• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.767-777
• /
• 2021

This study analyzed the microstructures and chemical composition of three samples of bronze mirrors excavated in the Jeollanam-do region, particularly Goheung and Damyang. Under x-ray irradiation, the analysis results confirmed the broken parts and pores caused by cracks, casting, and corrosion. Major and minor elemental analysis were performed on three mirrors by Scanning electron microscopy (SEM) with Energy dispersive x-ray spectrometry (EDS) and Inductively coupled plasma mass spe ctrome try (ICP-MS). The re sult shows that the bronze mirrors containe d Cu-Sn-Pb alloys. Alpha phase and eutectic phase were observed in the microstructure, confirming that the casting was performed without additional heat treatment. Notably, Three bronze mirrors were made early Three Kingdoms period in Korea.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.143-148
• /
• 2010

A bronze dagger excavated from the historical site at Bongili in Gyeongju was examined for its microstructure and chemical compositions. The results show that it was forged out of the Cu-10 weight % Sn alloy having no lead. The application of forging in fabrication and the use of an unleaded alloy distinguish this artifact from other bronze daggers that have been reported in Korea, the majority of which were cast from leaded Cu-Sn alloys. This dagger is a rare and valuable archaeological material suggesting a unique bronze technology practiced in ancient Gyeongju area.

• Journal of Applied Reliability
• /
• v.13 no.2
• /
• pp.109-116
• /
• 2013

The solder is any of various fusible alloys, usually tin and lead, used to join metallic parts that provide the contact between the chip package and the printed circuit board. Solder plays an important role of electrical signals to communicate between the two components. In this study, two kinds of Ag-free solder as sample is made to conduct the thermal shock test and the high humidity temperature test. Low resistance is measured to estimate crack size of solder, using daisy chain. The low speed shear test is also performed to analyze strength of solder. The appropriate degradation model is estimated using the result data. Depending on the composition of solder, lifetime estimation is conducted by adopted degradation model. The lifetime estimated two kinds of Ag-free solder is compared with expected lifetime of Sn-Ag-Cu solder. The result is that both Ag-free composition are more reliable than Sn-Ag-Cu solder.

• Korean Journal of Heritage: History & Science
• /
• v.37
• /
• pp.267-284
• /
• 2004

As an initial step to understand the transitions in Korean bronze technology the present study has examined metallurgical microstructures of 8 artifacts excavated from the Silla Wang-Gyong site in Kyongju. Important trends have been found in alloy compositions and also in manufacturing processes. In the design of alloys, the Sn content was apparently changing toward the peritectic point, 22 mass %, of the Cu-Sn phase diagram while the Pb addition was intentionally avoided. This trend in composition was found accompanied by the introduction, subsequent to casting, of such special thermo-mechanical treatments as quenching and forging in artifact manufacture. In addition, the Sn content in alloys containing a significant amount of As was relatively low and no evidence of forging was observed in them. The use of quenching and forging and the rejection of Pb and As from alloys are all necessary requirements if the brittle nature of high Sn alloys is to be overcome in bronze working. This paper will show that the Wang-Gyong era corresponds to that of innovations leading to the technical climax in Korean bronze tradition, which has been maintained up to the present.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.79-79
• /
• 2010

저온용 무연 솔더의 대표 조성으로 고려되고 있는 Sn-58Bi(융점: $138^{\circ}C$) 공정(eutectic) 조성은 우수한 강도에도 불구하고 연성(ductility) 측면에서의 문제점이 지속적으로 보고되고 있다. 따라서 이 합금계의 연성을 최대로 개선시킬 수 있으면서도 실제 상용화가 가능한 합금 조성의 개발 연구가 요청된다. 본 연구에서는 Sn-Bi 2원계 조성에서 최대의 연성을 나타내는 것으로 보고된 Sn-40Bi 조성에 미량의 합금원소를 첨가함으로써 최대의 연성을 확보하는 한편, 그 연성 특성이 변형속도에 어느 정도 민감한지를 인장 실험을 통해 결정하고자 하였다. 합금원소로는 0.1~0.5 wt%의 Ag, Mn, In, Cu를 선택하였으며, 인장 시편을 제조하여 $10^{-2}$, $10^{-3}$, $10^{-4}\;s^{-1}$의 3종류로 변형속도를 변형시켜가며 응력-변형 곡선(stress-strain curve)을 측정하였고, 조성별, 변형속도별로 최대인장강도(ultimate tensile stress, UTS) 및 연신율 결과들을 정리하였다. 합금원소를 첨가한 조성의 경우는 모든 시험 조건에서 Sn-40Bi보다 우수한 연신률을 나타내는 것으로 측정되었으나, $10^{-2}\;s^{-1}$의 빠른 변형속도에서는 그 향상 정도가 상대적으로 감소하는 경향이 관찰되었다. 특히 Sn-40Bi-0.5Ag 조성의 경우 느린 변형속도에서 특히 눈에 띄는 연신률 값을 나타내며, 모든 변형속도 조건에서 가장 우수한 연성을 나타내었다. 한편 Sn-40Bi-0.1Cu 조성의 경우 변형속도에 따른 연신률의 변화 정도, 즉, 변형속도에 따른 연신률의 민감도가 매우 커 $10^{-4}\;s^{-1}$ 속도에서는 Sn-40Bi-0.5Ag에 버금가는 연신률 값이 측정되었으나, $10^{-2}\;s^{-1}$ 속도에서는 가장 나쁜 연신률 특성을 보여주었다. Sn-40Bi-0.2Mn 조성은 최고의 연신률 향상 특성을 나타내지는 않았으나, In을 첨가한 경우보다는 대체적으로 우수한 연성을 나타내었다. 이상의 각 합금별 연성 특성은 인장시험 전의 미세조직 관찰 결과와 인장시험 후 파면부의 조직변화 관찰 결과로부터 해석되었다. 그 결과 석출상의 형성 여부, 인장 시험 중 재결정 조직의 형성 여부, 라멜라(lamellar) 조직의 분율과 라멜라 간격(lamellar spacing)의 정도 또는 $\beta$-Sn과 라멜라 조직 사이의 결정립계와 라멜라 조직 내 결정립계에서의 슬라이딩 모드(sliding mode) 변형 정도, 석출상의 크기와 분포 정도 등이 연신률 및 변형속도 민감도와 같은 연성 특성에 가장 큰 영향을 미치는 인자인 것으로 분석되었다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.11a
• /
• pp.57-57
• /
• 2000

