• Archives of Metallurgy and Materials
• /
• v.65 no.4
• /
• pp.1357-1360
• /
• 2020

The low adherence of diamond-like carbon (DLC) films on titanium (Ti) alloys can be improved by using interlayer coatings. In this study, DLC (a-C:H) films were deposited using radio-frequency plasma-enhanced chemical vapor deposition (rf-PECVD), and a TiCN interlayer was applied between the extra low interstitial (ELI) grade of Ti-6Al-4V alloy and a-C:H film. The characteristics of the a-C:H-coated Ti-6Al-4V ELI alloy were investigated using field emission scanning electron microscopy, Vickers hardness, and scratch and wear tests. The DLC (a-C:H) films deposited by rf-PECVD had a thickness of 1.7 ㎛, and the TiCN interlayer had a thickness of 1.1 ㎛. Vickers hardness of the DLC (a-C:H) films were increased as a result of the influence of the TiCN interlayer. The resulting friction coefficient of the a-C:H-coated Ti-6Al-4V with the TiCN interlayer had an extremely low value of 0.07.

• Journal of Periodontal and Implant Science
• /
• v.24 no.1
• /
• pp.131-143
• /
• 1994

For maintenance of exposed implant in healthy state, it is necessary to treat the surface of implant fixture and provide the surface adjustable to surrounding tissues. Variable techniques have been introduced such as citric acid and air-abrasive system to treat the failed implant. Although when the rough surface of HA coated implant was exposed to oral environment, the surface treatment method with citric acid or air-abrasive system is effective for removal of bacterial endotoxin, it is unsuccessful to prevent plaque deposition due to difficulty in removal of rough surface of HA coated implant. Thus, in this study the method that removes bacterial endotoxin and makes smooch surface without alteration of surface characteristics was studied. HA coated disc manufactured by IMZ Co. Was treated with high speed diamond bur, low speed diamond bur, stone bur, rubber point, jetpolisher. And then its surface state was examined with profilometer and SEM to evaluate the surface smoothness, and its surface component was analyzed with EDX to evaluate wheter the surface characteristics were altered or not. As a result, following results were obtained. When the surface roughness of each implant disc was measured by profilometer, the group I showed a $R_{max}\;2.11{\mu}m$ and the group II, III, IV, V showed a $R_{max2}\;4.17{\mu}m$, $7.28{\mu}m$, $8.61{\mu}m$ and $39.44{\mu}m$ respectively. That is, surface smoothness was highest in the group I and it has been gradually decreased in the group II, III, IV and V. Under the SEM examination, the group I showed relatively smooth surface and the group II showed slightly rougher surface than the group I due to partially remaining HA particles while most HA particle was removed. The group III and IV showed rough topography due to HA particles that was not grinded, and HA coated surface in group V showed very irregular surface with deep groove and prominence. In cross-sectional view, the group I showed uniform surface, and the group III, IV showed rough surface due to remaining HA particles but the thickness of HA coating was remarkably reduced. The group II has similar pattern in group I, and the group V showed about $40{\mu}m$ thickness although it was not constant. By analysis of surface component with EDX, the group II in which the grinding was effective showed a small quantity of calcium and phosphorous and the group III, IV, in which the grinding was incomplete showed calcium and phosphorus peak. In all experimental group, no other than titanium, aluminum, calcium, phosphorus was observed.

• Journal of the Korean Vacuum Society
• /
• v.10 no.4
• /
• pp.431-439
• /
• 2001

In this paper, the a-Diamond films were synthesized using filtered vacuum arc source (FVAS), FVAS was composed of a torus structure with bending angle of 60 degree. The radius of torus was 266 mm, the radius of plasma duct was 80 mm and the total length was 600 mm. The magnet parts were composed of one permanent magnet and five solenoid magnets. The plasma duct was electrically isolated from the ground so that a bias voltage could be applied. The baffles inside plasma duct were installed in order to prevent the recoil effect of macro-particles. Cathode was made of graphite with 80 mm in diameter. The effects of solenoid magnet on plasma extraction were investigated by computer simulation and experiment using Taguchi's methode. The source and extraction magnet affected the arc stabilization. The extraction beam current was maximized with low value of the source magnet current and high value of the filtering magnet current. The beam current density was 3.2 mA/$\textrm{cm}^2$ and average deposition rate was 5 $\AA$/sec when the currents of arc discharge, source, extraction, bending, deflection and outlet magnet were 30 A, 1 A, 3 A, 5 A, 5 A, and 5 A, respectively. The beam current density and the efficiency of beam transportation were increased with the positive bias voltage of the plasma duct.

