• Journal of Technologic Dentistry
• /
• v.23 no.1
• /
• pp.65-73
• /
• 2001

The purpose of this study was to investigate the microstucture and hardness, corrosion of pure Ti alloy, which is widely used as partial denture frame work these days, depending on the cooling method, followed by casting. The first group was bench cooling at room temperature($18^{\circ}C$), the second group was slowly cooled in the furnace from $700^{\circ}C$ to room temperature, and third. rapidly cooled in $0^{\circ}C$ water. The microstructure of each specimen observed by means of photomicrograph taken by electron microscope, in add to the physical characteristics of each specimen were obtained using the rockwell Hardnest Number. the characteristics of corrosion. The results were obtained as follows: 1. From Potentiodynamic plot. we conclude furnace-cooled specimen had the best stabiltity of passive film and that air-cooled specimen showed similar characteristics. The density of electric current of quenched specimen was the highest, which formed kind of unstable passive film. 2. Specimen cooled at room temperature (air cooling) had the highest value of hardness of 81.26HRB, specimen cooled at ice-water, $0^{\circ}C$, had the value of 78.42HRB, and specimen furnace-cooled at $700^{\circ}C$ had lowest value of 77.1HRB. 3. Quenching treated micro-structure formed martensite structure by and large. In case of air cooling, we could see $\alpha$-structure widmanstatten formed overall. In furnace cooling, widmanstatten structure and various shape $\alpha$-structures forming colony with direction were detected.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.337-344
• /
• 2015

Purpose: The purpose of present study is to examine the correlation between the accuracy of abutment preparation and the marginal adaptation of metal coping. With this view, this study compared the correlations regard to the three different manufacturing methods of selective laser sintering technique, milling and casting. Materials and methods: Two master models were made in a different way. First model with deep chamfer margin was prepared directly by a general clinician and the second model was designed by 3-D designing software program with the same abutment preparation principle and produced by computer aided manufacturing. 12 Co-Cr alloy copings were produced respectively with three different method; SLS system, CAD/CAM milling and conventional lost wax technique from each master model. The total 72 copings fully sit on the master model were stereoscopically evaluated at 40 points along the entire circumferential margin. Results: Significant differences in the absolute marginal discrepancies of Co- Cr copings from SLS system (P=.0231) and casting method (P<.0001) were shown between hand preparation model and computer designed model. However, no significant difference was found between the two model groups from milling method (P=.9962). Conclusion: Within the limitation of this study, the effect of the accuracy of abutment preparation on the marginal adaptation of Co-Cr coping is statistically significant in SLS system and casting group. The copings produced by SLS system exhibited the lowest marginal discrepancies among all groups, and the marginal gap of this method group was influenced by the accuracy of the abutment preparation.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.2
• /
• pp.169-177
• /
• 2000

The purpose of this study was to compare the retention of complete cast crown over amalgam ores, composite resin cores, and cast gold cores when cemented with three different luting agents. Eighteen core specimens each of amalgam(Bestaloy, Dong Myung, Seoul, Korea), composite resin (Z100, 3M Dental product, st. Paul, Minn) and type IV gold alloy (Ba-4, Heesung Engelhard Corp., Korea) were made in a customized milling stainless steel die. A wax pattern with a loop attached to occlusal surface was made for each core and a type II gold alloy casting was fabricated. The castings which had clinically acceptable marginal fit were used as test samples. The following luting cements were used to cement cast crowns on each core material : (1) zinc phosphate cement (Confi-dental Products Co., USA) (2) glass-ionomer cement (Fuji Plus, GC Industrial Corp., Tokyo, Japan) (3) resin cement (Panavia 21, Kuraray Co., USA). All cements were mixed according to manufacturers' instructions. A static load of 5kg was then applied for 10 minutes on the crowns. All specimens were stored in saline solution for 24 hours at $37^{\circ}C$ and thermocycled for 500 cycles. After storage and cycling, the tensile bond strengths were measured by using a universal testing machine (Instron Corp., Canton, Mass.) at a crosshead speed of 0.5mm/min. The results were as follows 1. The retentive strength of resin cement was the highest of alt three types of cement for resin core (p<0.05). 2. There was no statistical difference among the retentive strengths of three cements for amalgam core (p>0.05). 3. The retentive strength of resin cement was higher than that of zinc phosphate for cast core, but there was no difference between the retentive strength of glass ionomer cement and those of rein and zinc phosphate cement. 4. The retentive strength of the zinc phosphate cement for amalgam core was the highest of all type of cores.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.37-45
• /
• 2011

