• Korean Chemical Engineering Research
• /
• v.49 no.1
• /
• pp.75-82
• /
• 2011

Five different composition UV-cured poly(urethane acrylate-co-acrylic acid) (PU-co-AA) films have been prepared by reacting isophorone diisocyanate(IPDI), polycaprolactone triol(PCLT), 2-hydroxyethyl acrylate(HEA), and different weight ratio trimethylolpropane triacrylate(TMPTA) and acrylic acid(AA) as diluents, and characterized using a Fourier transform infrared spectroscopy(FT-IR). The adhesion properties onto the stainless steel, morphology, mechanical hardness, and electrical property of UV-cured PU-co-AA films were investigated as a function of acrylic acid(AA) content. All the PU-co-AA films are structure-less and the molecular ordering and packing density decreased with increasing content of AA due to the flexible structure and -COOH side chains in AA. The crosscut test showed that PU-co-AA films without AA and with low content of AA showed 0% adhesion(0B) and the adhesion of PU-co-AA films in the range of 40-50% AA increased dramatically as the content of AA increases. The pull-off measurements showed that the adhesion force of PU-co-AA films to stainless steel substrate varied from 6 to 31 kgf /$cm^2$ and increased linearly with increasing AA content. The mechanical hardness also decreased as the content of AA increases. This may come from relatively linear and flexible structure in AA and low crystallinity in PU-co-AA films with higher content of AA. The higher AA-containing PU-co-AA films showed higher dielectric constant due to the increase of polarization by introducing AA monomer. In conclusion, the physical properties of UV-cured PU-co-AA films are strongly dependent upon the content of AA and the incorporation of AA in polyurethane acrylate is very useful way to increase the adhesion strength of UV-curable polymers on the stainless steel substrate.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.3
• /
• pp.33-38
• /
• 2021

Recently, rollable and foldable displays are attracting great attention in the flexible display market due to their excellent form factor. To predict and prevent the mechanical failure of the display panels, it is essential to accurately understand the mechanical properties of brittle SiN_x thin films, which have been used as an insulating film in flexible displays. In this study, tensile properties of the ~130 nm- and ~320 nm-thick SiN_x thin films were successfully measured by coating a ~190 nm-thick organic nano-support-layer (PMMA, PS, P3HT) on the fragile SiN_x thin films and stretching the films as a bilayer state. Young's modulus values of the ~130 nm and ~320 nm SiN_x thin films fabricated through the controlled chamber pressure and deposition power (A: 1250 mTorr, 450 W/B: 1000 mTorr, 600 W/C: 750 mTorr, 700 W) were calculated as A: 76.6±3.5, B: 85.8±4.6, C: 117.4±6.5 GPa and A: 100.1±12.9, B: 117.9±9.7, C: 159.6 GPa, respectively. As a result, Young's modulus of ~320 nm SiN_x thin films fabricated through the same deposition condition increased compared to the ~130 nm SiN_x thin films. The tensile testing method using the organic nano-support-layer was effective in the precise measurement of the mechanical properties of the brittle thin films. The method developed in this study can contribute to the robust design of the rollable and foldable displays by enabling quantitative measurement of mechanical properties of fragile thin films for flexible displays.