• 한국세라믹학회지
• /
• 제31권10호
• /
• pp.1218-1230
• /
• 1994

In manufacturing process of porous glass-ceramics by the filler method, the sintering behaviour of crystallizable glass powder mixed with various salts was studied and also the effects of precipitated crystal phases on the properties of porous glass-ceramics were investigated. Fine-grained crystallizable glass powder was homogeneously mixed with various slat having grain size 100~200 ${\mu}{\textrm}{m}$ and sintered for densification. After washing out the inorganic salt with distilled water, the porous sintered body was heat treated additionly for crystallization. The MgO-Al2O3-SiO2 base glass was used as crystallizable glass powder and the water soluble salts such as K2SO4 and MgSO4 were used as filler. When K2SO4 was used, leucite crystal phase was formed as a result of the ion exchange and porous glass-ceramics which exhibit high temperature resistance and high thermal expansion coefficient of 17$\times$10-6/$^{\circ}C$ could be obtained. On the contrary, when MgSO4 was used, only slight ion exchange is observed and $\mu$-cordierite and $\alpha$-cordierite crystal phases were formed and porous glass-ceramics which exhibit low thermal expansion coefficient schedule were determined with the results of DTA curves, thermal shrinkage curves and XRD patterns analysis. From DTA curves and thermal shrinkage curves, it was found that the sintering densification have been completed at the temperature range of exothermic peak for crystallization. The pore size distributions and pore diameters were measured by mercury porosimeter. The pore diameter of porous glass-ceramics was 10~15 ${\mu}{\textrm}{m}$ when 100~200${\mu}{\textrm}{m}$ grain size of K2SO4 was used and it was 25~30 ${\mu}{\textrm}{m}$ when the same grain size of MgSO4 was used. The porous glass-ceramics K2SO4 used shows bimodal pore size distribution and its porous skeleton structure was ascertained by SEM observation.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 2000년도 Proceedings of 2000 International Nano Crystals/Ceramics Forum and International Symposium on Intermaterials
• /
• pp.1-33
• /
• 2000

Silicon carbide ceramics with sintering additives from the system AlN-Y$_2$O$_3$ can be gas-pressure sintered to theoretical density. While commonly a combination of sesquioxides is used such as Al$_2$O$_3$-Y$_2$O$_3$, the oxynitrid additives offer the advantage that only a nitrogen atmosphere is require instead of a powder. By starting form a mixture of ${\beta}$-SiC and ${\alpha}$-SiC, and by performing dedicated heat treatments after densification, anisotropic grain growth is obtained which leads to a platelet microstructure showing enhance fracture toughness. In the present work, recent improvement of the mechanical behaviour of these materials at ambient and high temperatures is reported. By means of a surface oxidation treatment in air it is possible to obtain four-point bending strengths in excess of 1 GPa, and the strength retention at high temperatures is significantly improved.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1997년도 Proceedings of the 12th KACG Technical Meeting and the 4th Korea-Japan EMGS (Electronic Materials Growth Symposium)
• /
• pp.13-17
• /
• 1997

The densification of $Al_2$O$_3$/15v/o ZrO$_2$ (Zirconia Toughened Alumina: ZTA) to the 99% of theoretical density was attempted by controlling the processing parameters affecting the each processing step i.e., milling, spray-drying, forming and pressureless sintering. The ZTA processed under the identical conditions showed a large variation in the green and sintered densities, and the mechanical properties. The deviation of 4-point bending strength was more than 100MPa for the ZTA with ~99% of theoretical density. Moreover, the relative green and sintered densities were deviated greatly from the average value. This low reproducibility could be caused by the variation of spray-dried granule properties. Thus, the effect of yield strength and morphology of spray-dried ZTA granule on the green and sintered densities and the mechanical properties needs to be studied in detail. The objective of this work is to fine out the optimum condition of compaction pressure and compaction method depending on the properties of spray-dried granules.

• 한국세라믹학회지
• /
• 제47권6호
• /
• pp.534-539
• /
• 2010

$HfB_2$-HfC composites were prepared by reactive hot pressing using Hf and $B_4C$ at temperatures of 1800 and $1900^{\circ}C$ for 60 min under 32 MPa in an Ar atmosphere. The reaction sequences of the $HfB_2$-HfC composite were studied through series of pressureless heat treatments ranging from 800 to $1600^{\circ}C$. The effect of size reduction of the starting powders on densification was investigated by vibration milling. Fully dense $HfB_2$-HfC composites were obtained by size reduction of the starting powders via vibration milling. The oxidation behaviour of the $HfB_2$-HfC composites at $1500^{\circ}C$ in air showed formation of a non-protective $HfO_2$ scale with linear mass gain. Examination of the mechanical properties showed that particle size reduction via vibration milling also led to improved flexural strength, hardness and fracture toughness.

• Bulletin of the Korean Chemical Society
• /
• 제29권5호
• /
• pp.1038-1042
• /
• 2008

Mono and multilayer TiO2(Fe, $PEG_{600}$) films were deposited by the dip-coating on $SiO_2$/glass substrate using sol-gel method. In an attempt to improve the antibacterial properties of doped $TiO_2$ films, the influence of the iron oxides and polyethilenglycol ($PEG_{600}$) on the morphological, optical, surface chemical composition and biological properties of nanostructured layers was studied. Complementary measurements were performed including Spectroscopic Ellipsometry (SE), Scanning Electron Microscopy (SEM) coupled with the fractal analysis, X-Ray Photoelectron Spectroscopy (XPS) and antibacterial tests. It was found that different concentrations of Fe and $PEG_{600}$ added to coating solution strongly influence the porosity and morphology at nanometric scale related to fractal behaviour and the elemental and chemical states of the surfaces as well. The thermal treatment under oxidative atmosphere leads to films densification and oxides phase stabilization. The antibacterial activity of coatings against Escherichia Coli bacteria was examined by specific antibacterial tests.

• 한국세라믹학회지
• /
• 제20권2호
• /
• pp.99-106
• /
• 1983

This experiment has been carried out for the purpose of investigating the effect of $Ga_2O_3$ and $GeO_2$ additivies on sintering of magnesium oxide over the temperature range of 130$0^{\circ}C$~150$0^{\circ}C$. The effect of calcining temperature on the bulk densities of fired compacts prepared from this material was observed MgO powder has been obtained by calcining extra reagent grade magnesium carbonate(basic fired) at 90$0^{\circ}C$ for 30 minutes $Ga_2O_3$and GeO2 were added in the ratio of 1, 2, and 3 wt% to MgO and mixed with calcined MgO. The specimens were prepared by compression with pressure of $700kg/cm^2$ than fired at 130$0^{\circ}C$~150$0^{\circ}C$ for 0-5hrs. Sintering behaviour and microstructure of the fired specimens were examined. The optimum calcination temperature of magnesium carbonate was 90$0^{\circ}C$. Densification rates obeyed the equation D=K in t+c. Theoretical density in the case of addition of $Ga_2O_3$ was 23.1 kcal/mole in the case of the additive $GeO_2$ was 14.176kcal/mole. This low value would appear to support a machanism of grain boundatry diffusion The range of average grain size in the case of addition of $Ga_2O_3$ and $GeO_2$ was 21$\mu\textrm{m}$-31$\mu\textrm{m}$.