• 한국염색가공학회지
• /
• 제32권2호
• /
• pp.111-120
• /
• 2020

In this study, lignin/chlorinated poly(vinyl chloride)(CPVC) blended fibers have been produced for the development of low-cost carbon fiber. Carbon fiber manufacturing was accomplished through stabilization and carbonization process. The lignin/CPVC blended fibers were prepared by wet spinning method. Dimethylacetamid e(DMAc) and cychlohexanone in a ratio of 5:1(wt%) was employed as co-solvent. The ratio of lignin/CPVC was prepared at 0/10, 1/9, 2/8, 3/7, 4/6, and 5/5(wt%). The spinning solution was extruded at a rate of 0.1 to 0.4ml/min according to the blending ratio. The speed of the rollers was the same for all ratios(draw ratio=1). Analysis of fiber cross-section by scanning eletron microscopy(SEM) showed that as the lignin ratio increased in the same coagulation bath and distilled water, the pore size of the spinning fiber decreased. Therefore, the highest tensile strength of the blending fibers was 6.3±1.2MPa at the 5/5 ratio. The carbon fiber also showed the best tensile strength of 120.78±2.43MPa at 5/5 ratio.

• 한국멀티미디어학회논문지
• /
• 제15권4호
• /
• pp.516-525
• /
• 2012

본 논문에서는 와이미디어(WiMedia) 통신네트워크용 분산협력적 매체접근제어 프로토콜(D-MAC)의 멀티미디어 서비스 QoS를 개선하기 기법을 제안하였다. D-MAC방식은 고속 WPAN시스템에 적용하기 위한 것으로 기존에 제안된 중앙집중적 방식인 IEEE 802.15.3 프로토콜과 달리 모든 디바이스 장치들이 자원을 분산적 예약이 가능하게 하는 방식이다. 본 논문에서는 기존의 WiMedia 프로토콜에서는 채널의 링크 상태 변화를 적절하게 대처하지 못하여 발생하는 멀티미디어 QoS 감소문제를 해결하는 분산협력방식 DMAC 프로토콜 기법을 제안하여 성능을 분석하였다.

• Membrane and Water Treatment
• /
• 제6권5호
• /
• pp.423-437
• /
• 2015

Polyvinylidene fluoride/fullerene nanoparticle (PVDF/$C_{60}$) composite microfiltration (MF) membranes were fabricated by a non-solvent induced phase separation (NIPS) using N, N-dimethylacetamide (DMAc) as solvent and deionized water (DI) as coagulation solution. Polyvinylpyrrolidone (PVP) was added to the casting solution to form membrane pores. $C_{60}$ was added in increments of 0.2% from 0.0% to 1.0% to produce six different membrane types: one pristine PVDF membrane type with no $C_{60}$ added as control, and five composite membrane types with varying $C_{60}$ concentrations of 0.2, 0.4, 0.6, 0.8 and 1.0%, respectively. The mechanical strength, morphology, pore size and distribution, hydrophilicity, surface property, permeation performance, and fouling resistance of the six membranes types were characterized using respective analytical methods. The results indicate that membranes containing $C_{60}$ have higher surface porosity and pore density than the pristine membrane. The presence of numerous pores on the membrane caused weaker mechanical strength, but the water flux of the composite membranes increased in spite of their smaller size. Initial flux and surface roughness reached the maximum point among the composite membranes when the $C_{60}$ concentration was 0.6 wt.%.