Brazing characteristics of the LTCC(Low Temperature Co-fired Ceramics)/ Kovar(Fe-Ni-Co alloy) was investigated. Kovar is one of the typical material for the lid of MCM and packages. In case of alumina package, Brazing process is done by higher temperature profile than 800 $^{\circ}C$ and Ag-Cu alloy. But, LTCC has sintering temperature near 850 $^{\circ}C$. So, it is difficult to use the same process as alumina brazing. The adhesion strength of the brazed part is affected by brazing alloy and metallization properties between conductor pattern and LTCC material. We investigated brazing characteristics of the LTCC/Kovar using various brazing alloys(Ag-Cu, Au-Sn) and process conditions. And, we examined the influence of the glass contents in conductor on the brazing characteristics of the LTCC/Kovar.

• Korean Journal of Heritage: History & Science
• /
• v.48 no.2
• /
• pp.110-119
• /
• 2015

Bronzes, Earthenwares and various artifacts were excavated from Pungnap earthen fortress in the early Baekje age in Korea. This study was performed in order to identify the manufacture technology of bronze artefacts and provenance of lead in bronzes. Microstructure and chemical composition results show that 3 of them are Cu-Sn-Pb alloys in which an intentional lead addition was carried out and one is tin bronze showing straight twin structure within crystal grains. Also $CuFeS_2$ or $Cu_5FeS_4$ was used as raw materials through the detection of S and Fe as trace elements. The lead isotope results could be matched with one of the zones of southern Korea and China on the East Asian map. This results shows that data were plotted either in zone 2 or zone 3 of the South Korean galena map. However, one of bronze artifacts was matched with the zone of Northern China.

• Journal of dental hygiene science
• /
• v.4 no.3
• /
• pp.103-109
• /
• 2004

The present study prepared 72 test samples - 24 made of amalgam alloy, 24 of Verabond (Ni-Cr alloy) for crown and 24 of Talladium $^{TM}alloy$ for denture - according to the manufacturers' manuals and general method in consideration of the width of the mesial-distal dental crown of the lower $1^{st}$ molar and MOD cavity in clinics, put them in a 200 ml beaker containing 80 ml of artificial saliva, and measured their galvanic corrosion at distances of 0 mm, 7 mm and 40 mm after 7 days. Isolated metals in the electrolyte such as Cu, Ag, Ni, Cr, Sn, Zn and Hg were quantitatively analyzed with Inductively Coupled Plasma - Atomic Emission Spectrometer (ICP-AES, JY-50P, VG Elemental Co. France), and from the results were drawn conclusions as follows. First, Cu, Sn, Ag, Hg and Zn were highly advantageous when amalgam contacted gold alloy compared to Ni-Cr alloy for crown and Talladium alloy for denture. In addition, although gold alloy was finest in terms of oral tissue and biocompatibility, it was most disadvantageous when it was with amalgam. Second, when amalgam contacted gold alloy, heavy metals such as Ni and Cr were not isolated at all because gold alloy did not contain such elements but Sn was isolated as much as $227.1{\pm}18.0035{\mu}g/cm^2$ although it was not included in the composition either. Hg was also isolated. These elements are assumed to have been isolated from amalgam itself. Third, when amalgam alloy was apart from gold alloy 0 mm, 7 mm and 40 mm, Cu and Ag showed significance but Hg did not. This suggests that gold alloy must not be used together with amalgam, and must not be used between dissimilar prostheses regardless of distance. Fourth, when amalgam alloy contacted Ni-Cr alloy for crown, Ag was not isolated from the amalgam, but Zn, Ni, Sn, Hg and Cu were isolated in order of quantity. Significance was observed according to distance - 0 mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Ni-Cr alloy for crown, the isolation Hg was less than that when amalgam alloy contacted Ni-Cr alloy for crown. Fifth, when amalgam alloy contacted Talladium alloy for denture, significance was observed at distances of 0mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Talladium alloy for denture, the isolation Hg was less than that when amalgam alloy contacted Talladium alloy for denture. Sixth, according to the result of ICPES test on Cu, Sn, Ag, Hg, Zn, Ni and Cr of amalgam alloy, gold ally, Verabond and Talladium alloy when these alloys contacted artificial saliva, significance was observed in Cu and Hg. Seventh, when amalgam alloy contracted two non-precious metals Ni-Cr alloy for crown and Talladium alloy for denture in artificial saliva, significance was observed in the isolated by-products of Hg, Ni and Cr according to distance.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.1-26
• /
• 1994

