• The Journal of the Korea Contents Association
• /
• v.11 no.3
• /
• pp.293-301
• /
• 2011

The material of the dental prosthesis was required bio-compatibility for biological, chemical, and physical stabilities. This study was conducted the stability evaluation of mechanical, biological characteristics through comparing Co-Cr alloy(SC group), Ti alloy(ST group) made by the selective laser melting method with Co-Cr alloy(CC group), Ni-Cr alloy(CN group) made by the casting method. Modulus of elasticity for mechanical characteristic evaluation was measured by the tensile test. And we conducted the release material analysis using lactic acid-NaCl solution for the evaluation of biological stability and were observed cytotoxicity through the content of this release medium. Taking these results into account, the Co-Cr alloy made by the selective laser melting method was observed modulus of elasticity higher than he Co-Cr alloy made by the casting method. And the Co-Cr alloy made by the selective laser melting method had more superior biological stability than the other groups as the result of cytotoxicity evaluation through the release material analysis. By this results, we think that alloys made by the selective laser melting method can be applied as materials for making the dental prosthesis.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.12
• /
• pp.434-439
• /
• 2020

Selective laser melting (SLM) manufactures an alloy using laser as a heat source, and has recently been introduced in the dental industry. However, there is a lack of analytical research on metal-ceramic restorations achieved by SLM. This study evaluates and compares the metal-ceramic bond strength of Co-Cr alloys produced by selective laser melting and casting methods. Co-Cr samples required for this study were produced through the sintering process of ceramics, by applying the SLM and CAST methods. The metal-ceramic bond strength was measured by applying the shear bond strength test. In order to determine the area fraction of adherent ceramic, Si content of the specimen was measured using scanning electron microscopy SEM/ EDS. Results of the metal-ceramic bond strength and AFAC were analyzed by t-test (α = 0.05). No significant difference was observed comparing the bond strength of SLM and CAST Co-Cr alloys (P> 0.05). However, the SLM group had much better ceramic adherence than the CAST group (P < 0.001). Moreover, oxidation characteristics were similar for both SLM and CAST Co-Cr alloys, but metal structures were different. These results imply that although the bond of ceramic and Co-Cr alloy is not related to the manufacturing method, SLM alloys impart better ceramic adherence. This indicates that alloys made with SLM can be used to fabricate upper implant prostheses in the future. In particular, it is expected to overcome the shortcomings of the CAST method, and save time and cost.

• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.1
• /
• pp.125-142
• /
• 1996

Bond strength of four different cements to dental casting alloys which were treated with #600 emery, tin-plating, and $50{\mu}m$ sandblasting were evaluated. The alloy specimens were Type III Gold alloy(Degulor C), Palladium-Silver alloy(Pors on 4), Nickel-Chromium(Rexillium III) alloy, which were embedded in acrylic resin disc. The specimens were treated with #600 emery and tin plating, #600 emery and sandblasting, then bonded using Fuji I, Ketac Cem(Glass ionomer cements), Poly F, Livcarbo(Polycarboxylate cements). The specimens were immersed in water for 24 hours and shear bond strengths were evaluated by Instron Machine. Tin plated, sandblasted, and debonded alloy surfaces were observed using scanning electron microscope. On the basis of this study, the following conclusions could be drawn. 1. In the tin plated alloy group, increase in bond strength of glass ionomer cements was statistically insignificant. 2. In the tin plated alloy group, increase in bond strength of polycarboxylate cements was statistically significant, except nickel-chromium alloy. 3. Sandblasted alloy group showed higher bond strength than that of tin-plated alloy group.