• 분석과학
• /
• 제27권6호
• /
• pp.339-346
• /
• 2014

근로자 건강진단 실무지침 상의 필수 검사항목 항목 중, N-메틸아세트아미드의 소변 표준시료를 제조하여 그 신뢰도를 확인하고자 하였다. DB-624 컬럼을 사용한 GC/MSD 분석 방법에 의해 기존 분석 컬럼보다 우수한 분리능과 선택성으로 N-메틸아세트아미드를 분석하였다. -60, -20, 5, $25^{\circ}C$에서 5-50 mg/L의 농도 범위의 소변 중 N-메틸아세트아미드의 안정성을 6개월 보관 시점까지 검토한 결과 모든 보관 조건에서 안정하였으며, 각 시료에 대한 균질성 검사 결과도 양호하였다. 이상의 결과로부터 유리형 NMAC를 첨가하는 방법으로 제조한 소변 중 NMAC 표준시료가 분석정도관리용으로 실용화하기에 적합한 균질성과 장기간 보관 시의 안정성을 모두 만족시킴을 확인하였고, 2008년부터 분석정도관리 표준시료로 활용하였다.

• 공업화학
• /
• 제23권3호
• /
• pp.266-270
• /
• 2012

무수물인 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA)에 2,2'-bis(trifluoromethyl)benzidine (TFB), 2,2'-bis(3-aminophenyl)hexafluoropropane (BAFP), 2,2'-bis(3-amino-4-methylphenyl)hexafluoropropane (BAMF), bis(3-aminophenyl) sulfone (APS), p-xylyenediamine (p-XDA), 및 m-xylyenediamine (m-XDA) 등 6종류의 각각 다른 아민 단량체를 이용하여 폴리이미드(PI) 필름을 제조하였다. 얻어진 무색 투명한 PI필름은 무수물과 아민을 반응시켜 폴리아믹산(PAA)을 합성한 후, 용액 캐스팅에 의한 열처리 과정을 통해 얻었다. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), thermo-mechanical analysis (TMA)를 이용하여 열적 성질을 측정하였고, universal tensile machine (UTM)을 이용하여 기계적 성질을 조사하였으며, 자외선/가시광선 분광광도계(UV-vis.)와 색차계를 이용하여 광학적 성질을 각각 확인하였다. 제조된 모든 필름들은 무색 투명하여 0.98~2.76 사이의 노란색 지수를 보였으며, 25.73~55.23 $ppm/^{\circ}C$사이의 열 팽창 계수를 나타냈다.

• Macromolecular Research
• /
• 제11권4호
• /
• pp.260-266
• /
• 2003

Ethylene vinyl acetate (EVA)/clay nanocomposites were synthesized by blending a solution of ethylene vinyl acetate copolymer containing 12% vinyl acetate abbreviated as EVA-12 in toluene and dispersion of dodecyl ammonium ion intercalated montmorillonite (l2Me-MMT) in N,N-dimethyl acetamide (DMAc). X-ray patterns of sodium montmorillonite ($Na^+$-MMT) and 12Me-MMT exhibited $d_{001}$ peak at $2{\theta}=7.4^{\circ}$ and $2{\theta}=5.6^{\circ}$ respectively; that is, the interlayer spacing of MMT increased by about 0.39 nm due to intercalation of dodecyl ammonium ions. The XRD trace of EVA showed no peak in the angular range of $3-10^{\circ}(2{\theta})$. In the XRD patterns of EVA/clay hybrids with clay content up to 6 wt% the basal reflection peak of 12Me-MMT was absent. leading to the formation of delaminated configuration of the composites. When the 12Me-MMT content was 8 wt% in the EVA-12 matrix, the hybrid revealed a peak at about $2{\theta}=5.6^{\circ}$, owing to the aggregation of aluminosilicate layers. Transmission electron microscopic photograph exhibited that an average size of 12-15 nm clay layers were randomly and homogeneously dispersed in the polymer matrix, which led to the formation of nanocomposite with delaminated configuration. The formation of delaminated nanocomposites was manifested through the enhancement of mechanical properties and thermal stability, e.g. tensile strength of an hybrid containing only 2 wt% 12Me-MMT was enhanced by about 36% as compared with neat EVA-12.

