• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.165-166
• /
• 2002

Hydrogen free diamond like carbon (DLC) films were prepared on steel substrates by using a single ion beam in a configuration that allowed sputtering of a graphite target and at the same time allowed to impact the substrate at a grazing angle. The DLC films so prepared have improved properties with increased disorder and with modest hardness that is slightly higher than previously reported values. We have studied the effects of $N_2^+$ ions implantation on such films. It is found that the implantations of nitrogen ions into DLC films lead to chemical modifications that allowed N atoms to be incorporated into the carbon network to produce a nitrogenated DLC. Nano-indentation experiments indicated that the nitrogenated films have consistently higher hardnesses ranging from 30 to 45GPa, which represents a considerable increase in surface hardness, compared with non-nitrogenated precursor films. The investigations by XPS and Raman spectroscopy suggests that the $N_2^+$ implanted DLCs had undergone both chemical and structural modifications through the incorporation of N atoms and the increased ratio of $sp^3/sp^2$ type bonding. The observed high hardness was therefore attributable to these structural and chemical modifications. This result has implication for the preparation of super hard wear resistant films required for tribological functions in devices.

• Tribology and Lubricants
• /
• 제11권5호
• /
• pp.59-65
• /
• 1995

Tribological behaviors of nitrogen incorporated amorphous diamond-like carbon films were experimentally measured under a vacuum ($3 \times 10^{-5}$ Torr) using a ball (AISI 52100 steel)-on-disk wear-rig. Nitrogen incorporated DLC films were deposited by r.f. plasma assisted chemical vapor deposition method. Mixtures of benzene and ammonia or nitrogen gases were used as the reaction gases for the r.f. PACVD, and Si (100) wafer was used as the substrate. In the tribo-test, effects of DLC film thickness and normal load in friction were measured and discussed. Results showed that friction of nitrogen incorporated DLC films from a mixture gas of benzene and ammonia was lower than that of 100% benzene, specially in the measurement of minimum coefficient of friction. Differences in frictional characteristics of nitrogen incorporated DLC films were explained with the changes in chemical structures of the films. Result also showed that friction of DLC films increased with the sliding contact cycle, which remarkably accompanied with roll-shaped wear debris. Mechanisms and roles of the polymer-like wear debris were presented and discussed.

• 한국광학회지
• /
• 제8권4호
• /
• pp.277-282
• /
• 1997

광학소자나 전자소자의 코팅에 많이 이용되고 있는 Diamond-like Carbon(DLC) 박막의 복소굴절율을 광학적 방법을 사용하여 구하였다. PECVD(Plasma enhanced CVD)법에 의해 Si(100)기판과 비정질실리카 기판위에 각각 성장시킨 DLC 박막을 분광타원해석기와 분광광도계를 이용하여 타원해석 스펙트럼과 광투과율 스펙트럼을 측정하고, Sellmeier 분산관계식과 양자역학적 진동자 모델을 이용하여 분석하였다. 비정질실리카 위에 증착된 DLC 박막의 광투과영역에서 분광타원해석분석으로 굴절률 및 박막의 유효두께를 구하고 광흡수영역에서 투과스펙트럼을 역방계산하여 소광계수를 구한 뒤, 이 소광계수 스펙트럼에 최적 근사하는 양자역학적 분산식의 계수들을 회귀분석법으로 결정하여 복소굴절율을 구하였다. 그리고 모델링방법을 타워해석 스펙트럼에 적용하여 Si기판과 비정질이산화규소 기판위에 증착된 DLC 박막의 조밀도, 표면거칠기 등 박막상수를 박막의 성장조건에 따라 분석하였다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 추계학술대회 논문집 학회본부
• /
• pp.683-687
• /
• 1997

The purpose of this work is to develop a highly reliable solar cell based on the diamond-like carbon(DLC)/silicon heterojunction. Thin films of DLC have been deposited by employing both filtered cathodic vacuum arc(FCVA) and magnetron plasma-enhanced chemical vapor deposition(m-PECVD) systems. Structural, electrical, and optical properties of DLC films deposited are systematically analyzed as a function of deposition conditions, such as magnetic field, substrate bias voltage, gas pressure, and nitrogen content. The I-V measurement has been used to elucidate the mechanism responsible for the conduction process in the DLC/Si junction. Photoresponse characteristics of the junction are measured and its reliability against temperature and light stresses is also analyzed.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2000년도 하계학술대회 논문집 C
• /
• pp.1717-1719
• /
• 2000

DLC films are deposited by using an FCVA deposition system with a mirror-type magnetic field configuration. Permanent magnets and: magnetic yokes around the cathode have been observed to enhance the mobility of arc spots on the cathode and the stability of arc plasma, Effects of reactor pressures and substrate biases on structural properties of DLC films deposited are investigated. The results show that the highest $sp^{3}/sp^{2}$ fraction is obtained when the films are deposited at a pressure of $3{\times}10^4$ Torr and a bias voltage of - 50 V. The variation of the structural properties due to thermal stress up to 500$^{\circ}C$ is also examined.

