• Korean Journal of Materials Research
• /
• v.13 no.7
• /
• pp.453-459
• /
• 2003

In this paper the effect of interstitial heat treatment on the microstructure and mechanical properties was examined both in the 0.15C-6Mn steels and 0.15C-6Mn steels added with Nb or Ti. This result will be applied into the development of a steel which has the properties of high strength and high ductility resulted from the transformation induced plasticity. The strength-elongation combination was increased as the holding time was increased when the temperature is at $625^{\circ}C$. However, the strength-elongation combination was decreased sharply as the holding time was increased when the temperature is at $675^{\circ}C$. The tensile strength and elongation of a reverse transformed steels added with Ti or Nb was 93 kg/$\textrm{mm}^2$ and 40%, respectively. This steel shows higher strength more than 10% of the 0.15C-6Mn steel without loss of ductility. The autenite formed from the reverse transformed treatment has a fine lath type, which has the width size of 0.1-0.3 $\mu\textrm{m}$. The TRIP sequence normally transforms the austenite to martensite, however, some of the sequence will produce retained austenite \longrightarrow deformation twin \longrightarrow martensite

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.858-868
• /
• 1995

Texture development and martensitic phase transformation, on rolling, are compared in two Hadfield's steels, one having low carbon content(0.65wt% C), the other high carbon content(1.35wt%). In spite of small difference in stacking fault energy(about 2 mJm$^{-2}$ ) between two Hadfield's steels, the differences in texture development are observed. In low carbon steel, the textures developed are similar to those of low stacking fault energy metals in low strain range. However, the abnormal textures such as {111} , {110} <001> are strongly developed at high strain, which are due to the disturbance of u martensite in the development of textures formed at the packets of shear bands or at the grain boundaries. In contrast to low carbon Hadfield's steel( LCHS), the texture development of high carbon Hadfield's steel(HCHS) is simitar to those of low stacking fault energy metals in the whole strain range. This may be due to the fact that the amount of deformation induced martensite was small, as observed by A.C. magnetic susceptibility and iron particle tests.

• Journal of Korea Foundry Society
• /
• v.39 no.6
• /
• pp.110-115
• /
• 2019

Recently, various studies have been conducted on additive manufacturing technology developed using metal materials. In this study, a numerical analysis was introduced to analyze the effects of the thermal deformation and residual stress which arise during the SLM (selective laser melting) manufacturing process. A phase-transformation mechanism is implemented with the use of the Ti-6Al-4V material, in which a solid-state phase transformation (SSPT) can be induced during a numerical analysis. In this case, the phase of the Ti-6Al-4V material changes from a powder to a solid state and then to the Martensite phase in sequence during heating and cooling steps. The numerical analysis during the SLM process was verified by comparing the results of tensile tests with those from the numerical analysis based on the SSPT material properties.