• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.11
• /
• pp.1137-1143
• /
• 2015

The stage II fretting fatigue crack growth and branching, i.e., the process of fretting fatigue crack growth starting in an inclined direction and then changing to the normal direction, is analyzed using the finite element method. The fretting fatigue experiment data of A7075-T6 are used in the analysis. The applicability of maximum tangential stress intensity factor, maximum tangential stress intensity factor range, and maximum crack growth rate as the crack growth direction criteria is examined. It is revealed that the stage II crack growth before and after the branching cannot be simulated with a single criterion, but can be done when different criteria are applied to the two stages of crack growth. Moreover, a method to determine the crack length at which the branching occurs is proposed.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.11 no.1
• /
• pp.29-36
• /
• 1991

The effects of heat treatment on fatigue crack growth behavior were studied in continuously reinfored, magnesium-based composite (FP/ZE41A). Following an earlier TEM investigation, specimens were thermally aged to modify the interfacial zone between the alumina fibers and mg alloy matrix. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction(longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparision of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth than as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens. SEM observations of fiber pullout and ductile tearing on the fatigue fracture surfaces indicate that the aging weakens the strength of the fiber/matrix interface, giving rise to the observed fatigue crack growth behavior.

• Journal of the Korean Society of Safety
• /
• v.13 no.4
• /
• pp.113-120
• /
• 1998

Fatigue crack growth rates(i.e. crack initiation and crack growth of short and long crack) are investigated using commercial plates of high strength Al alloy 7075-T651 for the transverse-longitudinal(T-L) direction in air, water and sea water. Also, the evaluation direct current potential drop(D.C.P.D) method and the fractographical analysis by SEM are carried out. Near threshold region, short crack growth rates were much faster than those of comparable long cracks, and these short crack growth rates actually decrease with increasing crack growth and eventually merge with long crack data. Fatigue crack propagation rates in aggressive media(i.e. sea water) increase noticeably over three times those in air. One of the most significant characters in this phenomenon as a corrosion-fatigue causes an acceleration in crack growth rates. Sea water environment, particularly Cl$^{[-10]}$ solution brings the most detrimental effects to aluminum alloy. The result of fractographical morphology in air, water and sea water by SEM shows obvious dimpled rupture and typical striation in air, but transgranular fracture surface in water and sea water.

• Journal of Korean Society of Steel Construction
• /
• v.14 no.6
• /
• pp.773-782
• /
• 2002

In this study, a series of fatigue tests are performed in order to estimate quantitatively the characteristics of fatigue crack growth rate according to the base metal, heat affected zone(HAZ) and weld metal, and the welding method and grade of strength of object steels, and the influence on fatigue crack growth rate according to the direction of welded line for high strength steels of SM570, POSTEN60, and POSTEN80 steels. From the fatigue test results, the retardations of fatigue crack growth rate are remarkable in case that the direction of notch is parallel to welded line than in case that the direction of notch is perpendicular to welded line because of compresive residual stress in weld metal & HAZ. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range. Meanwhile, fatigue safety is guaranteed sufficiently in the object steels because the fatigue crack growth rate in the range of fatigue crack propagation has a similar tendency to the test results & existing results.

• Journal of Welding and Joining
• /
• v.6 no.2
• /
• pp.30-39
• /
• 1988

Generally, as the welded region of weld structures has the incomplete bead and welded deposit which are able to behave like the surface cracks occasinally, there is a high possibility that the fatigue fracture of the weld structures is due to the surface cracks on the wlded region. This study was done to investigate the effects of post weld heat treatment (PWHT) on the fatigue behaviors of the surface crack of the heat affected zone (HAZ) for the multi-pass welds under the repetitive pure bending moment. The obtained results are summarized as follows : 1. The crack grows to the depth direction initially as the number of cylces increase, the amount of crack length is increased for the surface dir3ction and cive versa for the depth direction. 2. The fatigue life is increased in a order of as weld, PWHT specimens and parent. 3. As the number of cycles increase, the crack length is increased to th surface direction. The increase of the depth length is blunted at the center of specimen thickness. 4. The fatigue crack growth of PWHT specimens to the surface direction is dependent upon the holding time and applied stress during PWHT. In order words, the crack growth rate decreases with the holding time and increases with the applied stress during PWHT. 5. As the crack grows, the aspect formed in the course of crack propagation approaches to semicircle for parent and ellipse with the largest semidiameter for PWHT ($1/4hr, 15kgf/mm^2$) 6. At depth direction, it is difficult to apply to the paris' equation because of the scattered data between the crack growth rate and the stress intensity factor range.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.4
• /
• pp.474-482
• /
• 2006

