Objectives: The purpose of this study was to compare the microshear bond strength (${\mu}$SBS) and bonding interfaces of two-step total-etching and self-etching adhesive systems to three etch types of dentin either the acid etched, laser etched or laser and acid etched. Materials and Methods: The occlusal dentinal surfaces of thirty human molars were used. They were divided into six groups: group 1, 37% $H_3PO_4$ + Single Bond 2 (3M ESPE); group 2, Er:YAG laser (KEY Laser 3, KaVo) + Single Bond 2; group 3, Er:YAG laser + 37% $H_3PO_4$ + Single Bond 2; group 4, Clearfil SE Primer + Bond (Kuraray); group 5, Er:YAG laser + Clearfil SE Bond; group 6, Er:YAG laser + Clearfil SE Primer + Bond. The samples were subjected to ${\mu}$SBS testing 24 hr after bonding. Also scanning microscopic evaluations were made on the resin-dentin interfaces of six specimens. Results: The ${\mu}$SBS of group 2 was significantly lower than that of groups 1 and 3 in Single Bond 2 (p < 0.05). There were significant differences among the uSBS of groups 4, 5, and 6 in Clearfil SE Bond (p < 0.05). Very short and slender resin tags were observed in groups 2 and 5. Long and slender resin tags and lateral branches of tags were observed in groups 3 and 6. Conclusions: Treatment of dentin surface using phosphoric acid or self-etching primer improved the adhesion of Er:YAG lased dentin.
Purpose: The purpose of this study was to evaluate the validity of reference points for edentulous patient by examining the correlation of teeth and face, and intraoral anatomic landmarks. Materials and methods: We examined a facial outline, length, bizygomatic width, nasion - gnathion length, glabella - nasion distance in 270 men and 280 women satisfied with inclusion criteria from Seoul National School of Dentistry. The shape of maxillary central incisor, mesiodistal crown width and length of maxillary 6 incisors, distance from incisive papilla to labial surface of maxillary central incisor, and perpendicular distance from incisive papilla to intercanine line were measured in the stone model. We analyzed the ratio and relevant relation statistically. Results: The probability on having the same shape of face and the relative same shape maxillary incisor was 55.56% and 46.43% for men and women. The facial length proved to be a more valuable measurement in women in the tooth selection. The ratio of bizygomatic width to mesiodistal width of maxillary central incisor, and the ratio of bizygomatic width to width of maxillary 6 incisors were 16.8 : 1 and 3.0 : 1 and were positively correlated with each other. The distance of the canines from the maxillary incisal papilla was $1.33{\pm}1.28mm$. The distance between the center of the incisal papilla and the labial surface of their maxillary central incisor was $9.23{\pm}1.20mm$. Conclusion: It was showed that anatomical reference points in tooth selection and arrangement for edentulous patient are useful and have validity in our limited study.
Journal of Dental Rehabilitation and Applied Science
/
v.25
no.1
/
pp.13-22
/
2009
The composite resin, due to its esthetic quality, is considered the material of choice for restoration of anterior teeth. To get a satisfactory result in the composite resin restorations, it is necessary to choose right shade. At present, most of the commercial composite resins are based on the Vita Lumin shade guides or shade guides that are provided by their company, but color differences among them might be expected even using the same shade in various materials. This study is to measure color differences between various light-cured composite resins and shade guides and to provide the clinicians with information which may aid in improved color match of esthetic restoration. Four kinds of light-cured composite resins (Gradia Direct (GD), Z250 (Z250), Clearfil AP-X (AP-X), Esthet X (E X)) and shade guides with A2 and A3 shade were used. Three specimens of each material and one specimen of each shade guide were made. Each composite resin was filled into the Teflon mold (1.35 mm depth, 8 mm diameter), followed by compression, polymerization and polishing with wet sandpaper. Shade guides were grinded with polishing stones and rubber points to a thickness of approximately 1.35 mm. Color characteristics were performed with a spectrophotometer(color i5, GretagMacbeth, USA). A computer-controlled spectrophotometer was used to determine CIELAB coordinates ($L^*$, $a^*$, $b^*$) of each specimen and shade guide. The CIELAB measurements made it possible to evaluate the amount of the color difference values (${\Delta}E^*ab$) between composite resins and shade guides. CIE standard D65 was used as the light source. The results were as follows : 1. Among the $L^*$, $a^*$, $b^*$ values of most of 4 kinds of composite resin specimens which are produced by same shade, there were significant differences(p<0.05). 2. Among all 4 kinds of composite resin specimens which are produced by same shade, there were color differences that is perceptible to human eye(${\Delta}E^*>3.3$). 3. Between most of composite resin specimens investigated and their corresponding shade guides, there were color differences that is perceptible to human eye(${\Delta}E^*>3.3$). 4. In the clinical environment, it is recommended that custom shade guides be made from resin material itself for better color matching. Shade guides supplied by manufacturers or Vita Lumin shade guide may not provide clinicians a accurate standard in matching color of composite resins, and there are perceptible color differences in most of products. Therefore, it is recommended that custom shade guides be made from resin material itself and used for better color matching.