• Macromolecular Research
• /
• 제16권8호
• /
• pp.717-724
• /
• 2008

In this study, we prepared all-trans retinoic acid (ATRA)-encapsulated, surfactant-free, PLGA nanoparticles. The nanoparticles were formed by nanoprecipitation process, after which the solvent was removed by solvent evaporation or dialysis method. When a nanoparticle was prepared by the nanoprecipitation - solvent evaporation method, the nanoparticles were bigger than the nanoparticles of the nanoprecipitation - dialysis method, despite the higher although loading efficiency. Nanoparticles from the nanoprecipitation - dialysis method were smaller than 200 nm in diameter, while the loading efficiency was not significantly changed. Especially, nanoparticles prepared from DMAc, 1,4-dioxane, and DMF had a diameter of less than 100 nm. In the transmission electron microscopy (TEM) observations, all of the nanoparticles showed spherical shapes. The loading efficiency of ATRA was higher than 90% (w/w) at all formulations with exception of THF. The drug content was increased with increasing drug-feeding amount while the loading efficiency was decreased. In the drug release study, an initial burst was observed for $2{\sim}6$ days according to the variations of the formulation, after which the drug was continuously released over one month. Nanoparticles from the nanoprecipitation - dialysis method showed faster drug release than those from the nanoprecipitation - solvent evaporation method. The decreased drug release kinetics was observed at lower drug contents. In the tumor cell cytotoxicity test, ATRA-encapsulated, surfactant-free, PLGA nanoparticles exhibited similar cytotoxicity with that of ATRA itself.

• Macromolecular Research
• /
• 제16권3호
• /
• pp.212-217
• /
• 2008

PVDF ($Kynar^{(R)}$ 761) nanofibers were made by electrospinning with an external voltage of 6-10 kV, a traveling distance of 7-15 cm and a flow rate of 0.4-1 mL/h. Although the mean diameter of the fibers has not changed significantly, the conditions affected the change in diameter distribution. This was attributed to interactions, both attraction and repulsion, between the positive charges on the polymer solutions and the electrically grounded collector. Higher voltages and traveling distance increased the level of attraction between the positive charge on the polymer solution and the electrically grounded collector, resulting in a narrow diameter distribution, In addition, a high flow rate allowed a high population of uniformly charged solutions to travel to the grounded collector, which resulted in a narrow diameter distribution. The optimum conditions for electrospinning of PVDF in DMAc/acetone (3/7 by wt) were a collector voltage of 6 kV, a syringe tip to collector of 7 cm, a flux rate of 0.4 mL/h and 10 kV, 10 cm, 1 mL/h, Since PVDF is widely used as a filtration membrane, it was electrospun on a PET support with a rotating drum as a grounded collector. Surprisingly, some straight nanofibers were separated from the randomly deposited nanofibers. The straight nanofiber area was transparent, while the randomly deposited nanofiber area was opaque. Both straight nanofibers and aligned nanotibers could be obtained by manipulating the PET drum collector. These phenomena were not observed when the support was changed to an Al sheet. This suggests that a pseudo dual collector was generated on the PET sheet. No negative charge was created because the PET sheet was not a conductive material. However, less charge was created when the sheet was not perfectly attached to the metal drum. Hence, the nanotibers jumped from one grounded site to the nearest one, yielding a straight nanofiber.

