$ for 10 hours. When untreated kaolin sample was nitridated at the same condition, mullite remained. AlN and SiC were not found in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 5 hours. On the other hand, AlN and SiC remained in the product of untreated kaolin fired at the same condition.

• Korean Journal of Materials Research
• /
• v.2 no.6
• /
• pp.408-416
• /
• 1992

Stable TiS$i_2$was formed by RTA on single-Si and on poly-Si. Subsequently, an Al-1% Si layer with 600-nm thick was deposited on top of the TiS$i_2$, Finally, the specimens were annealed for 30min at 400-60$0^{\circ}C$in $N_2$ambient. The thermal stability of Al-1% Si/TiS$i_2$bilayer and interfacial reaction were investigated by measuring sheet resistance, Auger electron spectroscopy (AES), and scanning electron microscopy (SEM). The composition and phase of precipitates formed by the reaction of Al-1% Si with Ti-silicide were studied by energy dispersive spectroscopy (EDS), X-ray diffraction (XRD). In the case of single-Si substrate the reaction of Al-1% Si layer with TiS$i_2$layer resulted in precipitates, consuming all TiS$i_2$layer at 55$0^{\circ}C$. On the other hand, the disappearance of TiS$i_2$on poly-Si occurred at 50$0^{\circ}C$ and more precipitates were formed by the reaction of Al-1% Si/TiS$i_2$on potty-Si substrate than those of the reaction on single-Si substrate. This phenomenon resulted from the fact that Ti-silicide formed on poly-Si was more unstable than on single-Si by the effect of grain boundary. By EDS analysis the precipitates were found tobe composed of Ti, Al, and Si. X-ray diffraction showed the phase of precipitates to be theT$i_7$A$l_5$S$i_12$ternary compound.