Purpose: Heat pressed ceramics, used for all ceramic restorations, have the additional advantage of being technically less change through using of the lost-wax technique. Conceptually, combining the ceramic with the clinically proven reinforcing ability of a metal framework would be advantageous; however, cause of mismatching of fusion between ceramics and metal frameworks which from differences of casting temperature and coefficient of thermal expansion, pressed ceramics could not be used with a metal framework. The purpose of this study was to compare shear bond strength of press-to metal ceramic to porcelain fused non precious metal and feldspatic porcelain fused non precious metal. Methods: The 30 metal specimens were casted in a porcelain fused non precious metal nickel-chromium alloy. They were divided into 3 groups by surface treatment and applied ceramic: $125{\mu}m$ aluminium oxide sandblasting and veneered feldspatic porcelain (group FP), $125{\mu}m$ aluminium oxide sandblasting and had press-to-metal ceramic applied (group PC), porcelain bonder (gold bonder) fused on surface of metal specimens and had press-to-metal ceramic applied (group PCG). In each group 10 metal specimens were used. The press-to-metal ceramic applied 20 specimens had ash-free wax pattern applied, the metal-wax complexes invested, and were pressed with heat press ceramic. All specimens were subjected to shear bond strength test at a crosshead speed of 1.0 mm/min. Results: The results of measured in Mean SD and data were analyzed by one-way AVOVA (p= .05) and Tukey HSD test (p= .05).: group FP $16.090{\pm}1.841$ MPa, group PC $12.620{\pm}1.8256$ MPa, group PCG $10.920{\pm}0.9283$, significant differences between all groups (p < .05). Significant differences were found in each between group FP and group PC, group FP and group PCG (p < .05). Conclusion: The shear bond strength of press-to-metal ceramic to porcelain fused non precious metal was described higher in unused gold bonder group than used gold bonder groups.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.1
• /
• pp.73-79
• /
• 2011

Purpose of this experiment is to evaluate the effect of titanium on the castability when the titanium is added to the Co-Cr alloy. Raw materials Cobalt, Chrome, Molybdenum, Silicon, Manganase, Carbon, Nitrogen, Titanium were weighted and prepared. $Biosil^F$ (Degudent, Germany) was the control group. To the experimental group, different weight percent of titanium was added from 1 wt% to 4 wt%. The wax pattern is $30{\times}40$ cm in size, rectangular in shape and has total of 160 grids. Centrifugal machine (Neutrodyne Easy Ti: Manfredy) was used for casting. For evaluation of the castability, the number of complete grids was counted by visual inspection and X-ray inspection. The test showed similar castability with the control group in the titanium addition of 1 wt% to 3 wt%. The titanium addition of 4 wt% showed poor result. With titanium lower than 4 wt%, the experiment metals showed proper castability with high expectation of successful clinical use.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.3
• /
• pp.170-175
• /
• 2017