• Journal of the Korean Vacuum Society
• /
• v.15 no.3
• /
• pp.287-293
• /
• 2006

Diamond-like carbon (DLC) film was deposited using benzene $(C_6H_6)$ by r. f-plasma assisted chemical vapor deposition. The tribological properties of the DLC film were tested by rotating ball-on-disc type tribometer isolated by a chamber. The tribological test was performed in air environment of relative humidity ranging from 0 to 90% in order to observe the tribological behavior of the DLC film with the change of humidity. We used steel ball and DLC coated steel ball to investigate the effect of the counterface material. Using steel ball, the friction coefficient of DLC film increased from 0.025 to 0.2 as the humidity increased from 0% to 90%. In case of DLC coated steel ball which didn't form the Fe-rich debris, the friction coefficient showed much lower dependence of humidity as 0.08 in relative humidity 90%. We confirmed that the high humidity dependence of the friction coefficient using steel ball resulted from the increase of debris size with humidity and the formation of Fe-rich debris by the wear of steel ball. And the friction coefficient was immediately dropped when the relative humidity changed from 90% to 0% during test using steel ball. From this result, we confirmed that the effect of the Fe-rich debris on the friction coefficient was that Fe element in debris formed the highly sensitive graphitic transfer layer to humidity.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.59-65
• /
• 1998

Multi-layer diamond-like carbon (DLC) films were deposited by 13.56 MHz r.f. PACVD method. Multi-layer DLC film was composed of 2.5 $mu extrm{m}$ thick pure DLC filml and 0.2$\mu\textrm{m}$ thick Si incorporated DLC (Si-DLC) film as a surface layer. Tribological behaviors of the multi-layer DLC film were investigated with a ball-on-disk type tribometer in ambient atmosphere using AISI 52100 steel ball. Low friction coefficient (<0.1) period increased with increasing the Si content in the surface Si-DLC film. The wear rate after 44,000 cycles and 158,400 cycles were the $2.5\times10^{-8}\sim1.8\times10^{-7}\textrm{mm}^3$/rev. and $7.1\times10^{-9}\sim1.8\times10^{-8}\textrm{mm}^3$/rev.,respectively. The wear rate of the multi-layer DLC film after 158,400 cycles was about 2 times smaller than that of pure DLC films of 2.7 $\mu\textrm{m}$ thickness. This high wear resistance and low friction coefficient was caused by the formation of Si oxide layer on the wear scar surface, as confirmed by the debris composition analysis. It was further shown that this si oxide debris layer on the wear scar surface is formed again even after removing the debris of the steel ball, which maintain the low friction coefficient between multi-layer DLC films and steel ball.

• Tribology and Lubricants
• /
• v.33 no.4
• /
• pp.127-133
• /
• 2017

In order to characterize the adhesive properties and failure mechanisms of diamond-like carbon (DLC) films of two different thicknesses (130 nm and $1.2{\mu}m$), deposited by plasma-enhanced chemical vapor deposition on a Si substrate, scratch testing with a micro-indenter ($12.5{\mu}m$ tip radius) was performed under a linearly increasing load. These scratch tests were conducted under the same test conditions for both films. The critical load of each film was estimated from the scratch test results, based on a sharp increase in the coefficient of friction and a clear distinction of failure modes. The critical load was the basis for evaluating the adhesion strength of the films, and the $1.2{\mu}m-thick$ DLC film had superior adhesion strength. For better understanding of the failure modes, the following analyses were conducted: friction behavior and scratch tracks analysis using scanning electron microscopy, energy-dispersive spectroscopy, and 3-D profilometry. The scratch test results showed that failure modes were related to the thickness of the films. The 130 nm-thick DLC film underwent cohesive failure modes (cracks and chipping) before reaching to a gross failure stage. On the other hand, the thicker DLC film ($1.2{\mu}m-thick$) did not exhibit micro cracks before a sudden gross failure of the film together with the evidence of cracking and chipping of the Si substrate.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.5
• /
• pp.235-240
• /
• 2013