The purpose of this study was to investigate the dissolution components during corrosion of amalgams and to identify surface corrosion products in the modified Fusayama artificial saliva. Four type of amalgam alloys were used: low copper lathe cut amalgam alloy (Cavex 68), low copper spherical amalgam alloy (Caulk Spherical Alloy), high copper admixed amalgam alloy (Dispersalloy) and high copper single composition amalgam alloy (Tytin). Each amalgam alloy and Hg were triturated according to the manufacturer's direction by means of mechanical amalgamator (Capmaster, S.S.White), and then the triturated mass was inserted into the cylindrical metal mold which was 10mm in diameter and 2.0mm in height and condensed with compression of 150kg/$cm^2$ using oil pressor. The specimens were removed from the mold and stored at room temperature for 7 days and cleansed with distiled water for 30 minutes in an ultrasonic cleaner. The specimens were immersed in the modified Fusayama artificial saliva for the periods of 1 month, 3 months and 6 months. The amounts of Hg, Cu, Sn and Zn dissolved from each amalgam specimen immersed in the artificial saliva for the periods of 1 month, 3 months and 6 months were measured using Inductivity Coupled Plasma Atomic Emission Spectrometry (ICPQ-1000, Shimadzu, Japan) and amount of Ag dissolved from amalgam specimen was measured using Atomic Absorption Spectrophotometry (Atomic Absorption/Flame emission spectrophotometer M-670, Shimadzu, Japan). A surface corrosion products of specimens were analysed using Electron Spectroscopy Chemical Analyser (ESCA PHI-558, PERKIN ELMER, U.S.A.). The secondary image and back scattered image of corroded surface of specimens was observed under the SEM, and the corroded surface of specimens was analysed with the EDX. The following results were obtained. 1. The dissolution amount of Cu was the most in high copper admixed amalgam(Dispersalloy) and the least in high copper single composition amalgam(Tytin). 2. Sn and Zn were dissolved during all the experiment periods, and dissolution amounts were decreased as the time elapsed. 3. Initial surface corrosion products were ZnO and SnO. 4. Corrosion of ${\gamma}$ and ${\gamma}_2$ phase in low copper amalgams was observed and Ag-Cu eutectic alloy phase was corroded in low copper spherical amalgam(Caulk Sperical Alloy). 5. Corrosion of ${\gamma}$ and $\eta$' phase in high copper amalgams was observed and Ag-Cu eutectic alloy phase was corroded in high copper admixed amalgam(Dispersalloy). 6. Sn-Cl was produced in the subsurface of low copper amalgams and high copper admixed amalgam.

• Journal of Korean Society for Quality Management
• /
• v.45 no.4
• /
• pp.1003-1020
• /
• 2017

Purpose: The purpose of this study is to find the optimum working conditions for spot welding of wire Cu alloys to achieve high-level quality. The parts subject to spot welding are brush card assemblies, which are the main module of the electric movement method of the car seat. Methods: In this study, the signal-to-noise ratio(SN ratio) and the loss function [L(y)] are used as Taguchi method for dynamic characteristics. Results: The results of the study are as follows. First, the analysis of variance using SN ratio showed 6 significant factors(p = 0.1% or less) among 7 factors except press force. Second, the optimal design of the dynamic characteristics is the tip exchange cycle: 50,000 ea., the welding time is 110 ms, the pressing force is 11 kgf/cm2, the rise time is 40 ms, and the tip dressing is 3,000 ea., Tip angle is 12o and electric current is 1,800 A. Conclusion: The validity of the spot welding process of the manufacturer's brush card assembly was verified and proved to be consistent with the study results. The results of this study are expected to standardize the welding conditions and guarantee the quality level required by the customers.