• Journal of the Korean institute of surface engineering
• /
• v.36 no.1
• /
• pp.99-107
• /
• 2003

The diffusion coefficient of Xe-133 was obtained from an annealing test. The specimens were made from a UO$_2$ single crystal powder with natural enrichment. Weight and grain size were 300mg and ($23\mu\textrm{m}$, respectively. Oxygen potentials were obtained from an oxygen sensor. Released fractions were obtained from both results of gamma scans and quantitative analysis with MCNP code, The annealing test was performed at three temperatures at once. Diffusion coefficients of Xe-133 were calculated using slope of Booth theory in each O/M ratios. Activation energy and the pre-exponential factor of the diffusion coefficient were obtained. The activation energy of near stoichiomeric $UO_2$ is 310 kJ/mol. The measured values of near stoichiometric $UO_2$ are very close to other data available. Diffusion coefficients increase with hyper-stoichiometry, due to higher concentration of cation vacancies.