• Advances in materials Research
• /
• 제13권3호
• /
• pp.243-251
• /
• 2024

The asymmetric polylactic acid (PLA) membrane was prepared via phase inversion method using non-solvent induced separation (NIPS) technique. This study aims to synthesized as well as to characterize the PLA membrane and evaluating the membrane performance on water flux and permeability. In addition, this research also studied the removal performance of methylene blue dye. The polymer solution has been prepared using 12 wt.% of PLA and dissolved in 88 wt.% of Dimethylacetamide (DMAc) as a solvent. Then, the cast film was immersed in different ratio of coagulant bath medium (distilled water: methanol: ethanol) ranging from 100:0:0, 75:25:0, 75:0:25 and 75:12.5:12.5, respectively). Several characterizations were performed which include, membrane contact angle and membrane porosity. Performance PLA membranes were determined in terms of water flux and permeability at 1 bar transmembrane pressure using dead-end permeation cell. Finally, methylene blue (MB) removal efficiency was tested at the same transmembrane pressure. The findings revealed that the increase of alcohol concentration in coagulant bath resulted in higher porosity and lower contact angle. In short, MB dye rejection efficiency is also closely related to the amount of alcohol ratio used in coagulant baths. Increases in concentration of methanol and ethanol in coagulant bath medium increases the membrane porosity thus increased in efficiency of methylene blue rejection.

• 공업화학
• /
• 제9권2호
• /
• pp.207-213
• /
• 1998

전편의 연구결과[1]를 토대로 또 다른 방법으로써 폴리이미드의 구조를 변화시켜 방향족 폴리벤즈이미다졸(PBI)과의 블렌드들의 상용성 및 상용성을 가져다 주는 상호작용의 세기를 상대적으로 비교하였다. 이 연구에서 방향족 폴리이미드(PI)는 두 개의 디아민인 4,4'-methylene dianiline (4,4'-MDA)과 4,4'-oxydianiline (4,4'-ODA)을 dianhydride인 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride (DSDA)와의 축합반응을 통하여 용매인 DMAc로 폴리아믹산(PAA)을 합성한 후 열경화하여 얻었다. 이들 폴리아믹산(PAA)을 poly2,2-(m-phenylene)-5,5'-bibenzimidazole (PBI)와 용액 블렌딩하여 PBI/PAA 블렌드를 열경화시켜 PBI/PI의 블렌드로 전환시킨후 상용성을 조사하고 전편의 블렌드에 사용된 폴리이미드[1]와 이 연구에 사용된 폴리이미드의 구조변화에 대한 상호작용의 상대적인 크기를 조사하였다. 연구에 사용된 두 가지 블렌드인 PBI/DSDA+4.4'-MDA (Blend-V)와 PBI/DSDA+4.4'-ODA (Blend-VI)는 사용성을 보였다. 이는 성현된 필름이 투명하고, 전 블렌드 조성에 대해서 하나의 $T_g$를 가지며, 또한 블렌드 조성에 따른 N-H ($3418cm^{-1}$)와 C=O 스트레칭 밴드(1730 및 $1780cm^{-1}$)의 주파수 이동폭이 각각 $39{\sim}40cm^{-1}$, $5{\sim}6cm^{-1}$와 $3{\sim}4cm^{-1}$이었다. 이 연구에 사용된 블렌드들에 대하여 두 성분 고분자간 상호작용의 세기를 실험치와 Fox식으로 계산된 유리전이온도차로 생긴 면적(A), Gordon-Taylor 식에서의 ${\kappa}$ 값, 그리고 관능기인 N-H와 카보닐기의 주파수 이동폭의 변화로 살펴보았다. 이들에 대한 결과로 먼저, 면적 (A)와 ${\kappa}$ 값에 있어서 Blend-V와 Blend-VI이 전편의 블렌드 [1]인 Blend-III와 Blend-IV에 비해 작은 값을 보였다. 또한 관능기의 주파수 이동에 있어서도 이에 대한 결과와 유사한 결과를 보였다. 따라서 블렌드에 사용된 PI의 구조변화에 따라 상호작용이 다른 것은 PI 합성시에 사용된 서로 다른 dianhydride의 구조에서 페닐링 사이에 존재하는 linkage인 C=O보다 $SO_2$가 존재할 때[Fig. 2] 블렌드를 이루는 두 고분자사이의 상호작용인 수소결합력을 약화시키는 spacer로 작용한 것으로 사료된다. 다시 말하면, 전자가 후자보다 더 큰 입체장애를 일으켰기 때문이라 사려된다.