• The Journal of Korean Academy of Prosthodontics
• /
• v.33 no.3
• /
• pp.584-609
• /
• 1995

The purpose of this study was to evaluate the difference of the galvanic corrosion behaviour of the titanium in contact with gold alloy, silva-palladium alloy, and nickel-chromium alloy using the immersion and electrochemical method. And the effects of galvallit couples between titanium and the dental alloys were assessed for their usefulness as materials for superstructure. The immersion method was performed by measuring the amount of metal elementsreleased by Inductivey coupled plasma emission spectroscopy(ICPES) The specimen of fifteen titanium plates, the five gold alloy, five silver-palladium, five nickel-chromium plates, and twenty acrylic resin plates ware fabricated, and also the specimen of sixty titanium plugs, the thirty gold alloy, thirty silver-palladium, and nickelc-hromium plugs were made. Thereafter, each plug of gold alloy, silver-palladium, and nickel-chromium inserted into the the titanium and acrylic resin plate, and also titanium plug inserted into the acrylic resin plate. The combination specimens uf galvanic couples immersed in 70m1 artificial saliva solution, and also specimens of four type alloy(that is, titanium, gold, silver-palladium and nickel-chromium alloy) plugs were immersed solely in 70m1 artificial sativa solution. The amount of metal elements released was observed during 21 weeks in the interval of each seven week. The electrochemical method was performed using computer-controlled potentiosta(Autostat 251. Sycopel Sicentific Ltd., U.K). The wax patterns(diameter 11.0mm, thickness,in 1.5mm) of four dental casting alloys were casted by centrifugal method and embedded in self-curing acrylic resin to be about $1.0cm^2$ of exposed surface area. Embedded specimens were polished with silicone carbide paper to #2,000, and ultrasonically cleaned. The working electrode is the specimen of four dental casting alloys, the reference electrode is a saturated calmel electrode(SCE) and the ounter electrode is made of platinum plate. In the artificial saliva solution, the potential scanning was carried out starting from-700mV(SCE) TO +1,000mV(SCE) and the scan rate was 75mV/min. Each polarization curve of alloy was recorded automatically on a logrithmic graphic paper by XY recorder. From the polarization curves of each galvanic couple, corrosion potential and corrosion rates, that is, corrosion density were compared and order of corrosion tendency was determined. From the experiments, the following results were obtained : 1. In the case of immersing titanium, gold alloy, silver-palladium alloy, and nickel-chromium alloysolely in the artificial saliva solution(group 1, 2, 3, and 4), the total amount of metal elements released was that group 4 was greater about 2, 3 times than group 3, and about 7.8 times than group 2. In the case of group 1, the amount of titanium released was not found after 8 week(p<0.001). 2. In the case of galvanic couples of titanium in contact with alloy(group 5, 6), the total amount of metal elements released of group 5 and 6 was less than that of group 7, 8, 9, and 10(p<0.05). 3. In the case of galvanic couples of titanium in contact with silver-palladium alloy(group 7, 8), the total amount of metal elements released of group 7 was greater about twice than that of group 5, and that of group 8 was about 14 times than that of group 6(p<0.05). 4. In the case of galvanic couples of titanium in contact with nickel-chromium alloy(group 9, 10), the total amount of metal elements released of group 9 and 10 was greater about 1.8-3.2 times than that of group 7 and 8, and was greater about 4.3~25 times than that of group 5 and 6(p<0.05). 5. In the effect of galvanic corrosion according to the difference of the area ratio of cathode and anode, the total amount of metal elements released was that group 5 was greater about 4 times than group 6, group 8 was greater about twice than group 7, and group 10 was greater about 1.5 times than group 9(p<0.05). 6. In the effect of galvanic corrosion according to the elasped time during 21 week in the interval of each 7 week, the amount of metal elements released was decreased markedly in the case of galvanic couples of the titanium in contact with gold alloy and silver-palladium alloy but the total amount of nickel and beryllium released was not decreased markedly in the case of galvanic couples of the titanium in contact with nickel-chromium alloy(p<0.05). 7. In the case of galvanic couples of titanium in contact with gold alloy, galvanic current was lower than any other galvanic couple. 8. In the case of galvanic couples of titanium in contact with nickel-chromium alloy, galvanic current was highest among other galvanic couples.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.1
• /
• pp.56-61
• /
• 2015