Generally almost all fatigue crack growth is affected by mode I. For this reason a study on mode I has concentrated in the field of fracture mechanics. However the fatigue crack initiation and growth in machines and structures usually occur in mixed mode loading. If there is any relationship between the cause of fracture in mixed mode loading and fracture surface, fracture surface pattern will be the main mean explaining reasons of fatigue fracture and obtaining further information about fracture process. In this paper low point shear-fatigue test with Aluminum alloy hi 5083-O is carried out from this prospect and then the mixed mode distribution of fracture surface is examined from the result after identifying the generation of fatigue crack surface pattern. It was found from the experimental results that the fatigue crack surface pattern and the fatigue crack shear direction are remarkably consistent. Furthermore It is possible that the analysis of distribution of mixed mode through the fatigue crack surface pattern.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.43-44
• /
• 2006

Generally almost all fatigue crack growth is affected by model. For this reason a study on model has concentrated in the field of fracture mechanics. However the fatigue crack initiation and growth in machines and structures usually occur in mixed mode loading. If there is any relationship between the cause of fracture in mixed mode loading and fracture surface, fracture surface pattern will be the main mean explaining reasons of fatigue fracture and obtaining further information about fracture process. In this paper four point shear-fatigue test with Aluminum alloy Al 5083-O is carried out from this prospect and then the mixed mode distribution of fracture surface is examined from the result after identifying the generation of fatigue crack surface pattern. It was found from the experimental results that the fatigue crack surface pattern and the fatigue crack shear direction are remarkably consistent. Furthermore It is possible that the analysis of distribution of mixed mode through the fatigue crack surface pattern.

• Journal of Korean Society of Steel Construction
• /
• v.9 no.4 s.33
• /
• pp.515-521
• /
• 1997

The effects of heat treatment and fiber orientation on tensile strength and fatigue behavior were studied in a continuously reinforced. magnesium-based composite Following an earlier TEM investigation, specimens were thermally aged to modified the interfacial zone between the alumina fibers and the magnesium alloy matrix. From the tensile experimental results, the ultimate tensile strength of the aged specimens were lower than that of the as-fabricated due to weak fiber-matrix interfacial strength with chemical reaction during the thermal processing. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction (longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparison of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth the as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.4
• /
• pp.781-789
• /
• 1988

The fatigue crack growth and crack closure behavior of long through-thickness cracks and small half-penny shaped surface cracks were investigated in 5083-H113 Aluminum alloy under constant amplitude testing by the unloading elastic compliance method. It was found that, in the Region II, the crack growth behavior of both through-thickness and surface cracks exhibited the tri-linear form with two transitions and no concern with stress ratio R. In the Region I $I_{ab}$ and I $I_{b}$, through-thickness cracks grew faster than surface cracks in length direction, but at .DELTA. K .leq.4 MPa.root.m for R=0.1 the growth rates of surface cracks in depth direction, grew faster than those of through-thickness cracks. When the crack closure was considered, the growth rates of through-thickness cracks lay between the growth rates of depth direction and the growth rates of length direction in surface cracks. It is suspected that this was caused by the difference of crack closure at depth and length direction of surface cracks.s.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.14 no.3
• /
• pp.74-80
• /
• 2005

Steel plates used for common structures are manufactured by rolling processes in general. The rolling direction traces generated during the processes have significant influences on mechanical properties and fatigue behavior of the plates. The objective of present study is to investigate those directional characteristics for the enhancement of steel structure safety. SS400 steel plates of 3 mm thickness are tested in this study, When the angles between the tensile loading direction and the rolling direction of the plates are increased, their yield strengths are increased and elongations are rather decreased. It is also shown that fatigue crack growth rates in the plates can be increased according to the changes of those mechanical characteristics. For the safety of the structures, therefore, it is critical to decrease the angles between the rolling direction and the tensile loading direction.