Pure-carbon materials such as graphite, graphene, carbon nanotubes, and diamond have very high thermal conductivities. The reported thermal conductivity of graphene is in the range 3000~5000W/m-K at room temperature. Here, we developed graphene/cu foam hybrid type heat spreader to obtain higher thermal conductivity than Cu foam. Hybrid materials were characterized using optical microscopy (OM), scanning electron microscopy (SEM) and thermal conductivity measurement system; LFA (Laser Flash Analysis @ LFA 447, NETZSCH). We suggest that excellent thermal properties of graphene/cu foam hybrid structures are beneficial for all proposed electrical applications and can lead to a thermal management application.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.135-135
• /
• 1999

It is well known that Raman spectroscopy is powerful tool in analysis of sp3/sp3 bonding fraction in diamond-like carbon(DLC) films. Raman spectra of DLC film is composed of D-peak centered at 1350cm-1 and G-peak centered at 1530cm-1. The sp3/sp3 fraction is qualitatively acquired by deconvolution method. However, in case of DLC film, it is generally observed that G-peak position shifts toward low wavenumber as th sp3 fraction increases. However, opposite results were frequently observed in ta-C films. ta-C film has much higher residual compressive stress due to its high sp3 fraction compared to the DLC films deposited by CVD method. Effect of residual stress on G-peak position is most recommendable parameter in Raman analysis of ta-C, due to its smallest fitting error among many parameters acquired by peak deconvolution of symmetric spectra. In current study, the effect of residual stress on Raman spectra was quantitatively evaluated by free-hang method. ta-C films of different residual stress were deposited on Si-wafer by modifying DC-bias voltage during deposition. The variation of the G-peak position along the etching depth were observed in the free-hangs of 20~30${\mu}{\textrm}{m}$ etching depth. Mathematical result based on Airy stress function, was compared with experimental results. The more reliable analysis excluding stress-induced shift was possible by elimination of the Raman shift due to residual compressiove stress.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.6
• /
• pp.239-244
• /
• 2019

Two hydrogenation surface modifications, namely hydrogen atmosphere heat treatment and hydrogen plasma treatment, were found to lead to improved dispersion of nanodiamond (ND) seed particles and enhanced nucleation density for deposition of smooth ultrananocrystalline diamond (UNCD) film. After hydrogenation, the C-O and O-H surface functionalities on the surface of nanodiamond particles were converted to the C-H surface functionalities, and the Zeta potential was increased. As the degree of dispersion was improved, the size of nanodiamond aggregates decreased significantly and nucleation density increased dramatically. After hydrogen heat treatment at 600℃, average size of ND particles was greatly reduced from 3.5 ㎛ to 34.5 nm and a very high nucleation of ~3.9 × 10¹¹ nuclei/㎠ was obtained for the seeded Si surface.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.183-183
• /
• 2012

In the era of 45 nm or beyond technology, conventional etch mask using photoresist showed its limitation of etch mask pattern collapse as well as pattern erosion, thus hard mask in etching became necessary for precise control of etch pattern geometry. Currently available hard mask materials are amorphous carbon and polymetric materials spin-on containing carbon or silicon. Amorphous carbon layer (ACL) deposited by PECVD for etch hard mask has appeared in manufacturing, but spin-on carbon (SOC) was also suggested to alleviate concerns of particle, throughput, and cost of ownership (COO) [1]. SOC provides some benefits of reduced process steps, but it also faced with wiggling on a sidewall profile. Diamond like carbon (DLC) was also evaluated for substituting ACL, but etching selectivity of ACL was better than DLC although DLC has superior optical property [2]. Developing a novel material for pattern hard mask is very important in material research, but it is also worthwhile eliminating a potential issue to continuously develop currently existing technology. In this paper, we investigated in-situ dry-cleaning (ISD) monitoring of ACL coated process chamber. End time detection of chamber cleaning not only provides a confidence that the process chamber is being cleaned, but also contributes to minimize wait time waste (WOW). Employing Challenger 300ST, a 300mm ACL PECVD manufactured by TES, a series of experimental chamber cleaning runs was performed after several deposition processes in the deposited film thickness of $2000{\AA}$ and $5000{\AA}$. Ar Actinometry and principle component analysis (PCA) were applied to derive integrated and intuitive trace signal, and the result showed that previously operated cleaning run time can be reduced by more than 20% by employing real-time monitoring in ISD process.