• Elastomers and Composites
• /
• v.41 no.3
• /
• pp.182-193
• /
• 2006

The retardation effects of a new polymeric UV stabilizer, DGEBA-HALS, on the UV degradation of SBR and NR were investigated in this study. The UV degradation behaviors of three different rubber compounds, without any photostabilizer and with commercial Cyabsorb UV-3529 and DGEBA-HALS, were compared. Also, the physical characteristics such as Young's modulus, tensile strength, blow-off deformation and crosslink density were examined. The Young's modulus was increased by UV irradiation for all samples, and the tensile strength, after UV irradiation, of the compound with UV stabilizer was better than that of the compound without stabilizer. Especially, the tensile strength of UV irradiated NR was improved by adding DGEBA-HALS. The results of blow-off deformation were in accord with those of Young's modulus. The degree of transmission of SBR compounds obtained from UV-vis transmission spectra was improved about 4% by adding the UV stabilizer. Commercial Cyabsorb UJV-3529 and DGEBA-HALS showed similar trends of transmission. The SEM photographs of SBR surface showed that the size of cracks created by UV irradiation became smaller by adding UV stabilizer. In particular, it is observed that the stabilization effect of DGEBA-HALS was better than that of commercial Cyabsorb UV-3529.