PURPOSE. The purpose of this study was to evaluate the effects of the surface treatment and shape of the dental alloy on the composition of the prosthetic work and its metallic ion release in a corrosive medium after casting. MATERIALS AND METHODS. Orion Argos (Pd-Ag) and Orion Vesta (Pd-Cu) were used to cast two crowns and two disks. One of each was polished while the other was not. Two as-received alloys were also studied making a total of 5 specimens per alloy type. The specimens were submersed for 7 days in a lactic acid/sodium chloride solution (ISO standard 10271) and evaluated for surface structure characterization using SEM/EDAX. The solutions were quantitatively analysed for the presence of metal ions using ICP-MS and the results were statistically analysed with one-way ANOVA and a Tukey post-hoc test. RESULTS. Palladium is released from all specimens studied (range $0.06-7.08{\mu}g{\cdot}cm^{-2}{\cdot}week^{-1}$), with the Pd-Cu alloy releasing the highest amounts. For both types of alloys, ion release of both disk and crown pairs were statistically different from the as-received alloy except for the Pd-Ag polished crown (P>.05). For both alloy type, disk-shaped pairs and unpolished specimens released the highest amounts of Pd ions (range $0.34-7.08{\mu}g{\cdot}cm^{-2}{\cdot}week^{-1}$). Interestingly, in solutions submerged with cast alloys trace amounts of unexpected elements were measured. CONCLUSION. Shape and surface treatment influence ion release from dental alloys; polishing is a determinant factor. The release rate of cast and polished Pd alloys is between $0.06-0.69{\mu}g{\cdot}cm^{-2}{\cdot}week^{-1}$, which is close to or exceeding the EU Nickel Directive 94/27/EC compensated for the molecular mass of Pd ($0.4{\mu}g{\cdot}cm^{-2}{\cdot}week^{-1}$). The composition of the alloy does not represent the element release, therefore we recommend manufacturers to report element release after ISO standard corrosion tests beside the original composition.

• Journal of Periodontal and Implant Science
• /
• v.39 no.4
• /
• pp.385-390
• /
• 2009

Purpose: In this study we evaluated the morphologic aspects of defects created by a piezoelectric ultrasonic scaler with scaler tip on casting gold alloy using scanning electron microscope (SEM) images and defect surface profiles. Methods: 54 blocks of type III casting gold alloy (Firmilay, Jellenko Inc, CA, USA) were scaled by a piezoelectric ultrasonic scaler (P-MAX, Satelec, France) with scaler tip (No. 1 tip) on a sledge device. 2-dimensional profiles of defects on all samples were investigated by a surface profilometer (a-Step 500, KLA-Tencor, CA, USA). The selected working parameters were lateral force (0.5 N, 1.0 N, 2.0 N), mode (P mode, S mode), and power setting (2, 4, 8). SEM images were obtained. Defect surface profiles were made on Microsoft Excel program using data obtained by a surface profilometer. Results: Among P mode samples, there were similarities on defect surface profiles and SEM images regardless of lateral force. The defects created in P mode were narrow and shallow although the depth and the width increased as power setting changed low (2) to high (8). In P mode samples, the defect depth was the greatest when lateral force of 0.5 N was applied. However all the depths were smaller than 1 m. SEM images of Lateral force of 0.5 N, S mode, power setting 2 and 4 were similar to that of P mode, but the other SEM images of S mode showed discernible changes. Defect depth of S mode samples was the greatest when lateral force of 1.0 N was applied. Conclusions: Within the limitations of this study, it can be concoluded that removing capability of piezoelectric scaler with scaler tip becomes maximized as power level becomes higher but the capability is restricted when excessive lateral force is applied on scaler tip.