Park, So-Ra;Park, Se-Hee;Cho, Kyung-Mo;Kim, Jin-Woo
Journal of Dental Rehabilitation and Applied Science
/
v.30
no.2
/
pp.121-130
/
2014
Purpose: To assess the surface profile of dentinal wall, dentin chips and smear layer during the canal shaping with rotary (ProTaper) and ProFile and reciprocating (WaveOne) nickel-titanium file. Materials and Methods: Sixty human extracted mandibular premolars and incisors with single canals were randomly selected. Three experimental groups (n = 20) were instrumented with ProTaper (F2), ProFile (25/.06), WaveOne (25/.08) with irrigation of 2.5% NaOCl. The dentin chips were collected from flute of file during each canal preparation. After canal preparation, roots were grinded and each group was divided into two subgroups (n = 10) for surface profile and smear layer of dentinal wall of shaped root canal. Each specimen was observed under scanning electron microscope for evaluating size of dentin chips, root canal surface recessions and smear layer. Scores of Smear layer were statistically analyzed using Kruskal Wallis test and Mann Whitney test at P = 0.05 level. Results: The size of dentin chips from ProFile, ProTaper and WaveOne was up to $7{\mu}m$, $6.5{\mu}m$, and$4{\mu}m$, respectively. In the surface profile, the width of surface irregularity was measured and Profile, ProTaper and WaveOne was up to $150{\mu}m$, $70{\mu}m$, and $80{\mu}m$, respectively. Completely cleaned root canals were not found. In the middle and apical third of the canals, WaveOne group showed higher smear layer score than ProFile and ProTaper groups (P < 0.05). Conclusion: Within limits of this study, reciprocating motion WaveOne group was not significant difference of shaping ability with the full-sequence ProFile and ProTaper systems except canal clearness of middle and apical third of root canal. When using WaveOne to shaping root canal, thorough root canal irrigation is recommended.
The ultimate goal of periodontal therapy is the regeneration of periodontal tissue which has been lost due to destructive periodontal disease. To achieve periodontal regeneration, various kinds of methods have been investigated and developed, including guided tissue regeneration and bone graft. Bone graft can be catagorized into autografts, allografts, xenografts, bone substitutes. And materials of all types have different biological activity and the capacity for periodontal regeneration, but ideal graft material has not been developed that fits all the requirement of ideal bone graft material. Recently, bioactive glass that has been utilized in plastic surgery is being investigated for application in dental practice. But, there has not been any long-term assessment of bioactive glass when used in periodontal intrabony defects. The present study evaluates the long-term effects of bioactive glass on the periodontal regeneration in intrabony defects of human and the effect of plaqu control on long term treatment results after dividing patients into those who underwent 3-month regular check-up and those who didn't under go regular check-up The clinical effect on 74sites from 17 infrabony pockets of 11 patients were analyzed 36months after treatment. 51 sites which underwent regular check up were classified as the Follow-up group(F/U group), and 23 sites which did not undergo regular check up were classified as Non Follow-up group(Non F/U group). After comparing the probing depth, attachment loss, bone probing depth before and 36months after treatment, the following results could be concluded. 1. The changes of probing pocket depth showed a statistically significant decrease between after baseline and 36 months after treatment in F/U group(1.79${\pm}$0.68mm) and did no show astatistically significant decrease between after baseline and 36months after treatment in Non F/U group(0.61${\pm}$0.54mm) (P<0.05). 2. The changes of loss of attachment showed a statistically significant decrease between after baseline and 36 months after treatment in F/U group(1.44${\pm}$0.74mm) and did no show astatistically significant decrease between after baseline and 36months after treatment in Non F/U group(1.18${\pm}$1.54) (P<0.05). 3. The changes of bone probing depth showed a statistically significant decrease between after baseline and 36 months after treatment in both F/U(1.35${\pm}$0.28) and Non F/U group(0.78${\pm}$0.55mm) (P<0.05). The results suggest that treatment of infrabony defects with bioactive glass resulted in significan reduction of attachment loss and bone probing depth 36months after the treatment. The use of bioactive glass in infrabony defects, combined with regular check-up and proper plaque control generally shows favorable clinical results. This measn that bioactive glass could be a useful bone substitute.
