• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.415-423
• /
• 2016

Cylindrical laminated veneer lumber (LVL) is produced by winding the veneer tape on a circular cylinder. The veneer tape was produced by cutting the veneer into a rectangular shape and sewing it in a vertical direction to the fiber. The tensile strength test was carried out by producing the veneer tape specimen with different species of veneer, types and combinations of sewing yarn. The Radiata pine veneer tape produced with three sewing lines using the reinforced sewing thread had the best tensile strength. Also, the separation and snapping problems of the veneer tape were improved, resulting in the improvement in the workability of cylindrical LVL. The bending strength of various cylindrical LVL produced with different types of veneer tape and a different number of lamination layers and the application of reinforcement with glass fiber cloth was compared with that of Larix log. Bending MOR of cylindrical LVL reinforced with glass fiber cloth at the volume ratio of 11% was improved by 65% in comparison to the non-reinforced cylindrical LVL. In the case of the cylindrical LVL produced with 2 sewing lines of veneer tape, a fracture occurred at the butt joint between the veneer tapes. However, in the case of the cylindrical LVL produced with 3 sewing lines of veneer tape a fracture occurred in the fiber direction.

• Journal of the Korean Wood Science and Technology
• /
• v.40 no.6
• /
• pp.418-423
• /
• 2012

In order to develop the end use of cylindrical laminated veneer lumber (LVL) such as wooden crafts, the water proof-bonding strength, the resistance to abrasion and the surface hardness by painting the surface of LVL were investigated. The study results were as follows; The water proof-bonding strength through 5 cyclic test by boiling in water immersion and drying were favorable without delamination of glue line. Then the formulation of glue was resorcinol resin (100) to hardener of paraformaldehyde (5) by mixed weight percentage. The resistance to abrasion was relatively higher at cross section than tangential section. When tangential section of LVL was painted by UV protection oil, the resistance to abrasion was improved. In case of an cross section of LVL, the higher surface hardness appeared at larch core than radiata pine LVL. Also, in case of an tangential section of LVL, the higher surface hardness appeared at glue line than veneer side.

• Journal of the Korea Furniture Society
• /
• v.23 no.4
• /
• pp.407-414
• /
• 2012

In order to develop the end use of cylindrical laminated veneer lumber (LVL) such as wooden crafts, the light resistance properties of natural dye-colored and finished cylindrical LVL was investigated. The study results were as follows; The cross section of LVL showed the higher light resistance than its tangential section, and the light resistance also increased with surface coated. On the other hand, LVL specimen were colored by 9 natural dyes of amur cork-tree etc., and the natural and apparent hue harmonized with wood was found after coating and light resistance test. Particularly, The dyes extracted from amur cork-tree, persimon and sappan wood showed orange color, reddish brown and red color respectively, giving an accenting effect to original wood color.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.3
• /
• pp.282-289
• /
• 2014

After being laminated with a combination of glass fiber reinforced plastic and plywood, the GFRP laminated plate was densificated for 1 hour at $150^{\circ}C$ with pressure of $1.96N/mm^2$. A partial reinforced beam was produced by attaching the 5 GFRP laminated plates to the joint of glulam and the column. In addition, the column to beam joint was produced by using reinforced laminated wooden pin which was made of GFRP sheet and plywood, fiber glass reinforced cylindrical-LVL column. The joint was made of round log, glulam and drift pin as the reference specimen, and its moment resistance was evaluated. As a result, the strength performance of specimens with partial reinforced beams were 1.8 times stronger than the reference specimen on average. Furthermore, rupture was neither occurred on partial reinforced beam nor column. Toughness and stiffness of joints were also fine. The GFRP sheet reinforced laminated plate showed better reinforcement effect than GFRP textile reinforced one. GFRP sheet was inserted into each layer of laminate, and it showed good condition in rotation-angle and strength, therefore it is the most appropriate to reinforce the part of the beam.