• Journal of Technologic Dentistry
• /
• v.34 no.3
• /
• pp.237-245
• /
• 2012

Purpose: This study was conducted to evaluate the corrosion resistance of metal ions of alloys and use the results as the dental health data. These were performed by examining the corrosion levels of Co-Cr alloys for the full and removable partial denture metal frameworks and porcelain-fused-to-metal crown, among the dental casting nonprecious alloys. Methods: The alloy specimens (N = 10) were manufactured in $15mm{\times}10mm{\times}1.2mm$ and stored in two types of corrosive solutions at $37^{\circ}C$ for seven days. The metal ions were quantitatively analyzed using the Inductively Coupled Plasma-Atomic Emission Spectrometer. Results: Of the three Co-Cr alloys, the Co ion concentration of the porcelain-fused-to-metal alloy was 1.512 ${\mu}g/cm^2$, which indicated the highest metal ion dissolution. The metal corrosion was higher in the more acidic pH 2.2 solution compared with the pH 4.4 solution. In all three Co-Cr alloys, Co ion dissolution was predominant in the two corrosive solutions. Conclusion: The corrosion resistance of the three Co-Cr alloys was high, indicating a good biocompatibility.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.22 no.3
• /
• pp.203-210
• /
• 2006

Although porcelain fused to metal crowns made from non-precious metal have good mechanical properties, they also have disadvantages such as the poor biological acceptability and the low corrosional resistance. Titanium is used as the alternative metal for porcelain fused to metal crowns, in spite of difficulties in casting. For that reason non-precious alloy including titanium which is easy to cast is currently used. This study evaluated the bond strength between non-precious alloy including titanium and Ni-Cr alloy. $Tilite^{(R)}V$ as non-precious alloy including titanium, $Rexilium^{(R)}V$ as Ni-Cr alloy and $Omega900^{(R)}$ and $Vintage(Regular)^{(R)}$ as porcelain powders were used. The results were as follows. 1. In comparison with the kind of alloy, the bond strength of $Tilite^{(R)}V$ was lower than that of $Rexilium^{(R)}V$. There was no significant difference between two groups. 2. In comparison with the kind of porcelain powder, the bond strength of $Omega900^{(R)}$ was higher than that of $Vintage(Regular)^{(R)}$ in $Tilite^{(R)}V$. There was significant difference between two groups(p < 0.05).

• Journal of Technologic Dentistry
• /
• v.13 no.1
• /
• pp.9-13
• /
• 1991

The purpose of this study was to determine the marginal fit of recasting by used nickel-chromium metal alloys, Hi-Crown, New-Crown and CB-80. Ninety crown prosthetics were divided into eighteen groups according to new to old metal ratios. Each crown was seated on its master die and then the marginal gaps were measured under optical microscope($\times$50). All groups were showed good marginal fit, except group 3 of Hi-Crown(156$\mu$m). The results suggest that the marginal fit of Ni-Cr metal alloy casting bodies were good as without concerned to mixed ratios and metals.

• Korean Journal of Dental Materials
• /
• v.42 no.2
• /
• pp.95-106
• /
• 2015

Hardening mechanism associated with post-firing heat treatment of softening heat treated and then firing simulated Pd-Ag-Au alloy for bonding porcelain was examined by observing the change in hardness, crystal structure and microstructure. By post-firing heat treatment of as-cast, solution treated and pre-firing heat treated specimens at $650^{\circ}C$ after casting, the hardness value increased within 10 minutes. Then, hardness consistently increased until 30 minutes, and gap of hardness value among the specimens was reduced. The increase in hardness after post-firing heat treatment was caused by grain interior precipitation in the matrix. The softening heat treatment did not affect the increase in hardness by post-firing heat treatment. The precipitated phase from the parent Pd-Ag-Au-rich ${\alpha}$ phase with face-centered cubic structure by post-firing heat treatment was $Pd_3$(Sn, In) phase with face-centered tetragonal structure, which has lattice parameters of $a_{200}=4.0907{\AA}$, $c_{002}=3.745{\AA}$. From above results, appropriate post-firing heat treatment in order to support the hardness of Pd-Ag-Au metal substructure was expected to bring positive effects to durability of the prosthesis.