• 한국분말재료학회지
• /
• 제17권6호
• /
• pp.456-463
• /
• 2010

This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM, nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and $1.14\;{\mu}m$. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.

• 전자공학회논문지
• /
• 제52권5호
• /
• pp.197-205
• /
• 2015

함정용 전자광학추적장비 열영상센서부 전면창의 신뢰성 및 성능 개선을 위해 플라즈마 화학기상증착법을 통해 제작되는 DLC 박막을 제안하였다. DLC 박막은 현재 사용되고 있는 실리콘 박막과 비교하여 뛰어난 강도와 낮은 마찰, 화학적 안정성이 우수하며 이로 인해 해상 환경에서 필연적으로 발생하는 열영상센서 전면창의 표면 박리를 최소화할 수 있는 장점이 있다. 본 실험을 통해, DLC 박막이 갖는 물리적 특성을 바탕으로 다양한 전자광학장비에 적용이 가능함을 확인하였다.

• The Korean Journal of Ceramics
• /
• 제3권2호
• /
• pp.88-91
• /
• 1997

The diamondlike (DLC) films were deposited by RF plasma CVD system which had cathode consisting of mesh sheet, for the purpose of a protection from wear of OPC surface of the electrophotographic photosensitive body. Material charateristics and tribological properties of the films were also investigated and finally copying performance was evaluated with DLC deposited OPC samples. The surface resistance of the DLC film unaffected by the surface potential of the OPC was about $10^{11}{\Omega}$ and its hardness was about 1200 kg/$\textrm{mm}^2$. In this case the film showed typical material strcture of dimondlike hydrocarbon. The friction coefficient of the film was lowered to 0.2~0.3 at the optimum condition in this investigation and their wear resistant was inproved by DLC-deposition on the OPC surface. DLC-deposited OPC samples with a good copying performance without image flow and draft could be obtained at some depositing conditions.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 C
• /
• pp.1663-1664
• /
• 2006

Carbon films was grown on Si substrates using the method of electrolysis for methanol liquid. Deposition parameters for the growth of the carbon films were current density for the electrolysis, methanol liquid temperature and electrode spacing between anode and cathode. We examined electrical resistance and the surface morphology of carbon films formed under various conditions specified by deposition parameters. It was clarified that the high electrical resistance carbon films with smooth surface morphology are grown when a distance between the electrodes was relatively wider. We found that the electrical resistance in the films was independent of both current density and methanol liquid temperature for electrolysis. The temperature dependence of the electrical resistance in the low resistance carbon films was different from one obtained in graphite.

• 한국진공학회지
• /
• 제10권4호
• /
• pp.387-395
• /
• 2001

증착 조건에 따라 나타나는 폴리머상, 경질, 흑연상의 다이아몬드상 카본(DLC) 박막에서 두께 감소에 따른 탄성률의 변화거동을 구조적인 관점에서 살펴보았다. 실험에 사용된 박막은 r.f.-PACVD 장비를 이용하여 증착하였으며, 반응 가스로는 벤젠과 메탄을 사용하였다. 기판을 식각 과정을 통해 완전히 제거시켜 주기 때문에 다른 방법들과는 달리 기판의 영향 없이 박막만의 탄성률을 정확히 측정할 수 있는 free overhang 방법을 이용하여 DLC 박막의 biaxial elastic modulus를 측정하였다. 또한 Raman 분석을 이용하여 박막의 구조를 조사하였다. 박막이 폴리머상 혹은 흑연상인 경우 두께가 감소함에 따라 탄성률이 감소하는 것을 확인하였고, Ramanm spectrum의 G-peak 위치를 분석한 결과 그 원인은 폴리머상인 경우 증착 초기에 낮은 물성을 가지는 폴리머상의 박막이 형성되기 때문이며, 흑연상인 경우 증착 초기에 낮은 물성을 가지는 흑연상의 박막이 증착되기 때문이다. 반면에 경질의 박막에서는 두께에 상관없이 일정한 탄성률을 가지고 있었으며, 두께에 따른 박막의 구조적인 변화도 관찰되지 않았다.