PURPOSE. The aim of the present study was to evaluate the fracture resistances of zirconia, cast nickel-chromium alloy (Ni-Cr), and fiber-composite post systems under all-ceramic crowns in endodontically treated mandibular first premolars. MATERIALS AND METHODS. A total of 36 extracted human mandibular premolars were selected, subjected to standard endodontic treatment, and divided into three groups (n=12) as follows: cast Ni-Cr post-and-core, one-piece custom-milled zirconia post-and-core, and prefabricated fiber-glass post with composite resin core. Each specimen had an all-ceramic crown with zirconia coping and was then loaded to failure using a universal testing machine at a cross-head speed of 0.5 mm/min, at an angle of 45 degrees to the long axis of the roots. Fracture resistance and modes of failure were analyzed. The significance of the results was assessed using analysis of variance (ANOVA) and Tukey honest significance difference (HSD) tests (${\alpha}=.05$). RESULTS. Fiber-glass posts with composite cores showed the highest fracture resistance values ($915.70{\pm}323N$), and the zirconia post system showed the lowest resistance ($435.34{\pm}220N$). The corresponding mean value for the Ni-Cr casting post and cores was reported as $780.59{\pm}270N$. The differences among the groups were statistically significant (P<.05) for the zirconia group, as tested by ANOVA and Tukey HSD tests. CONCLUSION. The fracture resistance of zirconia post-and-core systems was found to be significantly lower than those of fiber-glass and cast Ni-Cr post systems. Moreover, catastrophic and non-restorable fractures were more prevalent in teeth restored by zirconia posts.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.196-196
• /
• 2016

치과나 기공소로부터 높은 원가로 인한 재료선택에 어려움을 겪고 있어 귀금속 금합금의 물성을 가질 수 있도록 하면서 가격급등으로 인한 문제 해결하기 위한 비귀금속 합금으로 대체가 필요하기에 이에 따른 연구가 이루어져 국산 제품의 상품화를 위해 파라듐을 이용하여 적합한 새로운 합금을 개발하는 것이 필요하다. 치과용 골드합금은 미국치과의사 협회의 구정에 의하면 1형부터 4형까지 분류하고 있으며 3형에 해당하는 강도와 기계적인 특성을 갖도록 파라듐으로 대체하는 연구가 진행중이거나 시판되고 있다. 따라서 본 연구에서는 2형, 3형 및 4형을 대체가능하도록 팔라듐을 기반으로 한 새로운 합금을 설계하고 합금의 성분원 소인 Au(1~5), Pd(20~25), Ag(70~75), In(1.5) 및 Zn(2)등으로 조성을 변화시켜 측량 후 합금을 제조하기 위하여 아르곤 분위기하의 진공아크용해로를 이용하여 용해하였다. 정량된 금속을 진공아크 용해로에 장입하고 용해는 균질한 합금이 되도록 최소한 6회 이상 용융을 실시하며 합금성분의 손실이 발행하지 않도록 보정을 하였다. 합금의 미세조직 관찰을 위하여 샘플을 고속 다이아몬드 정밀 절단기(Acculom-5, STRUERS, Denmark)를 이용하여 절단한 후 2000 grit의 Sic 연마지에서 단계적으로 $0.3{\mu}m$ 알루미나 분말까지 연마한 후 초음파 세척을 하였다. 준비한 시편은 KCN과 $(NH_4)_2S_2O_8$을 1:1로 혼합한 부식액으로 에칭한 후 OM과 SEM을 이용하여 조직을 관찰하였으며 각 샘플의 성분변화는 EDS 분석을 통해 확인하고 결정구조는 XRD를 사용하여 분석하였다. 경도시험은 비커스경도시험기를 이용하여 5kg의 하중을 30초간 작동시켜 압흔을 연결된 micron으로 평균값을 측정하였다. 각 시편의 부식거동은 POTENTIOSTAT(Model PARSTAT 2273, EG&G, USA)을 이용하여 구강 내환경화 유사한 $36.5{\pm}1^{\circ}C$의 0.9% NaCl에서 실시하였다. 인가전위는 -1500mV에서 1000mV까지 1.67 mV/min의 주사속도로 인가하여 시험을 수행하였으며 분극곡선으로부터 부식전위와 부식전류밀도 및 부동태영역의 전류밀도로 금속의 용출거동을 조사하였으며 부식이 끝난 시편은 FE-SEM과 EDS를 사용하여 조사하였다. 기계적인 특성은 Pd-Ag에 3wt%의 Au를 첨가한 합금이 Pd-Ag에 1.5wt%합금을 첨가한 경우에 비하여 기계적인 특성이 증가하고 내식성이 크게 증가하였다. 이들 합금에 Cu를 11wt%를 첨가한 경우는 비커스경도가 200이상으로 높게 나타났지만 내식성이 크게 감소하였다.