The major goals of periodontal therapy are the functional regeneration of periodontal supporting structures already destructed by periodontal disease as well as the reduction of signs and symptoms of progressive periodontal disease. There have been many efforts to develop materials and therapeutic methods to promote periodontal wound healing. There have been increasing interest on the chitosan made by chtin. Chitosan is a derivative of chitin made by deacetylation of side chains. Chitosan has been widely studied as bone substitution and membrane material in periodontology. Many experiments using chitosan in various animal models have proven its beneficial effects. Tetracycline has been considered for use in the treatment of chronic periodontal disease and gingivitis. The aim of this study is to evlauate the osteogenesis of tetracycline blended chitosan membranes on the calvarial critical size defect in Sprague Dawley rats. An 8mm surgical defect was produced with a trephine bur in the area of the midsagittal suture. The rats were divided into five groups: Untreated control group versus four experimental group. Four types of membranes were made and comparative study was been done. Two types of non-woven membranes were made by immersing non-woven chitosan into either the tetracycline solution or chitosan-tetracycline solution. Other two types of sponge membranes were fabricated by immersing chitosan sponge into the tetracycline solution, and subsequent freeze-drying. The animals were sacrificed at 2 and 8 weeks after surgical procedure. The specimens were examined by histologic analyses. The results are as follows: 1. Clinically the use of tetracycline blended chitosan membrane showed great healing capacity. 2. The new bone formations of all the experimental group, non-woven and sponge type membranes were greater than those of control group. But, there was no significant difference between the experimental groups. 3. Resorption of chitosan membranes were not shown in any groups at 2 weeks and 8 weeks. These results suggest that the use of tetracycline blended chitosan membrane on the calvarial defects in rats has significant effect on the regeneration of bone tissue in itself. And it implicate that tetracycline blended chitosan membrane might be useful for guided tissue regeneration.
Kim, Seong-Jin;Kim, Moon-Gwan;Park, So-Min;Ban, Jae-Sam;Park, Sang-Won
The Journal of Korean Academy of Prosthodontics
/
v.50
no.4
/
pp.249-257
/
2012
Purpose: This study was designed to help to provide the criteria of the esthetic smile in oromaxillary region on twenties, fifties and sixties. Materials and methods: The facial straight photographs of 33 adults (male 15, female 18, mean age 27.2 years old) and 20 seniors (male 7, female 13, mean age 55.6 years old) in resting and smile position were taken. The measurements and proportion of lip-teeth relation during smile were statistically analyzed, and survey of freshmen and seniors who belong to School of Dentistry, Chonnam National University were taken to select the best esthetic smile among the photographs. Results: In the relationship between the upper lip and the teeth, average smile was the most frequent, and mean of smile line ratio was 1.090 in young group and 0.90 in old group. The correlation between the buccal corridor ratio and exposed teeth count was inversed. At smile, most frequently exposed tooth was the second premolar (63.64%) in young gourp and the first premolar (35.00%) in old group. The correlation between the upper lip change ratio and exposed clinical crown length of maxillary central incisor was inverse, but there was no correlation between the lower lip change ratio and exposed clinical crown length of maxillarycentral incisor. Conclusion: In the result of survey, the students selected the case exposed to the first premolar as the most esthetic smile. The most esthetic smile between full facial photograph and the lip only photograph by the freshmen was different, but that by seniors was identical.
Purpose: The purpose of this study is to compare the removal torque between prefabricated and customized implant abutment screw. Materials and methods: Three types of implant system (Osstem, Astra, Zimmer) were used. For each system, prefabricated abutment screw (control group) and customized abutment screw (test group) were used to connect the fixture and the abutment (n = 6). Digital torque gauze was used to control the tightening torque and the screws were tightened under each manufacturer's recommendation. 10 minutes after the connection the same tightening torque was applied, and 5 minutes after the second connection, the removal torque was measured. This procedure was repeated 10 times. In the cyclic loading test, 10 minutes after the first connection to the 6 groups (n = 3), the same tightening torque was applied, and a total of 1,000,000 time loading was applied at 30 degree angle to long axis with 50 N load. Repeated measures of ANOVA test (${\alpha}$=.05) was used as statistics to evaluate the effect of repeated loading number on the removal torque. Independent t-test was used to evaluate the difference in removal torque after cyclic loading. Results: The removal torque significantly decreased as the number of loading repetition increased (P<.05). In the 10 time repetition test, there was no significant difference between the prefabricated and customized implant abutment screw of the 3 implant system (P<.05). Also in the cyclic loading test, there was no significant difference between the prefabricated and customized implant abutment screw of the 3 implant system (P<.05). Conclusion: Within the limitation of this study, there was no significant difference in the removal torque between the prefabricated abutment screw and customized abutment screws.
Aquaplast Thermoplastic (AT) is a tissue-equivalent oral compensator that has been developed to improve dose uniformity at the common boundary and around the treated area during radiotherapy in patients with head and neck cancer. In order to assess the usefulness of AT, the degree of improvement in dose distribution and physical properties were compared to those of oral compensators made using paraffin, alginate, and putty, which are materials conventionally used in dental imprinting. To assess the physical properties, strength evaluations (compression and drop evaluations) and natural deformation evaluations (volume change over time) were performed; a Gafchromic EBT2 film and a glass dosimeter inserted into a developed phantom for dose verification were used to measure the common boundary dose and the beam profile to assess the dose delivery. When the natural deformation of the oral compensators was assessed over a two-month period, alginate exhibited a maximum of 80% change in volume from moisture evaporation, while the remaining tissue-equivalent properties, including those of AT, showed a change in volume that was less than 3%. In a free-fall test at a height of 1.5 m (repeated 5 times as a strength evaluation), paraffin was easily damaged by the impact, but AT exhibited no damage from the fall. In compressive strength testing, AT was not destroyed even at 8 times the force needed for paraffin. In dose verification using a glass dosimeter, the results showed that in a single test, the tissue-equivalent (about 80 Hounsfield Units [HU]) AT delivered about 4.9% lower surface dose in terms of delivery of an output coefficient (monitor unit), which was 4% lower than putty and exhibited a value of about 1,000 HU or higher during a dose delivery of the same formulation. In addition, when the incident direction of the beam was used as a reference, the uniformity of the dose, as assessed from the beam profile at the boundary after passing through the oral compensators, was 11.41, 3.98, and 4.30 for air, AT, and putty, respectively. The AT oral compensator had a higher strength and lower probability of material transformation than the oral compensators conventionally used as a tissue-equivalent material, and a uniform dose distribution was successfully formed at the boundary and surrounding area including the mouth. It was also possible to deliver a uniformly formulated dose and reduce the skin dose delivery.
This study was conducted to see the effect of TiN ion-plating on the bond strength of orthodontic bracket. Three stainless-steel brackets with different base types were chosen; when TiN ion-plated brackets and non iorrplated brackets were bonded to the teeth, initial and long-term bond strength were measured, The observations oi bonding surface and failure sites through the scanning electron microscope were analysed and compared. The summary of this study was as follows; ${\cdot}$ When TiN ion-plating was not applied, the Micro-Loc type was the highest in bond strength atter 24 hours as $5.89{\pm}1.77$ MPa, followed by $4,27{\pm}1.12MPa$ for Foil Mesh type and $2.64{\pm}0.58MPa$ for Undercut type(P<0.05). ${\cdot}$ Under TiN ion-plating, the bond strength after 24 hours showed: Micro-Loc type $-6.26{\pm}1.51MPa$, Foil Mesh type $-7.45{\pm}2.01MPa$, Undercut type $-2.93{\pm}0.84MPa$. Unlike in the case of non ion-plating, Foil Mesh type showed a higher strength than Micro-Loc type, with Undercut type still showing the lowest bond strength(P<0.05). The bond strength, after 24 hours, increased in case of ion-plated in all 3 types, but a significant increase was shown only in Foil Mesh type(P<0.001). ${\cdot}$ Under a long-term immersion, regardless of ion or non ion-plating, bond strength in general increased over the initial bond strength(one day), with more stability. ${\cdot}$ Through scanning electron microscopic observation of bonding surface, it was found that, regardless of the bracket base type or the application of ion-plating, the resin was thoroughly spreaded into bracket base to form a solid bonding surface between the bracket and the tooth. This was also true in case of a long-term immersion. ${\cdot}$ The scanning electron microscopic observation of failure sites revealed diverse failure patterns.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.